Catalyst components, catalyst systems and applications thereof for olefin polymerization

An olefin polymerization and catalyst technology, which is applied in the field of catalyst components for olefin polymerization, can solve the problems of high preparation cost and narrow molecular weight distribution of olefin polymers.

Active Publication Date: 2021-03-16
CHINA PETROLEUM & CHEM CORP +1
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation cost of this type of compound is high, and the molecular weight distribution of the prepared olefin polymer is narrow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst components, catalyst systems and applications thereof for olefin polymerization
  • Catalyst components, catalyst systems and applications thereof for olefin polymerization
  • Catalyst components, catalyst systems and applications thereof for olefin polymerization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0116] Take 10 g of the above-mentioned dialkoxymagnesium carrier, 50 mL of toluene, and 0.8 g of compound internal electron donor 1 to prepare a suspension. In a 300mL reaction kettle that has been repeatedly replaced with high-purity nitrogen, add 40mL of toluene and 60mL of titanium tetrachloride, raise the temperature to 65°C, then slowly add the prepared suspension into the kettle, keep the temperature at 65°C for 1 hour, and slowly raise the temperature to 110°C, when the temperature rises to 80°C, add 2.2g of compound internal electron donor 1, keep the temperature at 110°C for 1 hour, press filter to obtain a solid. The obtained solid was washed twice with 150 mL of toluene, and the liquid was removed by pressure filtration. A mixed solution of 90 mL of toluene and 60 mL of titanium tetrachloride was added and stirred at 110° C. for 1 hour, and treated twice in this way. Press filtration, wash the obtained solid once with toluene and 4 times with 150 mL of hexane, pre...

Embodiment 2-15

[0118] The internal electron donors were replaced with 3.0 g each of compound internal electron donors 2-15, and other steps were the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a catalyst component and a catalyst system for olefin polymerization and an application thereof. The catalyst component provided by the invention consists of titanium, magnesium, halogen, and internal electron donor, wherein the internal electron donor comprises 2,2'-dialkyl-1,3-dicarbonate ester compound shown as formula (I) and 2-cyano-2,3-alkyl succinate dialkyl ester compound shown as formula (II). The catalyst component and the catalyst system comprising same provided by the invention are applicable to the development of polyolefin, particularly polypropylene, resin. (img file='DDA0000982168490000011.TIF' wi='1097' he='411' / ).

Description

technical field [0001] The invention belongs to the field of catalysts, and in particular relates to a catalyst component for olefin polymerization, a catalyst system and applications thereof. Background technique [0002] A solid titanium catalyst component based on magnesium, titanium, halogen and an electron donor, known in the art as a Ziegler-Natta catalyst, can be used for CH 2 =CHR Polymerization of olefins, especially in the polymerization of α-olefins with 3 carbon atoms or more, can give polymers with higher yield and higher stereoregularity. It is well known that electron donor compounds are one of the essential components in Ziegler-Natta catalyst components. From the early disclosed monobasic carboxylic acid ester compounds, such as ethyl benzoate, to the widely used dibasic aromatic carboxylic acid ester compounds, such as di-n-butyl phthalate or diisobutyl phthalate, Then to the recently disclosed 1,3-diethers (CN1020448C), succinates (CN1313869) and 1,3-dio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F110/06C08F4/649
CPCC08F110/06C08F2410/01C08F4/6494C08F4/6495
Inventor 张锐谭忠周奇龙徐秀东李凤奎宋维玮于金华尹珊珊
Owner CHINA PETROLEUM & CHEM CORP