Vinyl phenyl silicon resin with side chain containing epoxy group and preparation method of vinyl phenyl silicon resin

A vinyl phenyl silicon, epoxy group technology, applied in the direction of adhesives, etc., can solve the problems of poor adhesion and poor mechanical properties, achieve high transparency, easy operation, and reduce the use of tackifiers.

Inactive Publication Date: 2015-06-03
SHANGHAI INST OF TECH
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the above-mentioned technical problems in the prior art, the present invention provides a vinyl phenyl silicone resin containing epoxy groups in the side chain and a preparation method thereof, the vinyl phenyl silicone resin containing epoxy groups in the side chain Phenyl silicone resin and preparation method thereof solve technical problems such as poor adhesion and poor mechanical properties of silicone resin in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vinyl phenyl silicon resin with side chain containing epoxy group and preparation method of vinyl phenyl silicon resin
  • Vinyl phenyl silicon resin with side chain containing epoxy group and preparation method of vinyl phenyl silicon resin
  • Vinyl phenyl silicon resin with side chain containing epoxy group and preparation method of vinyl phenyl silicon resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of preparation method of the vinyl phenyl silicone resin that side chain contains epoxy group, specifically comprises the steps:

[0033] (1) Preparation of cyclotetrasiloxane containing epoxy cyclohexane group

[0034] Under a nitrogen atmosphere, 100 parts by weight of 1,3,5,7-tetramethylcyclotetrasiloxane and 206 parts by weight of 4-vinyl epoxycyclohexane were added in proportion to the In a 500ml four-necked flask with a funnel and a thermometer, add 100 parts by weight of toluene, 0.001 parts by weight of chloroplatinic acid-isopropanol solution, and simultaneously add 0.001 parts by weight of 4-methoxyphenol; then heat up to 80°C and react for 2 hours. The reaction mixture was distilled under reduced pressure at -0.096MPa at 150°C to remove the solvent and residual low boilers to obtain a liquid with a viscosity of 3000mPa.s, namely cyclotetrasiloxane containing epoxycyclohexane groups.

[0035] The above-mentioned cyclotetrasiloxane containing epoxycyclo...

Embodiment 2

[0047] A kind of preparation method of the vinyl phenyl silicone resin that side chain contains epoxy group, specifically comprises the steps:

[0048] (1) Preparation of cyclotetrasiloxane containing epoxy cyclohexane group

[0049] Under a nitrogen atmosphere, 100 parts by weight of 1,3,5,7-tetramethylcyclotetrasiloxane and 208 parts by weight of 4-vinyl epoxycyclohexane were added in proportion to the In a 500ml four-necked flask with a funnel and a thermometer, add 100 parts by weight of cyclohexane, 0.002 parts by weight of chloroplatinic acid, and 0.003 parts by weight of hydroquinone; then heat up to 85°C and react for 5 hours. Under reduced pressure at -0.096MPa, the solvent and residual low boilers were removed to obtain a light yellow liquid with a viscosity of 3600mPa.s, namely cyclotetrasiloxane containing epoxycyclohexane groups.

[0050] According to the national standard GB / T 1677-2008, the epoxy value of the plasticizer is determined to be 0.54; it is close to...

Embodiment 3

[0060] A kind of preparation method of the vinyl phenyl silicone resin that side chain contains epoxy group, specifically comprises the steps:

[0061] (1) Preparation of cyclotetrasiloxane containing epoxy cyclohexane group

[0062] Under a nitrogen atmosphere, 100 parts by weight of 1,3,5,7-tetramethylcyclotetrasiloxane and 210 parts by weight of 4-vinyl epoxycyclohexane were added in proportion to the In a 500ml four-necked flask with a funnel and a thermometer, add 100 parts by weight of cyclohexane, 0.003 parts by weight of chloroplatinic acid, and 0.003 parts by weight of hydroquinone; then heat up to 90°C and react for 10 hours. Under reduced pressure at -0.096MPa, the solvent and residual low boilers were removed to obtain a light yellow liquid with a viscosity of 4300mPa.s, namely cyclotetrasiloxane containing epoxycyclohexane groups.

[0063] According to the national standard GB / T 1677-2008, the epoxy value of the plasticizer is determined to be 0.54; it is close t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to vinyl phenyl silicon resin with a side chain containing an epoxy group, and the structural formula is as shown in the specification. The invention also discloses a preparation method of the vinyl phenyl silicon resin. The preparation method comprises the following steps: under nitrogen condition, adding 1,3,5,7-tetramethyl cyclotetrasiloxane and 4-vinyl cyclohexene oxide to a reaction container according to a proportion, adding a solvent, a catalyst and a polymerization inhibitor in parts by weight, increasing temperature to react, carrying out reduced pressure distillation to obtain a cyclotetrasiloxane containing cyclohexene oxide group, then adding cyclotetrasiloxane containing cyclohexene oxide group, vinyl cyclosiloxane, methyl phenyl cyclosiloxane and an end-capping reagent to the other reaction container according to a proportion, increasing temperature to react, and carrying out reduced pressure distillation to obtain vinyl phenyl silicon resin with a side chain containing an epoxy group. The preparation method is simple, flexible, moderate in reaction condition and suitable for industrial production.

Description

technical field [0001] The invention belongs to the field of polymer materials, and relates to a vinyl phenyl silicone resin, in particular to a vinyl phenyl silicone resin with epoxy groups in its side chain and a preparation method thereof. Background technique [0002] The rapid development of the LED packaging industry requires the development of packaging materials that are resistant to thermal shock, non-yellowing, high light transmittance, and high refractive index. At present, common LED packaging materials are mainly bisphenol A transparent epoxy resin and silicone resin. Epoxy resin is suitable for low-power LED packaging process. Silicone resin is suitable for the packaging of high-power LEDs. Silicone resin has the advantages of high light transmittance, good thermal stability, low stress, and low moisture absorption. However, silicone resin has poor adhesion to the chip as an encapsulant and poor mechanical properties. It is often used in silicone encapsulant....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G77/20C08G77/06C09J183/07C09J183/06
Inventor 张英强赵永新徐耀民王晓瑞郑康生吴蓁
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap