A low-cost low-halogen transparent polypropylene film material and its preparation method

A transparent polypropylene and film material technology, applied in the field of film materials, can solve the problems of poor thermal resistance of polypropylene film, affect the transparency of polypropylene film, and easily produce toxic and harmful corrosive gases, etc., so as to achieve the improvement of mechanical properties, Low cost, low impact effect

Active Publication Date: 2019-02-26
四川潽鑫科技集团有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is that the heat resistance performance of polypropylene film containing halogenated flame retardant is poor, and it is easy to produce toxic and harmful corrosive gas, which affects the transparency of polypropylene film. The purpose is to provide a low-cost and low-cost The halogen transparent polypropylene film material and its preparation method have the advantages of low halogen content, good transparency, low cost and aging resistance, and can be widely used in electronic appliances, building interior decoration materials, components and electronic product packaging materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-cost low-halogen transparent polypropylene film material and its preparation method
  • A low-cost low-halogen transparent polypropylene film material and its preparation method
  • A low-cost low-halogen transparent polypropylene film material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A low-cost low-halogen transparent polypropylene film material, made of the following raw materials in parts by weight:

[0029]

[0030]

[0031] Among them, the polypropylene resin is a combination of homopolypropylene resin and copolymerized polypropylene resin, and the weight ratio of the two is 2:1; the modifier is polyethylene, maleic anhydride grafted PP, acrylic acid copolymer and transparent nucleating agent The combination of the agent and the weight ratio is 5:5:1:0.1; the flame retardant is the combination of hypophosphite, melamine, brominated phosphate, tetrabromobisphenol A and magnesium hydroxide, the weight ratio is 8:4:2 :1:1; the flame retardant synergist is a combination of pentaerythritol, zinc oxide and antimony trioxide, the weight ratio is 1:2:0.5; the filler is talcum powder, and the filler fineness is 3000 mesh; the lubricating and dispersing agent is pentaerythritol The combination of stearate and polyethylene wax, the weight ratio of th...

Embodiment 2

[0037] A low-cost low-halogen transparent polypropylene film material, made of the following raw materials in parts by weight:

[0038]

[0039] Among them, the polypropylene resin is a combination of homopolypropylene resin and copolymerized polypropylene resin, and the weight ratio of the two is 2:1; the modifier is polyethylene, maleic anhydride grafted PP, acrylic acid copolymer and transparent nucleating agent The combination of the agent and the weight ratio is 5:5:1:0.1; the flame retardant is the combination of hypophosphite, melamine, brominated phosphate, tetrabromobisphenol A and magnesium hydroxide, the weight ratio is 8:4:2 :1:1; the flame retardant synergist is a combination of pentaerythritol, zinc oxide and antimony trioxide, the weight ratio is 1:2:0.5; the filler is talcum powder, the filler fineness is 3500 mesh; the lubricating and dispersing agent is pentaerythritol The combination of stearate and polyethylene wax, the weight ratio of the two is 5:1; th...

Embodiment 3

[0045]A low-cost low-halogen transparent polypropylene film material, made of the following raw materials in parts by weight:

[0046]

[0047]

[0048] Among them, the polypropylene resin is a combination of homopolypropylene resin and copolymerized polypropylene resin, and the weight ratio of the two is 2:1; the modifier is polyethylene, maleic anhydride grafted PP, acrylic acid copolymer and transparent nucleating agent The combination of the agent and the weight ratio is 5:5:1:0.1; the flame retardant is the combination of hypophosphite, melamine, brominated phosphate, tetrabromobisphenol A and magnesium hydroxide, the weight ratio is 8:4:2 :1:1; the flame retardant synergist is a combination of pentaerythritol, zinc oxide and antimony trioxide, the weight ratio is 1:2:0.5; the filler is talcum powder, the filler fineness is 3500 mesh; the lubricating and dispersing agent is pentaerythritol The combination of stearate and polyethylene wax, the weight ratio of the two...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-cost and low-halogen transparent polypropylene film material and a preparation method thereof. The material is prepared from the following raw materials in parts by weight: polypropylene resin, a modification agent, a flame retardant, an antioxidant, a lubrication dispersing agent, terpene resin, an antistatic agent and the like, and is prepared by the steps of mixing the raw materials by using a high speed mixer, granulating by using a twin-screw extruder to obtain polypropylene resin granules, then adding the polypropylene resin granules into a three-roll calendered sheet extrusion molding machine to obtain the low-cost and low-halogen transparent polypropylene film material. The transparent polypropylene film material has the advantages of being low in cost, low in halogen content, good in transparency, and the like, can realize a UL-94 VTM-0 flame-retardant grade at 0.3mm or more, and maintains good high voltage breakdown resistance of polypropylene.

Description

technical field [0001] The invention relates to a film material, in particular to a low-cost low-halogen transparent polypropylene film material and a preparation method thereof. Background technique [0002] Polypropylene, English name: Polypropylene, abbreviated name PP. Its chemical formula is: (C 3 h 6 ) N. [0003] Polypropylene resin is a semi-crystalline thermoplastic. It has excellent properties such as non-toxic, light density, easy processing, chemical corrosion resistance, good electrical insulation, and good mechanical strength. It is widely used in daily necessities, electronic appliances, interior decoration materials, packaging materials, transportation, electromechanical and building materials, etc. Many fields. However, PP is a flammable material, and its oxygen index (LOI) is only 17.4 to 18.5. When burning, a large number of molten droplets are easily spread, which limits the application of PP in many fields. For the flame retardancy of PP, halogen-c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L23/14C08L91/00C08L71/02C08L23/06C08L51/06C08L33/02C08L45/00C08K13/02C08K3/32C08K5/3492C08K5/521C08K3/22C08K5/053C08K3/34
CPCC08L23/12C08L2201/02C08L2201/10C08L2203/14C08L2205/02C08L2205/035C08L2205/08C08L23/14C08L91/00C08L71/02C08L23/06C08L51/06C08L33/02C08L45/00C08K13/02C08K3/32C08K5/34922C08K5/521C08K2003/2224C08K5/053C08K2003/2296C08K3/2279C08K3/34
Inventor 李祚鑫张小林李剑铭
Owner 四川潽鑫科技集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap