Flattened iron nitride magnetic powder and preparation method thereof

A ferromagnetic nitride and flattening technology, which is applied in the direction of magnetic materials, magnetic objects, inorganic materials, etc., can solve the problem of reducing the magnetization of the system

Active Publication Date: 2016-08-17
东阳市顶峰磁材有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But a new problem has emerged, aluminum oxide and silicon oxide are non-magnetic components, which reduces the magnetization of the system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The steps are:

[0037] 1) Material preparation

[0038] Choose atomized iron powder with an average particle size of 2 μm as the raw material;

[0039] 2) Flattening by ball milling

[0040] Put the iron powder into the ball mill tank, select the ball-to-material ratio as 5:1, select n-hexane as the medium, control the speed of the ball mill to 300r / min, and control the ball milling time to 10h to obtain flake iron powder with good flattening effect;

[0041] 3) oxidation

[0042] Take out the flattened iron powder, place it in a heat treatment furnace, and pass O at a constant rate 2 , oxidized at 300°C for 10 hours to obtain flattened iron oxide;

[0043] 4) restore

[0044] Introduce hydrogen and reduce at 300°C for 20 hours to regain flattened iron powder;

[0045] 5) Nitriding

[0046] Introduce ammonia gas, nitriding at 120°C for 30h; lower the temperature, cool to room temperature with the furnace, and take out the sample.

[0047] The sample prepared in...

Embodiment 2

[0049] The steps are:

[0050] 1) Material preparation

[0051] Select hydroxyl iron powder with an average particle size of 10 μm as the raw material;

[0052] 2) Flattening by ball milling

[0053] Put the iron powder into the ball mill tank, select the ball-to-material ratio as 10:1, choose anhydrous ethanol as the medium, control the speed of the ball mill to 400r / min, and control the ball mill time to 6h to obtain flake iron powder with good flattening effect;

[0054] 3) oxidation

[0055] Take out the flattened iron powder, place it in a heat treatment furnace, and pass O at a constant rate 2 , oxidized at 320°C for 8 hours to obtain flattened iron oxide;

[0056] 4) restore

[0057]Introduce hydrogen and reduce at 320°C for 16 hours to regain flattened iron powder;

[0058] 5) Nitriding

[0059] Introduce ammonia gas, nitriding at 140°C for 15h; lower the temperature, cool to room temperature with the furnace, and take out the sample.

[0060] The sample prepar...

Embodiment 3

[0062] The steps are:

[0063] 1) Material preparation

[0064] Choose reduced iron powder with an average particle size of 40 μm as the raw material;

[0065] 2) Flattening by ball milling

[0066] Put the iron powder into the ball mill tank, select the ball-to-material ratio as 15:1, choose anhydrous ethanol as the medium, control the speed of the ball mill to 500r / min, and control the ball mill time to 2h to obtain flake iron powder with good flattening effect;

[0067] 3) oxidation

[0068] Take out the flattened iron powder, place it in a heat treatment furnace, and pass O at a constant rate 2 , oxidized at 340°C for 6h to obtain flattened iron oxide;

[0069] 4) restore

[0070] Introduce hydrogen and reduce at 340°C for 12 hours to regain flattened iron powder;

[0071] 5) Nitriding

[0072] Introduce ammonia gas, nitriding at 160°C for 6h; lower the temperature, cool to room temperature with the furnace, and take out the sample.

[0073] The sample prepared in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to flattened iron nitride magnetic powder and a preparation method thereof. The preparation method includes: adopting a wet ball milling method, adopting normal hexane or anhydrous alcohol as a medium, selecting a ball-material ratio as 5:1-20:1, controlling rotating speed of a ball mill to be 300-600 r / min, and controlling ball milling time to be 0.1-10 h to obtain flaky iron powder having good flattening effect; feeding O2 for oxidation for 1-10 h at 300-400 DEG C to obtain flattened iron oxide; feeding hydrogen for reduction for 4-20 h at 300-400 h to re-obtain flattened iron powder; feeding ammonia for nitridation for 1-30 h at 120-200 DEG C. By flattening iron powder, surface area of the iron powder of unit volume is increased effectively, and nitriding is facilitated; the iron powder after going through ball milling is large in internal stress, many in defect and conducive to nitrogen seepage.

Description

technical field [0001] The invention relates to a flat iron nitride magnetic powder and a preparation method thereof, belonging to the field of material preparation. Background technique [0002] With the advancement of science and technology, the development of society, and the acceleration of people's life rhythm, information has attracted more and more people's attention, and the information age has come. The development of information carrier materials has become a hot topic, and information recording, especially magnetic recording, is closely related to people's production and life. Magnetic recording technology products, such as tapes, disks, and magnetic drums, have been widely used by people. Fe-N thin films have attracted people's attention because of their high saturation magnetization, low coercive force, high magnetic permeability, wear resistance and corrosion resistance, and high application value. [0003] With the change of nitrogen content, iron nitride ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01F1/03B22F1/00B22F9/04
CPCH01F1/0311B22F9/04B22F2009/043B22F1/068
Inventor 彭晓领杨艳婷李静王攀峰徐靖才金红晓洪波金顶峰王新庆葛洪良
Owner 东阳市顶峰磁材有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com