Spray-free PC composition with special aesthetic effect and its preparation method and application
A special effect powder, spray-free technology, applied in the field of polymer materials, can solve the problems of uneven distribution of special effect powder, unstable flow rate, poor compatibility, etc. metal texture effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1-6
[0044] Example 1-6 Preparation of polymer-coated special effect powder microspheres:
[0045] According to the formula in Table 1, firstly, add anti-oxidation and corrosion inhibitor to the water-based polymer dispersion at room temperature, stir and disperse for 15 minutes to obtain a dispersion; while stirring, slowly add special effect powder, or water-based Special effect powder slurry, then add curing agent while stirring, and continue to stir for 30-120 minutes, so that the special effect powder is fully dispersed and covered by the dispersion liquid, and finally a composite dispersion liquid of polymer-coated special effect powder is obtained; The composite dispersion liquid is spray-dried to obtain polymer-coated special-effect powder microspheres. The temperature of the air inlet during the spray-drying process is 150-300° C., and the temperature of the air outlet is 50-130° C.
Embodiment 1
[0048]In Example 1: the water-based polymer dispersion is a water-based epoxy resin, and its solid content is 10wt%; the metal powder is a surface-treated flake aluminum powder, and the content of the Al element in the aluminum powder is 60wt%, containing Zn and Sn; its particle size is 100 μm; the anti-oxidant corrosion inhibitor is pyrogallic acid; the curing agent is dicyandiamide.
Embodiment 2
[0049] In Example 2: the water-based polymer dispersion is ASA emulsion, and its solid content is 60wt%; the metal powder is surface-treated flake copper powder, and the content of Cu element in the copper powder is 70wt%, containing Zn and Sn; The particle size is 5 μm; the antioxidant and corrosion inhibitor is benzotriazole; the curing agent is aziridine.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com