Waterborne antistatic wear-resistant coating

A wear-resistant coating and anti-static technology, applied in the direction of coating, can solve the problems of wear-resistant coating limitation, use limitation, unstable performance, etc., and achieve the effect of good wear resistance and poor adhesion improvement.

Inactive Publication Date: 2015-11-11
TAICANG JINXIN PAINT
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are some water-based coatings on the market that have antistatic effect, but the performance is unstable, wear resistance and other issues limit the application of coatings
[0003] The use of traditional solvent-based coatings is increasingly restricted due to their high levels of volatile organic compounds (VOCs) and harmful air pollutants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A water-based antistatic wear-resistant coating, comprising: water: 32%, water-based resin: 30%, film-forming aid: 1.2%, dispersant: 1.5%, leveling agent: 0.85%, defoamer: 0.15%, Water-based adhesion promoter: 2.3%, titanium dioxide: 3.7%, talcum powder: 4.5%, nano calcium carbonate: 6%, pH regulator: 1%, silicon carbide: 10%, antistatic agent: 6.8%.

[0021] The water-based antistatic wear-resistant paint prepared by the above formula is tested according to the static electricity test method of AATCC76-1995, and its variation value is less than 3.5%.

Embodiment 2

[0023] A water-based antistatic wear-resistant coating, comprising: water: 25%, water-based resin: 30%, film-forming aid: 1.98%, dispersant: 2.5%, leveling agent: 0.7%, defoamer: 0.18%, Water-based adhesion promoter: 3.5%, titanium dioxide: 4.6%, talcum powder: 8.7%, nano calcium carbonate: 4.7%, pH regulator: 0.8%, silicon carbide: 11.1%, antistatic agent: 6.24%.

Embodiment 3

[0025] A water-based antistatic wear-resistant coating, comprising: water: 35%, water-based resin: 25%, film-forming aid: 0.99%, dispersant: 2.4%, leveling agent: 0.76%, defoamer: 0.1%, Water-based adhesion promoter: 3.5%, titanium dioxide: 5%, talc powder: 4.6%, nano calcium carbonate: 5.5%, pH regulator: 1.2%, silicon carbide: 6.5%, antistatic agent: 9.45%.

[0026] Other performance results of the coating of embodiment one:

[0027] Test items

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a waterborne antistatic wear-resistant coating. The waterborne antistatic wear-resistant coating comprises 25-35% of water, 25-30% of waterborne resin, 0.7-2% of film-forming additives, 0.8-2.5% of dispersing agent, 0.3-1% of levelling agent, 0.1-0.2% of defoaming agent, 2-3.5% of waterborne adhesion promoter, 0.3-5% of titanium dioxide, 0-10% of talcum powder, 0-18% of nano calcium carbonate, 1-1.5% of pH regulator, 10-15.5% of silicon carbide and 6.5-10% of antistatic agent. The waterborne antistatic wear-resistant coating has the advantages of strong adhesion, good wear resistance, antistatic property, acid and alkali resistance, economical property and environment friendliness.

Description

technical field [0001] The invention relates to a water-based antistatic wear-resistant coating Background technique [0002] With the development of modern science and technology, there are more and more applications on walls and floors that require cleanliness and antistatic requirements, such as in electronic and electrical workshops, computer rooms, printing factories, textile factories, and pharmaceutical factories. Coatings are paid more and more attention to, and antistatic coating products are mainly made by adding antistatic agents or antistatic fillers to coatings. At present, there are also some water-based coatings on the market that have antistatic effect, but the application of coatings is limited due to problems such as unstable performance and wear resistance. [0003] The use of traditional solvent-based coatings is increasingly restricted due to their high levels of volatile organic compounds (VOCs) and harmful air pollutants. Therefore, pollution-free wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D7/12C09D5/00
Inventor 王觉明
Owner TAICANG JINXIN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com