Multi-coating bio-degradable metal support and preparation method thereof

A metal stent, multi-coating technology, applied in the field of medical devices, can solve the problems of uncontrollable service life and curative effect of stents, complicated manufacturing process of magnesium stents, uncontrollable degradation time, etc. restenosis effect

Active Publication Date: 2017-05-17
万瑞飞鸿(北京)医疗器材有限公司
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] It can be seen that due to the need for additional corrosion-resistant treatment, the manufacturing process of magnesium stents is more complicated, and the degradation time is uncontrollable, resulting in uncontrollable service life and curative effect of the stent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-coating bio-degradable metal support and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Such as figure 1 As shown, it is a multi-coated biodegradable metal stent of the present invention,

[0054] It includes: a stent body 1, a drug coating 2, a first temperature control coating 3 and a second temperature control coating 4; the inner surface of the stent body 1 is provided with a first temperature control coating 3, and the outer surface is provided with a second temperature control coating. Temperature coating 4; The drug coating 2 is arranged on the outer surface of the second temperature control coating 4;

[0055] The bracket body 1 is made of pure magnesium;

[0056] The first temperature-controlling coating 3 and the second temperature-controlling coating 4 are degradable polymer layers with blood-cooling, antipyretic and temperature-controlling molecules;

[0057] The drug coating 2 is a composite degradable drug coating with drugs for inhibiting intimal hyperplasia, PDLLA and PLLA.

[0058] Preparation Process:

[0059] The high-purity magnesiu...

Embodiment 2

[0071] Such as figure 1 As shown, it is a multi-coated biodegradable metal stent of the present invention,

[0072] It includes: a stent body 1, a drug coating 2, a first temperature control coating 3 and a second temperature control coating 4; the inner surface of the stent body 1 is provided with a first temperature control coating 3, and the outer surface is provided with a second temperature control coating. Temperature coating 4; The drug coating 2 is arranged on the outer surface of the second temperature control coating 4;

[0073] The bracket body 1 is made of magnesium alloy;

[0074] The first temperature-controlling coating 3 and the second temperature-controlling coating 4 are degradable polymer layers with blood-cooling, antipyretic and temperature-controlling molecules;

[0075] The drug coating 2 is a composite degradable drug coating with drugs for inhibiting intimal hyperplasia, PDLLA and PLLA.

[0076] Preparation Process:

[0077] The magnesium alloy tub...

Embodiment 3

[0090] With embodiment 1, difference is:

[0091] The thickness of the stent body is 90 μm;

[0092] The thickness of the first temperature control coating is 10 μm;

[0093] The thickness of the second temperature control coating is 2 μm;

[0094] The thickness of the drug coating is 5 μm;

[0095] The degradable polymer with blood-cooling, antipyretic and temperature-controlling molecules is a mixed solution of acetaminophen, polyglycolic acid, polylactic acid and polyglycolic acid copolymer (the mixing ratio is 0.5:0.5:1:1).

[0096] The results of the stent test were similar to Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multi-coating bio-degradable metal support. The multi-coating bio-degradable metal support comprises a support body, a medicine coating, a first temperature-control coating and a second temperature-control coating; an inner surface of the support body is provided with the first temperature-control coating, and an outer surface is provided with a second temperature-control coating; and the medicine coating is arranged at the outer surface of the second temperature-control coating. The invention also discloses a preparation method of the metal support. The multi-coating bio-degradable metal support is long in service life, good in curative effect, high in supporting force, and good in biological safety.

Description

technical field [0001] The invention relates to the field of medical instruments. More specifically, it relates to a multi-coated biodegradable metal stent and a preparation method thereof. Background technique [0002] At present, the main method for treating cardiac artery stenosis is long-term implantation of metal stents. However, the implantation of metal stents still has some disadvantages, such as thrombus formation leading to restenosis of blood vessels at the implantation site, long-term local inflammatory response, stimulation of surrounding tissues, mechanical behavior of stent implantation and no stent Mismatch, etc., making it problematic for long-term use. Therefore, it is urgent to develop a human degradable and absorbable stent as a coronary stent. [0003] For the more mature biodegradable polymer scaffolds, because their mechanical properties cannot meet the requirements, in order to improve the strength of the scaffolds, the volume must be increased, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/58A61L27/54A61L27/34A61L27/18A61L27/04A61F2/82
Inventor 唐文军王海军
Owner 万瑞飞鸿(北京)医疗器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com