A technology of aluminum rolling and epoxidized soybean oil, applied in the field of aluminum rolling oil, can solve the problems of easy scratches and low gloss, and achieve the effects of good lubricating performance, high gloss and simple preparation method

Inactive Publication Date: 2015-03-25
WUXI HEBANG METAL PROD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Products rolled with existing aluminum rolling oil have low gloss and are prone to scratches

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of the aluminum rolling oil of the present invention is as follows:

[0011] Epoxidized soybean oil 4.5kg, sodium dodecyl sulfonate 0.6kg, sorbitol 1.3kg, sodium benzoate 0.5kg, sodium silicate 0.25kg, lauric acid diethanolamide 0.15kg, polyacrylamide 0.3kg, methyl laurate Ester 0.2kg, sodium tripolyphosphate 0.6kg, sodium borate 0.3kg, butyl stearate 0.3kg.

[0012] The preparation method of the aluminum rolling oil of the present invention is as follows:

[0013] Epoxidized soybean oil 4.5kg, sodium dodecyl sulfonate 0.6kg, sodium silicate 0.25kg, lauric acid diethanolamide 0.15kg, polyacrylamide 0.3kg, methyl laurate 0.2kg, sodium tripolyphosphate 0.6 kg mixed, heated to 70°C, stirred for 38min; then cooled to 48°C, added sorbitol 1.3kg, sodium benzoate 0.5kg, sodium borate 0.3kg and butyl stearate 0.3kg, stirred at 18°C, cooled to room temperature to obtain .

Embodiment 2

[0015] The formula of the aluminum rolling oil of the present invention is as follows:

[0016] Epoxidized soybean oil 4kg, sodium dodecyl sulfonate 0.8kg, sorbitol 1.2kg, sodium benzoate 0.4kg, sodium silicate 0.2kg, lauric acid diethanolamide 0.1kg, polyacrylamide 0.4kg, methyl laurate 0.1kg, sodium tripolyphosphate 0.4kg, sodium borate 0.4kg, butyl stearate 0.2kg.

[0017] The preparation method of the aluminum rolling oil of the present invention is as follows:

[0018] Epoxidized soybean oil 4kg, sodium dodecyl sulfonate 0.8kg, sodium silicate 0.2kg, lauric acid diethanolamide 0.1kg, polyacrylamide 0.4kg, methyl laurate 0.1kg, sodium tripolyphosphate 0.4kg Mix, heat to 65°C, stir for 40min; then cool to 45°C, add sorbitol 1.2kg, sodium benzoate 0.4kg, sodium borate 0.4kg and butyl stearate 0.2kg, stir at 20°C, and cool to room temperature.

Embodiment 3

[0020] The formula of the aluminum rolling oil of the present invention is as follows:

[0021] Epoxidized soybean oil 5kg, sodium lauryl sulfonate 0.5kg, sorbitol 1.5kg, sodium benzoate 0.6kg, sodium silicate 0.3kg, lauric acid diethanolamide 0.2kg, polyacrylamide 0.2kg, methyl laurate 0.3kg, sodium tripolyphosphate 0.7kg, sodium borate 0.2kg, butyl stearate 0.4kg.

[0022] The preparation method of the aluminum rolling oil of the present invention is as follows:

[0023] Epoxidized soybean oil 5kg, sodium dodecyl sulfonate 0.5kg, sodium silicate 0.3kg, lauric acid diethanolamide 0.2kg, polyacrylamide 0.2kg, methyl laurate 0.3kg, sodium tripolyphosphate 0.7kg Mixed, heated to 75°C, stirred for 35min; then cooled to 50°C, added sorbitol 1.5kg, sodium benzoate 0.6kg, sodium borate 0.2kg and butyl stearate 0.4kg, stirred at 15°C, and cooled to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides aluminum rolling oil. The aluminum rolling oil is composed of the following components in parts by mass: 4-5 parts of epoxidized soybean oil, 0.5-0.8 part of sodium dodecyl sulfonate, 1.2-1.5 parts of sorbitol, 0.4-0.6 part of sodium benzoate, 0.2-0.3 part of sodium silicate, 0.1-0.2 part of lauric diethanolamide, 0.2-0.4 part of polyacrylamide, 0.1-0.3 part of methyl laurate, 0.4-0.7 part of sodium tripolyphosphate, 0.2-0.4 part of sodium borate and 0.2-0.4 part of butyl stearate. The invention also provides a preparation method of the aluminum rolling oil. An aluminum product rolled by using the aluminum rolling oil provided by the invention is high in glossiness, free of scratches and good in lubricating property. In addition, the preparation method of the aluminum rolling oil, provided by the invention, is simple and suitable for popularization and application.

Description

technical field [0001] The invention relates to an aluminum rolling oil. Background technique [0002] Rolling is a processing method in which metal passes through the gap between two relatively rotating rolls on a rolling mill, and is rolled and deformed into profiles (such as steel plates, round steel, angle steel, etc.). The main function of rolling oil is to reduce the friction between the roll and the aluminum foil, provide a stable friction interface, realize stable rolling, and improve surface quality. Products rolled with existing aluminum rolling oil have low gloss and are prone to scratches. Contents of the invention [0003] The invention provides an aluminum rolling oil. Aluminum products rolled by using the aluminum rolling oil of the invention have good gloss and no scratches; therefore, the invention also provides a preparation method thereof. [0004] The invention provides an aluminum rolling oil, which is composed of the following components in parts by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/04C10N40/24
Inventor 邓义增
Owner WUXI HEBANG METAL PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap