Anti-static anti-flaming oil-proof water-repellent cotton/tencel blended fabric and preparation method thereof

A blended fabric, anti-static technology, applied in the field of cotton/tencel blended fabric and its preparation, can solve the problems of single anti-static, flame retardant, oil-proof, water-repellent functions, etc., achieve huge social and economic benefits, excellent performance, The effect of reducing static electricity

Active Publication Date: 2015-07-08
SHAANXI GILDLAND SCI & TECH CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems existing in the prior art, the object of the present invention is to provide an antistatic, flame-resistant, oil-repellent and water-repellent cotton / tencel blended fabric and its preparation method, which solves the common cotton / tencel blended fabric existing in the prior art. Silk blended fabrics generally only have a single function of anti-static, flame-retardant, oil-proof, and water-repellent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-static anti-flaming oil-proof water-repellent cotton/tencel blended fabric and preparation method thereof
  • Anti-static anti-flaming oil-proof water-repellent cotton/tencel blended fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An antistatic, flame-resistant, oil-repellent and water-repellent cotton / tencel blended fabric is prepared by the following method:

[0034] Step 1, anti-static gray fabric weaving

[0035] Nylon 20D / 3F conductive yarn and cotton / tencel blended yarn are twisted together to form conductive yarn, the cotton fiber content is 80%, and the tencel fiber content is 20%. The twist of the conductive yarn is 25 twists / 10cm. Weaving gray fabric with cotton / tencel blended yarn as warp and weft. During the weaving process, conductive yarns were woven into the warp and weft directions at intervals, the distance between two adjacent conductive yarns in the warp direction was 0.5 cm, and the distance between two adjacent conductive yarns in the weft direction was 0.5 cm. Prepare antistatic gray cloth.

[0036] Step two, dye

[0037] The antistatic gray cloth in step 1 is subjected to pre-dyeing treatment, dipped and rolled on a dyeing machine, then dried and soaped to obtain an ant...

Embodiment 2

[0044] An antistatic, flame-resistant, oil-repellent and water-repellent cotton / tencel blended fabric is prepared by the following method:

[0045] Step 1, anti-static gray fabric weaving

[0046] Nylon 20D / 3F conductive yarn and cotton / tencel blended yarn are twisted together to form conductive yarn, the cotton fiber content is 90%, and the tencel fiber content is 10%. The twist of the conductive yarn is 40 twists / 10cm. Weaving gray fabric with cotton / tencel blended yarn as warp and weft. During the weaving process, conductive yarns were woven into the warp and weft directions at intervals, the distance between two adjacent conductive yarns in the warp direction was 1 cm, and the distance between two adjacent conductive yarns in the weft direction was 1 cm. Prepare antistatic gray cloth.

[0047] Step two, dye

[0048] The antistatic gray cloth in step 1 is subjected to pre-dyeing treatment, dipped and rolled on a dyeing machine, then dried and soaped to obtain an antista...

Embodiment 3

[0055] An antistatic, flame-resistant, oil-repellent and water-repellent cotton / tencel blended fabric is prepared by the following method:

[0056] Step 1, anti-static gray fabric weaving

[0057] Nylon 20D / 3F conductive yarn and cotton / tencel blended yarn are twisted together to form conductive yarn, the content of cotton fiber in the conductive yarn is 95%, and the content of tencel fiber is 5%. The twist of the conductive yarn is 50 twists / 10cm. Weaving gray fabric with cotton / tencel blended yarn as warp and weft. During the weaving process, conductive yarns were woven into the warp and weft directions at intervals, the distance between two adjacent conductive yarns in the warp direction was 2 cm, and the distance between two adjacent conductive yarns in the weft direction was 2 cm. Prepare antistatic gray cloth.

[0058] Step two, dye

[0059] The antistatic gray cloth in step 1 is subjected to pre-dyeing treatment, dipped and rolled on a dyeing machine, then dried and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of a functional fabric, in particular to an anti-static anti-flaming oil-proof water-repellent cotton / tencel blended fabric and a preparation method thereof. The preparation method comprises the following steps: step 1, weaving an anti-static gray fabric, and respectively and intermittently weaving conductive yarns in a weft direction and a warp direction in the course of weaving; step 2, dyeing; step 3, carrying out flame-proof treatment by adopting a process of two-dipping and two-rolling, drying and baking; step 4, carrying out oil-proof water-repellent treatment by adopting a process of one-dipping and one-rolling, drying and roasting to obtain the anti-static anti-flaming oil-proof water-repellent cotton / tencel blended fabric. The fabric has the effects of excellent static electricity resistance, flame resistance, oil prevention and water repellence, meets the national relevant specifications, and meets the demands of industrial production and utilization.

Description

technical field [0001] The invention belongs to the technical field of functional textiles, and in particular relates to an antistatic, flame-resistant, oil- and water-repellent cotton / tencel blended fabric and a preparation method thereof. Background technique [0002] Cotton / tencel blended fabrics are comfortable to the touch, natural in style, cool and breathable, and are deeply loved by consumers. However, cotton / tencel blended fabrics have a strong affinity for oil stains and are easy to absorb oil stains, and they are prone to static electricity and absorb dust during wearing in autumn and winter. [0003] Static electricity will attract dust, which is not beautiful, affects the comfort of wearing, and is not easy to clean. In some special occasions, static electricity will generate sparks, leading to fire or even explosion accidents. Textiles will burn quickly once they encounter fire. In daily life or industrial production, textiles often burn due to negligence and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A41D31/00D03D15/00D06B3/18D06M13/44D06M15/564D06M11/155D06M11/55D06M13/188D06M15/256D06M101/06D06M101/10D03D15/217D03D15/225D03D15/47D03D15/533
Inventor 侯连书
Owner SHAANXI GILDLAND SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap