Photo refraction double-doped potassium sodium strontium barium niobate single crystal and preparation method thereof

A technology of barium strontium niobate and single crystal, which is applied in the field of optical materials, can solve the problems of unseen polycrystalline preparation, etc., and achieve the effects of improving the ability to resist light damage, improving the ability to resist light damage, and reducing time and energy consumption

Inactive Publication Date: 2017-03-29
HEILONGJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no report of chromium-gallium double-doping or nickel-gallium double-doping in patents or journal literature, and there is no preparation method combining polycrystalline preparation and pulling method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A photorefractive double-doped potassium sodium strontium barium niobate single crystal, wherein the molecular formula of potassium sodium strontium barium niobate is (KNa) 0.1 (Sr 0.65 Ba 0.35 ) 0.9 Nb 2 o 6 , while doping the oxides of Cr and Gr, taking the content of potassium, sodium, strontium and barium niobate as a reference, the doping content is: Cr 2 o 3 The content is 0.2mol%, Gr 2 o 3 The content is 1 mol%.

[0021] The preparation method of the above-mentioned photorefractive double-doped potassium sodium strontium barium niobate single crystal comprises the following steps:

[0022] (1) Weigh the raw materials containing corresponding metal elements according to the proportion, BaCO 3 , SrCO 3 、K 2 CO 3 、Na 2 CO 3 and Nb 2 o 5 , according to the molecular formula (KNa) 0.1 (Sr 0.65 Ba 0.35 ) 0.9 Nb 2 o 6 Weigh the ingredients; weigh Cr containing the blended content 2 o 3 、Gr 2 o 3 ; Prepare solid ammonium acetate by 12-18% of the t...

Embodiment 2

[0028] The difference from Example 1 is that the content of Cr and Gr added is: Cr 2 o 3 The content is 0.2mol%, Gr 2 o 3 The content is 1.8 mol%.

[0029] It was found through experiments that at 40mW / cm 2 The writing time constant measured under the total writing light intensity is between 23-31s, which is much smaller than the writing time constant of pure potassium sodium strontium barium niobate single crystal, and also smaller than that of single chromium-doped potassium sodium strontium barium niobate single crystal. The time constant is in the range of 43-65s; the light damage resistance and optical uniformity are also significantly better than pure potassium sodium strontium barium niobate single crystal.

Embodiment 3

[0031] The difference from Example 1 is that the content of Cr and Gr added is: Cr 2 o 3 The content is 0.5mol%, Gr 2 o 3 The content is 1 mol%. It was found through experiments that at 40mW / cm 2 The writing time constant measured under the total writing light intensity is between 17-24s, which is much smaller than the writing time constant of pure potassium sodium strontium barium niobate single crystal, and also smaller than that of single chromium-doped potassium sodium strontium barium niobate single crystal. The time constant is in the range of 43-65s; the light damage resistance and optical uniformity are also significantly better than pure potassium sodium strontium barium niobate single crystal.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a photo refraction double-doped potassium sodium strontium barium niobate single crystal. Two kinds of metal oxide are doped into (KNa)0.1(Sr0.65Ba0.35)0.9Nb2O6 crystals, one kind is Cr2O3 or Ni2O3, and the other kind is Cr2O3; when the metal oxide is a combination of Cr2O3 and Gr2O3, the content of Cr2O3 is 0.2-0.5 mol%%, and the content of Gr2O3 is 1-1.8 mol%; when the metal oxide is a combination of Ni2O3 and Gr2O3, the content of Ni2O3 is 0.1-0.4 mol%, and the content of Gr2O3 is 1-1.6 mol%. The product has the advantages of being high in sensitivity to weak light, high in optical damage resistance and high in record response speed in photo refraction application. The invention further discloses a preparation method of the photo refraction double-doped potassium sodium strontium barium niobate single crystal. The preparation method comprises the procedures of raw material preparation, ball milling, heating, stirring and reacting, temperature rise lifting and drawing, high temperature annealing, polarization and the like, and has the advantages of being simple in process step, good in finished product quality and low in energy consumption.

Description

technical field [0001] The invention relates to the field of optical materials, in particular to a photorefractive double-doped potassium sodium strontium barium niobate single crystal and a preparation method thereof. Background technique [0002] Photorefractive material is an excellent holographic optical storage material, and has been widely used in the field of holographic optical storage. Photorefractive materials store holograms or optical data through the photorefractive effect. The so-called photorefractive effect means that when a weak laser light from the outside shines on the photorefractive crystal, the carriers in the crystal are excited, and in the crystal Migration and re-entrapment in the crystal, resulting in a space charge field inside the crystal, and then through the electro-optic effect, the spatial distribution of the refractive index in the crystal is changed, thereby changing the process of the refractive index of the material. It is the "damage" an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C30B29/30C30B15/00
CPCC30B15/00C30B29/30
Inventor 石宏新任常愚田雪松王丰丁红伟金永君李娜尹向宝
Owner HEILONGJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com