A polymer material, fire-retardant technology, applied in the field of fire-retardant and flame-retardant polymer materials, can solve the problems of low flame retardancy, low ignition point, hidden safety hazards, etc., and achieve good wear resistance, high flame retardancy, and fire resistance. Good results
Inactive Publication Date: 2016-03-02
QINGDAO YUXING INTELLIGENT TECH DEV CO LTD
View PDF0 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Existing flame retardant materials have low flame retardancy, poor effect, low ignition point, can not achieve
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] A fire-resistant and flame-retardant polymer material, made of the following raw materials in parts by mass:
[0012] 30 parts of epoxy resin, 8 parts of asbestos, 5 parts of calcium carbonate, 11 parts of acrylic emulsion, 11 parts of dimethylacetamide, 6 parts of ethyl acetate, 7 parts of magnesium stearate, 9 parts of magnesium hydroxide, silicon dioxide 6 parts, 4 parts of aluminum hydroxide, 11 parts of simethicone.
Embodiment 2
[0014] A fire-resistant and flame-retardant polymer material, made of the following raw materials in parts by mass:
[0015] 35 parts of epoxy resin, 9 parts of asbestos, 6 parts of calcium carbonate, 14 parts of acrylic emulsion, 13 parts of dimethylacetamide, 8 parts of ethyl acetate, 7.5 parts of magnesium stearate, 9.6 parts of magnesium hydroxide, silicon dioxide 7 parts, aluminum hydroxide 6 parts, simethicone 12 parts.
Embodiment 3
[0017] A fire-resistant and flame-retardant polymer material, made of the following raw materials in parts by mass:
[0018] 40 parts of epoxy resin, 10 parts of asbestos, 7 parts of calcium carbonate, 16 parts of acrylic emulsion, 14 parts of dimethylacetamide, 9 parts of ethyl acetate, 8 parts of magnesium stearate, 10 parts of magnesium hydroxide, silicon dioxide 8 parts, aluminum hydroxide 7 parts, simethicone 14 parts.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a fireproof and flame-retardant polymer material. The fireproof and flame-retardant polymer material is prepared from raw materials in parts by mass as follows: 30-40 parts of epoxy resin, 8-10 parts of asbestos, 5-7 parts of calcium carbonate, 11-16 parts of an acrylic emulsion, 11-14 parts of dimethylacetamide, 6-9 parts of ethyl acetate, 7-8 parts of magnesium stearate, 9-10 parts of magnesium hydrate, 6-8 parts of silica, 4-7 parts of aluminium hydroxide and 11-14 parts of dimethicone. The fireproof and flame-retardant polymer material is good in fireproof performance, high in flame retardance, high in strength, good in abrasion resistance, economical and environment-friendly.
Description
technical field [0001] The invention relates to the technical field of polymer materials, in particular to a fire-proof and flame-retardant polymer material. Background technique [0002] Flame-retardant materials are materials that can inhibit or delay combustion but are not easy to burn. They are widely used in clothing, petroleum, chemical industry, metallurgy, shipbuilding, fire protection, national defense and other fields. Existing flame-retardant materials have low flame retardancy, poor effect, low ignition point, can not achieve the effect of use, and have great potential safety hazards. Therefore, a fire-resistant and flame-retardant material is urgently needed. Contents of the invention [0003] In order to solve the above existing problems, the present invention provides a fire-resistant and flame-retardant polymer material with good fire resistance, high flame retardancy, high strength, good wear resistance, economical and environmental protection. [0004] T...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more