Adhesive for dye-sublimation transfer printing, and synthesis process thereof

A synthesis process and adhesive technology, applied in the direction of adhesives, adhesive additives, epoxy resin glue, etc., can solve the problems of scratch resistance, adhesion, water resistance and high temperature resistance, etc., and achieve environmental protection in the preparation process No pollution, high adhesion, good physical properties

Inactive Publication Date: 2017-04-19
SUZHOU JIGU NEW MATERIAL CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although many companies have developed a variety of thermal transfer adhesives for bonding layers in recent years, their scratch resistance, adhesion, water resistance and high temperature resistance are not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive for dye-sublimation transfer printing, and synthesis process thereof
  • Adhesive for dye-sublimation transfer printing, and synthesis process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In this embodiment, the adhesive components include 40 parts by weight of bisphenol A epoxy resin, 10 parts of polyurethane resin, 3 parts of toughening agent, 3 parts of sodium acrylate, 3 parts of glycerin, ethylene-acetic acid 5 parts of ethylene copolymer, 5 parts of oil-absorbing filler, 3 parts of organic bentonite, 4 parts of kaolin, 2 parts of antioxidant, 5 parts of ethylene glycol and 1 part of nano silicon oxide.

[0019] The synthesis technique of the present embodiment comprises the following steps:

[0020] A. Mix bisphenol A epoxy resin, polyurethane resin, toughening agent, sodium acrylate, glycerol, and ethylene-vinyl acetate copolymer and add them to the stirring tank for stirring. The stirring tank speed is 3000 rpm, and the stirring time For 20min, stand still to obtain mixture A;

[0021] B. Add oil-absorbing filler, organic bentonite, kaolin, antioxidant, ethylene glycol, and nano-silicon oxide to the mixture A. After mixing, add it to the reactio...

Embodiment 2

[0024] In this embodiment, the adhesive components include 60 parts by weight of bisphenol A epoxy resin, 20 parts of polyurethane resin, 8 parts of toughening agent, 8 parts of sodium acrylate, 10 parts of glycerol, ethylene-acetic acid 12 parts of ethylene copolymer, 12 parts of oil-absorbing filler, 8 parts of organic bentonite, 10 parts of kaolin, 8 parts of antioxidant, 15 parts of ethylene glycol and 4 parts of nano silicon oxide;

[0025] The synthesis technique of the present embodiment comprises the following steps:

[0026] A. Mix bisphenol A epoxy resin, polyurethane resin, toughening agent, sodium acrylate, glycerol, and ethylene-vinyl acetate copolymer and add them to the stirring tank for stirring. The stirring tank speed is 5000 rpm, and the stirring time For 40min, stand still to obtain mixture A;

[0027] B. Add oil-absorbing filler, organic bentonite, kaolin, antioxidant, ethylene glycol and nano-silicon oxide to the mixture A, mix and add to the reaction ke...

Embodiment 3

[0030] In this embodiment, the adhesive components include 45 parts by weight of bisphenol A epoxy resin, 12 parts of polyurethane resin, 4 parts of toughening agent, 4 parts of sodium acrylate, 4 parts of glycerin, ethylene-acetic acid 6 parts of ethylene copolymer, 6 parts of oil-absorbing filler, 4 parts of organic bentonite, 5 parts of kaolin, 3 parts of antioxidant, 6 parts of ethylene glycol and 2 parts of nano silicon oxide.

[0031] The synthesis technique of the present embodiment comprises the following steps:

[0032] A. Mix bisphenol A epoxy resin, polyurethane resin, toughening agent, sodium acrylate, glycerol, and ethylene-vinyl acetate copolymer and add them to the stirring tank for stirring. The rotating speed of the stirring tank is 3500 rpm, and the stirring time For 25min, stand still to obtain mixture A;

[0033] B. Add oil-absorbing filler, organic bentonite, kaolin, antioxidant, ethylene glycol and nano-silicon oxide to the mixture A. After mixing, add i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an adhesive for dye-sublimation transfer printing, and a synthesis process thereof. The adhesive comprises the following components in parts by weight: 40-60 parts of bisphenol-A epoxy resin, 10-20 parts of polyurethane resin, 3-8 parts of flexibilizer, 3-8 parts of sodium acrylate, 3-10 parts of glycerol, 5-12 parts of ethylene-vinlacetate copolymer, 5-12 parts of oil-absorbing filler, 3-8 parts of organic bentonite, 4-10 parts of kaolin, 2-8 parts of antioxidant, 5-15 parts of ethylene glycol and 1-4 parts of nano-silicon dioxide. The preparation method disclosed by the invention is simple, and environment-friendly and pollution-free in preparation process; and the prepared adhesive is high in adhesion force, and excellent in high-temperature resistance and scratch resistance.

Description

technical field [0001] The invention relates to the technical field of thermal sublimation transfer material preparation, in particular to an adhesive for thermal sublimation transfer printing and a synthesis process thereof. Background technique [0002] Thermal transfer printing is a newly emerging special printing technology in recent years. Its principle is to directly contact the transfer printing film with the pattern on the substrate, and through the heating and pressure of the thermal transfer head and the impression cylinder, the ink on the transfer film The graphic layer is melted and transferred to the substrate. The most important material in thermal transfer printing technology is the transfer film, and the research and development of materials related to thermal transfer film such as carrier layer, release layer, protective layer, ink layer, and adhesive layer is still in its infancy. The coatings are closely related and affect each other. Among them, the bon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C09J175/04C09J123/08C09J11/04C09J11/06
CPCC09J163/00C08K2201/014C08L2201/08C08L2205/03C09J11/04C09J11/06C08L75/04C08L23/0853C08K13/06C08K5/098C08K5/053C08K9/04C08K3/346C08K3/36
Inventor 戚裕
Owner SUZHOU JIGU NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap