Blood material for ancient building materials and preparation method thereof

A technology of ancient buildings and blood materials, which is applied in the field of blood materials for building materials, can solve the problems of single components of blood materials and insufficient viscosity, and achieve the effects of improved dispersibility, good viscosity, and enhanced pulling force

Active Publication Date: 2018-12-18
山西省古建筑集团工程有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solve the technical problems of the existing blood materials with single components and insufficient viscosity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The blood material used for ancient building materials in Example 1 of the present invention is made of the following raw materials in parts by weight: 90 parts of pig plasma with a water content lower than 50%, 10 parts of quicklime water, 15 parts of activated carbon, light calcium 10 parts of powder and 2 parts of hypocrellin. The particle size of the activated carbon is 1-10 μm, and the particle size of the light calcium powder is 200-800 nm.

[0024] Wherein, the quicklime water is obtained by adding quicklime into water to dissolve according to the mass ratio of quicklime and water of 1:9.

[0025] The preparation method of the blood material that is used for ancient building material in the present embodiment 1, comprises the following steps:

[0026] Step 1. Prepare pig plasma with a water content lower than 50%: coagulate the pig blood, then filter to remove the serum to obtain a pig blood clot; then grind the pig blood clot, re-coagulate, and then filter to r...

Embodiment 2

[0030] The blood material used for ancient building materials in Example 2 of the present invention is made of the following raw materials in parts by weight: 85 parts of pig plasma with a water content lower than 50%, 8 parts of quicklime water, 12 parts of activated carbon, light calcium 8 parts of powder and 1 part of hypocrellin. The particle size of the activated carbon is 1-10 μm, and the particle size of the light calcium powder is 200-800 nm.

[0031] Wherein, the quicklime water is obtained by adding quicklime into water to dissolve according to the mass ratio of quicklime and water of 1:8.

[0032] The preparation method of the blood material used for ancient building materials in Example 2 is the same as that in Example 1.

Embodiment 3

[0034] The blood material used for ancient building materials in Example 2 of the present invention is made from raw materials comprising the following parts by weight: 95 parts of pig plasma with a water content lower than 50%, 15 parts of quicklime water, 18 parts of activated carbon, light calcium 15 parts of powder and 3 parts of hypocrellin. The particle size of the activated carbon is 1-10 μm, and the particle size of the light calcium powder is 200-800 nm.

[0035] Wherein, the quicklime water is obtained by adding quicklime into water to dissolve according to the mass ratio of quicklime and water of 1:10.

[0036] The preparation method of the blood material used for ancient building materials in this embodiment 3 is the same as that in embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a blood material for a historic building material and a preparation method of the blood material. The blood material is prepared from, by weight, pig plasma, quicklime water, activated carbon, light calcium carbonate powder and hypocrellin. The preparation method comprises the steps that all raw materials are prepared, and activated carbon and light calcium carbonate powder are ground, mixed to be uniform and loaded before being added into pig plasma; hypocrellin is added into quicklime water; the two mixtures are mixed to be uniform, and standing is conducted to obtain the blood material. When applied to preparation of ash oil loam, the obtained blood material can be well organically-inorganically compounded with ash oil and brick dust, and an excellent bonding effect is achieved. The tension of the ash oil loam obtained by being mixed with the blood material is enhanced, and the ash oil loam does not crack after being smeared and dried, is easy to polish, has excellent waterproof, anticorrosion and antibacterial properties, is especially suitable for repairing and filling of the historic building material, achieves an excellent wood filling effect when used for historic building wood particularly, and meanwhile is resistant to water, corrosion and bacteria.

Description

technical field [0001] The invention relates to the technical field of blood materials for building materials, in particular to blood materials used for ancient building materials and a preparation method thereof. Background technique [0002] Blood matter, a paint made from the blood of livestock, has the function of bonding, and also has the function of repelling moisture and insects. At present, the traditional method of making blood material is as follows: soak air-hardened lime into a thinner lime slurry, pour a small amount of it into the blood bucket after passing through the iron gauze grate, and stir it slightly at any time. Within one or two hours, The blood water changes, the foam rises and becomes jelly-like, that is, the blood material is formed. The main application of blood material is to mix it with gray oil, brick ash and other substances to obtain gray oil putty, which is used for repairing or filling of ancient building materials, especially for filling o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 董学明
Owner 山西省古建筑集团工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com