A kind of linear-hyperbranched phosphate ester salt surfactant and preparation method thereof

A technology of surfactant and phosphate ester salt, applied in chemical instruments and methods, organic chemistry, phosphorus-organic compounds, etc., can solve problems such as the limitation of surfactant application

Active Publication Date: 2017-08-29
广东方中高新材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, general phosphate ester salt surfactants only contain one or two hydrophilic groups, which limits the application of surfactants.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of linear-hyperbranched phosphate ester salt surfactant and preparation method thereof
  • A kind of linear-hyperbranched phosphate ester salt surfactant and preparation method thereof
  • A kind of linear-hyperbranched phosphate ester salt surfactant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1. Preparation of hydroxyl-terminated hyperbranched polymers:

[0038] Add diethanolamine and methyl acrylate in a molar ratio of 1:2 to a reactor containing 10 mL of methanol solution, raise the temperature to 30°C, keep the temperature for 4 hours, remove methanol and excess methyl acrylate by vacuuming, and prepare AB 2 Monomer (methyl N,N-dihydroxyethyl-3-aminopropionate).

[0039] In the monomer prepared above, add pentaerythritol, the molar ratio of pentaerythritol to monomer is 1:4, then add p-toluenesulfonic acid with a total mass fraction of 0.5% in the reactor, mix and heat to 110°C, mix well After heating up to reflux, react for 6h, after cooling the reaction, dissolve in CH 2 Cl 2 Washing, suction filtration under reduced pressure for 3 times, and rotary evaporation to produce a hydroxyl-terminated hyperbranched polymer.

[0040] 2. Preparation of linear-hyperbranched polymers:

[0041] Add 50mL of pyridine solution in the reactor, remove the moisture in...

Embodiment 2

[0045] 1. Preparation of hydroxyl-terminated hyperbranched polymers:

[0046]Add diethanolamine and methyl acrylate in a molar ratio of 1:3 to a reactor containing 15 mL of methanol solution, raise the temperature to 50°C, keep the temperature for 5 hours, remove methanol and excess methyl acrylate by vacuuming, and prepare AB 2 Monomer (methyl N,N-dihydroxyethyl-3-aminopropionate).

[0047] Add pentaerythritol to the monomer prepared above, the molar ratio of pentaerythritol to monomer is 1:4, then add concentrated sulfuric acid with a total mass fraction of 1.0% in the reactor, mix and heat to 120°C, mix well and then heat up Reflux, react for 6h, after cooling the reaction, dissolve in CH 2 Cl 2 Washing, suction filtration twice under reduced pressure, and rotary evaporation to produce a hydroxyl-terminated hyperbranched polymer.

[0048] 2. Preparation of linear-hyperbranched polymers:

[0049] Add 60mL of pyridine solution in the reactor, remove the moisture in the re...

Embodiment 3

[0053] 1. Preparation of hydroxyl-terminated hyperbranched polymers:

[0054] Add diethanolamine and methyl acrylate in a molar ratio of 1:2 to a reactor containing 15 mL of methanol solution, raise the temperature to 35°C, keep the temperature for 4 hours, remove methanol and excess methyl acrylate by vacuuming, and prepare AB 2 Monomer (methyl N,N-dihydroxyethyl-3-aminopropionate).

[0055] In the monomer prepared above, add pentaerythritol, the molar ratio of pentaerythritol to monomer is 1:5, then add hydrochloric acid with a total mass fraction of 0.6% in the reactor, mix and heat to 120°C, mix well and then heat up to reflux , reacted for 6h, cooled the reaction, dissolved in CH 2 Cl 2 Washing, suction filtration under reduced pressure for 3 times, and rotary evaporation to produce a hydroxyl-terminated hyperbranched polymer.

[0056] 2. Preparation of linear-hyperbranched polymers:

[0057] Add 60mL of pyridine solution in the reactor, remove the moisture in the rea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of graftingaaaaaaaaaa
degree of graftingaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention discloses a linear-hyperbranched phosphate ester salt surfactant and a preparation method thereof. By synthesizing an AB2 monomer and then synthesizing a hydroxyl-terminated hyperbranched polymer, a long chain is introduced into the hydroxyl-terminated hyperbranched polymer, and Continue phosphorylation at the unmodified hydroxyl group to synthesize a linear-hyperbranched phosphate polymer; the present invention introduces an alkyl long chain to increase lipophilicity, and modifies the terminal hydroxyl group into a phosphate group, and the prepared polymer has Multi-terminal hydrophilic groups and hydrophobic groups can be used as surfactants, and can impart special properties such as dispersibility, flame retardancy, antibacterial and antistatic properties, and have excellent surface activity and biocompatibility.

Description

technical field [0001] The invention belongs to the technical field of chemical industry, in particular to a linear-hyperbranched phosphate salt surfactant and a preparation method thereof. Background technique [0002] Linear-hyperbranched polymer refers to a linear long-chain group or a linear block long chain at one end, and a hyperbranched polymer at the other end, which has several hydrophilic and lipophilic groups, making linear-hyperbranched surfactants With versatility and better surface activity. Meanwhile, hyperbranched polymers have a highly branched three-dimensional structure, which exhibit properties quite different from linear molecules, such as low viscosity, no chain entanglement, and good compatibility. In addition, hyperbranched macromolecules contain multiple end group molecules, and corresponding properties can be obtained through end group modification. [0003] Phosphate ester salt surfactants have good emulsifying, dispersing, wetting, solubilizing,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01F17/14B01F17/52B01F17/34B01F17/38B01F17/22B01F17/28C07F9/09C08G83/00C09K23/14C09K23/22C09K23/28C09K23/34C09K23/38C09K23/52
CPCC07F9/091C08G83/005C08G83/006C09K23/14
Inventor 王学川郭笑笑王海军强涛涛
Owner 广东方中高新材料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com