Railway vehicle wheel and heat treatment method thereof

A heat treatment method and technology for railway vehicles, applied in heat treatment furnaces, heat treatment equipment, wheels, etc., can solve problems such as service performance decline and wheel structure becoming brittle, and achieve balanced mechanical properties, reduced hardness gradient, high strength hardness and plastic toughness. Effect

Active Publication Date: 2019-01-22
TAIYUAN HEAVY IND
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in recent years, with the needs of heavy-duty railway transportation, the requirements for the hardness, wear resistance and load capacity of the wheel 1 are getting higher and higher, and the carbon content of the wheel 1 is getting higher and higher. Quenching with water is difficult to avoid the formation of bainite on the surface of the wheel, which makes the wheel structure brittle and reduces service performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Railway vehicle wheel and heat treatment method thereof
  • Railway vehicle wheel and heat treatment method thereof
  • Railway vehicle wheel and heat treatment method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] Example embodiments will now be described more fully with reference to the accompanying drawings. Example embodiments may, however, be embodied in many forms and should not be construed as limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the concept of example embodiments to those skilled in the art. The same reference numerals in the drawings denote the same or similar structures, and thus their detailed descriptions will be omitted.

[0037] In the following description of various examples of the invention, reference is made to the accompanying drawings, which form a part hereof, and in which are shown by way of illustration various exemplary structures, systems and steps which may implement aspects of the invention. It is to be understood that other specific arrangements of components, structures, exemplary means, systems and steps may be utilized and stru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a railway vehicle wheel heat treatment method and a railway vehicle wheel formed through the method. The railway vehicle wheel heat treatment method includes the following steps that firstly, the wheel is integrally heated and subjected to complete austenitizing; secondly, constant-pressure and small-flow spray water is used for conducting short-time cooling on the tread of the wheel; and thirdly, continuous and controllable water volume stepped spray water is used for conducting quenching on the tread of the wheel, a balanced cooling speed is formed below the tread of the wheel, and therefore a balanced fine pearlite structure is obtained in a rim area of the whole wheel. According to the railway vehicle wheel heat treatment method and the railway vehicle wheel formed through the method, small flow under relatively high water pressure is used for eliminating a film boiling stage or shortening the film boiling stage, meanwhile, the phenomenon that bainite is formed due to the relatively high cooling speed is avoided, afterwards, continuous and controllable water volume stepped spray water is adopted for quenching, the balanced cooling speed is formed under the tread of the wheel, the balanced fine pearlite structure is obtained in the whole rim area, and therefore the balanced mechanical performance is obtained, relatively high hardness and plasticity are achieved, and the hardness gradient in the wheel abrasion direction is reduced.

Description

technical field [0001] The present invention relates generally to railway vehicle wheels and, in particular, to a method of heat treating railway vehicle wheels. Background technique [0002] Railway vehicle wheels are generally produced by casting or forging, followed by heat treatment. The wheel 1 type is usually as follows figure 1 As shown, the weight of the wheel 1 is generally about 500KG, and the material is carbon steel. The part of the wheel 1 in contact with the track is the rim 11 , and the contact surface is the tread 12 . [0003] For a long time, the main heat treatment method of railway wheel 1 is to heat the whole wheel 1 to austenitize, and then spray water to cool and quench the tread surface 12. This heat treatment method requires quenching in the wheel rim 11 area to obtain excellent fine pearlite structure and very Important compressive stress, while normalizing treatment is achieved on the web and hub to obtain better toughness. [0004] However, in r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D9/34C21D1/18B60B17/00
CPCB60B17/00B60B2310/542C21D1/18C21D9/34C21D2211/009
Inventor 贾托胜张晓峰薛川高康魏华成赵兴龙
Owner TAIYUAN HEAVY IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products