Carbon fiber composite line for automobile clutch surface patch, preparation method and application thereof

A clutch face and carbon fiber technology, applied in the textile field, can solve the problems of resource waste, short service life, environmental pollution, etc., and achieve the effect of prolonging service life, good wear resistance and smooth use

Active Publication Date: 2014-06-11
NANTONG XINYUAN SPECIAL FIBER
View PDF8 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Since the reinforcement materials for automobile clutch face sheets all contain metal wires such as copper wires, the friction coefficient, wear performance, product density and burst strength of the face sheets are not very ideal, and the actual use of the face

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Example 1 A carbon fiber composite wire for automobile clutch face

[0037] It is made of glass fiber roving with a linear density of 350tex, glass fiber roving with a linear density of 350tex, carbon fiber core-spun yarn with a linear density of 370tex and acrylic fiber roving with a linear density of 200tex. Among them, the core yarn of the carbon fiber core-spun yarn is 3k high carbon fiber filament, and the cover yarn is composed of viscose fiber (30% by weight) and acrylic fiber (70% by weight).

[0038] The carbon fiber composite wire of this embodiment is prepared by the following method:

[0039] 1. be the glass fiber roving bulking treatment of 350tex with linear density, obtain described glass non-twisting fiber bulking yarn;

[0040] II. get the viscose fiber and acrylic staple fiber according to the weight ratio, mix and loosen, make sliver, then spin with the carbon fiber filament on an air friction spinning machine to obtain the carbon fiber core-spun ya...

Embodiment 2

[0045] Example 2 A carbon fiber composite wire for automobile clutch face

[0046] It is made of twisted glass fiber roving with a linear density of 450tex, glass fiber untwisted bulked yarn with a linear density of 450tex, carbon fiber core-spun yarn with a linear density of 350tex and acrylic fiber roving with a linear density of 200tex. Among them, the core yarn of the carbon fiber core-spun yarn is 3k high carbon fiber filament, and the cover yarn is composed of viscose fiber (30% by weight) and acrylic fiber (70% by weight).

[0047] The carbon fiber composite wire of this embodiment is prepared through the same steps as in Embodiment 1, except that:

[0048] 1. be the glass fiber roving bulking treatment that linear density is 450tex, obtain described glass non-twisting fiber bulking yarn;

[0049] IV. The degree of twisting is S80TPM.

[0050] The main technical parameters of the carbon fiber composite wire prepared in this embodiment are:

[0051] Linear density: ...

Embodiment 3

[0052] Example 3 A carbon fiber composite wire for automobile clutch face

[0053] It is twisted from glass fiber roving with a linear density of 600tex, glass fiber roving with a linear density of 600tex, carbon fiber core-spun yarn with a linear density of 370tex and acrylic fiber roving with a linear density of 300tex. Among them, the core yarn of the carbon fiber core-spun yarn is 3k high carbon fiber filament, and the cover yarn is composed of viscose fiber (30% by weight) and acrylic fiber (70% by weight).

[0054] The carbon fiber composite wire of this embodiment is prepared through the same steps as in Embodiment 1, except that:

[0055] 1. be the glass fiber roving bulking treatment that linear density is 600tex, obtain described glass non-twisting fiber bulking yarn;

[0056] IV. Twisting degree is S70TPM.

[0057] The main technical parameters of the carbon fiber composite wire prepared in this embodiment are:

[0058] Linear density: 1870tex; Tensile strength...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Linear densityaaaaaaaaaa
Linear densityaaaaaaaaaa
Linear densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a carbon fiber composite line for automobile clutch surface patch and the application thereof in preparation of an automobile clutch. The carbon fiber composite line for the automobile clutch comprises a carbon fiber long filament and a carbon fiber core spun yarn with the carbon fiber long filament as the core yarn, and does not comprise metal wires; the carbon fiber composite line also can comprise glass fiber twistless roving, a glass fiber twistless extrusion yarn and chemical fiber roving. The invention also provides the automobile clutch surface patch comprising the carbon fiber composite line. With the adoption of the carbon fiber composite line, the environmental pollution and waste of resources caused by copper wires and other metal wires in the automobile clutch are solved, and the performances of the automobile clutch are also improved.

Description

technical field [0001] The invention belongs to the field of textiles, and in particular relates to a carbon fiber composite thread for an automobile clutch face and a preparation method and application thereof. Background technique [0002] With the development of the automobile industry, higher requirements are put forward for the supporting friction materials; especially for the quality of the clutch face in the transmission system, which is responsible for transmitting power torque, the requirements are more stringent: in addition to requiring a suitable and stable friction coefficient, relatively In addition to low wear and high burst strength, good clutch stability must also be required. The clutch face consists of rubber compound and composite fibers. In the prior art, the composite fibers for clutches all contain metal wires except chemical fibers and inorganic fibers. For example, the Chinese utility model patent (authorized notification number CN201582324U) discl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/04D02G3/36D02G3/44F16D13/64D02G3/18
Inventor 蔡安兰杨余章邓育新钱勤
Owner NANTONG XINYUAN SPECIAL FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap