Inorganic foam filling reinforcement composition for coal mine and its use method and application

An inorganic foaming and composition technology, which is applied in the fields of filling, application, mining equipment, etc., can solve the problems of inability to spray injection, fast filling of large roadways, and inability to spray at will, and achieve simple output flow and pressure, treatment The problem is timely and fast, and the effect of the jet hardness is controllable

Active Publication Date: 2016-08-17
廊坊坐城矿用材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Once foamed, it can no longer be moved, let alone sprayed at will, and the foaming lasts for a long time (more than 30 minutes), and it takes a long time (more than 60 minutes) to keep the original shape for a long time and uncontrollable
In addition, after foaming, neither agitation jet nor jet injection
However, coal seams of different shapes, gaps of different sizes, and roadways of different lengths in coal mines are impossible without flexible and controllable grouting materials.
[0006] Although cement foam, glass foam, etc. are inorganic materials, they cannot be moved freely after foaming. After being formed, they are hard block materials, which cannot be filled and injected into coal mine gaps like slurry. Problems such as injection plugging and filling reinforcement of voids cannot solve the problem of rapid filling of large roadways

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] A material formula (calculated in 1000g dose):

[0064] 95g silicon-calcium powder (produced by Jingxing County Dongtai Calcium Industry Co., Ltd.; industrial grade, average particle size 62 μm);

[0065] 16g iron oxide (Shijiazhuang Luancheng Dexin Chemical Co., Ltd., industrial grade, average particle size 62 μm);

[0066] 270g calcium powder (produced by Jingxing County Dongtai Calcium Industry Co., Ltd.; industrial grade, average particle size 76 μm);

[0067] 10g lithium carbonate (produced by Jiangxi Yinli New Energy Co., Ltd., industrial-grade purity 95%, average particle size 28 μm);

[0068] 10g quick-drying powder (produced by Jiangxi Yinli New Energy Co., Ltd., industrial grade, with an average particle size of 28 μm);

[0069] 510g calcium silicate (produced by Jingxing County Dongtai Calcium Industry Co., Ltd.; industrial grade, average particle size 28 μm);

[0070] 34g gypsum powder (produced by Jingxing County Dongtai Calcium Industry Co., Ltd.; indus...

Embodiment 2

[0084] A material formula (calculated in 1000g dose):

[0085] 70g silicon-calcium powder (produced by Jingxing County Dongtai Calcium Industry Co., Ltd.; industrial grade, average particle size 62 μm);

[0086] 15g iron oxide (Shijiazhuang Luancheng Dexin Chemical Co., Ltd., industrial grade, average particle size 62 μm);

[0087] 260g calcium powder (produced by Jingxing County Dongtai Calcium Industry Co., Ltd.; industrial grade, average particle size 76 μm);

[0088] 10g lithium carbonate (produced by Jiangxi Yinli New Energy Co., Ltd., industrial-grade purity 95%, average particle size 28 μm);

[0089] 10g quick-drying powder (produced by Jiangxi Yinli New Energy Co., Ltd., industrial grade, with an average particle size of 28 μm);

[0090] 500g calcium silicate (produced by Jingxing County Dongtai Calcium Industry Co., Ltd.; industrial grade, average particle size 28 μm);

[0091] 80g gypsum powder (produced by Jingxing County Dongtai Calcium Industry Co., Ltd.; indus...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an inorganic foaming filling and reinforcing composition for a coal mine as well as a using method and application thereof. The inorganic foaming filling and reinforcing composition for the coal mine can be used as a novel safe plugging and reinforcing material, is especially suitable for plugging and reinforcing of the coal mine, and is the best water-proof, fire-proof, gas-proof, collapse-proof and accident-proof material.

Description

technical field [0001] The invention relates to the field of chemical industry, in particular to an inorganic foaming filling and reinforcing composition for coal mines and its use method and application. Background technique [0002] In recent years, due to the needs of safe production in coal mines, researchers and enterprises have studied expandable foaming materials such as foaming, filling, and reinforcement for coal mines. The use of organic foaming materials in coal mines is still tentative. The organic foaming materials used are mainly polystyrene foaming materials, polyvinyl chloride foaming materials, polyurethane foaming materials, phenolic resin foaming materials and other polymeric organic materials. It is obviously very dangerous to use organic materials in coal mines to solve gas accumulation, prevent gas fires, block fire sources, prevent fires, and extinguish fires. First of all, during the foaming and curing process of organic materials, a high temperatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02C04B28/14E21F15/00E21D11/10
Inventor 高万水
Owner 廊坊坐城矿用材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products