Fireproof mud used for power cable and preparation method thereof

A power cable and installation technology, applied in the field of fireproof mud for power cable installation and its preparation, can solve the problems of fire resistance, smoke blocking, oil resistance, water resistance, corrosion resistance, poor service life, poor environmental protection and the like, Achieve the effect of ensuring physical strength, increasing service life, and reducing environmental pollution

Inactive Publication Date: 2017-11-17
HEFEI ANLI ELECTRIC POWER ENG CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the current fireproof mud has poor service life and poor environmental protection during use. It has insufficient fire resistance, smoke blocking, oil resistance, water resistance, and corrosion resistance, which cannot meet the needs of the development of the power cable field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of fireproof mud for power cable installation of the present embodiment includes the following raw materials in parts by weight:

[0027] 25 parts of condensed polycyclic aromatic hydrocarbon resin, 15 parts of epoxy resin, 8 parts of chlorinated paraffin, 14 parts of clay, 11 parts of china clay powder, 7 parts of perlite, 6 parts of quartz sand, 5 parts of high alumina bauxite, 2 parts of magnesium hydroxide 6 parts, 6 parts of tributyl citrate, 4 parts of ethylene glycol, 7 parts of ammonium phosphate, 2 parts of antioxidant, 1 part of preservative, and 1 part of antistatic agent.

[0028] In this embodiment, the epoxy value of the epoxy resin is 0.3.

[0029] In this embodiment, the antioxidant includes a hindered phenolic antioxidant and an auxiliary antioxidant, and the weight ratio between them is 3:1.

[0030] In this example, the hindered phenolic antioxidant is 2,6-tertiary butyl-4-methylphenol, and the auxiliary antioxidants are didodecyl alcohol este...

Embodiment 2

[0041] A kind of fireproof mud for power cable installation of the present embodiment includes the following raw materials in parts by weight:

[0042] 27 parts of condensed polycyclic aromatic hydrocarbon resin, 18 parts of epoxy resin, 9 parts of chlorinated paraffin, 16 parts of clay, 12 parts of china clay powder, 8 parts of perlite, 8 parts of quartz sand, 6 parts of high alumina bauxite, 3 parts of magnesium hydroxide parts, 7 parts of tributyl citrate, 5 parts of ethylene glycol, 8 parts of ammonium phosphate, 3 parts of antioxidant, 1.5 parts of preservative, and 2 parts of antistatic agent.

[0043] In this embodiment, the epoxy value of the epoxy resin is 0.35.

[0044] In this embodiment, the antioxidant includes a hindered phenolic antioxidant and an auxiliary antioxidant, and the weight ratio between them is 3:1.

[0045] In this example, the hindered phenolic antioxidant is 2,6-tertiary butyl-4-methylphenol, and the auxiliary antioxidants are didodecyl alcohol e...

Embodiment 3

[0056] A kind of fireproof mud for power cable installation of the present embodiment includes the following raw materials in parts by weight:

[0057] 28 parts of condensed polycyclic aromatic hydrocarbon resin, 20 parts of epoxy resin, 10 parts of chlorinated paraffin, 18 parts of clay, 13 parts of china clay powder, 9 parts of perlite, 9 parts of quartz sand, 7 parts of high alumina bauxite, 4 parts of magnesium hydroxide 8 parts, 8 parts of tributyl citrate, 6 parts of ethylene glycol, 9 parts of ammonium phosphate, 4 parts of antioxidant, 2 parts of preservative, and 3 parts of antistatic agent.

[0058] In this embodiment, the epoxy value of the epoxy resin is 0.4.

[0059] In this embodiment, the antioxidant includes a hindered phenolic antioxidant and an auxiliary antioxidant, and the weight ratio between them is 3:1.

[0060] In this example, the hindered phenolic antioxidant is 2,6-tertiary butyl-4-methylphenol, and the auxiliary antioxidants are didodecyl alcohol est...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses fireproof mud used for installation of a power cable, and belongs to the technical field of fireproof mud. The fireproof mud is composed of, by weight, the raw materials of 25-28 parts of condensed polycyclic aromatic hydrocarbon resin, 15-20 parts of epoxy resin, 8-10 parts of chlorinated paraffin, 14-18 parts of clay, 11-13 parts of porcelain clay powder, 7-9 parts of perlite, 6-9 parts of quartz sand, 5-7 parts of bauxite chamotte, 2-4 parts of magnesium hydroxide, 6-8 parts of tributyl citrate, 4-6 parts of ethylene glycol, 7-9 parts of ammonium phosphate, 2-4 parts of antioxidant, 1-2 parts of anti-corrosion agent and 1-3 parts of antistatic agent. The invention further discloses a preparation method of the fireproof mud used for installation of the power cable. The fireproof mud is easy to prepare, environmentally friendly, low in pollution and good in durability, and has the effects of good fire resistance, corrosion resistance, water resistance and static resistance.

Description

technical field [0001] The invention relates to the technical field of fireproof mud, in particular to a fireproof mud for power cable installation and a preparation method thereof. Background technique [0002] Fireproof mud is a kind of flexible flame-retardant material, which has the characteristics of high fire-resistant limit and low smoke emission. Reduce fire damage. To avoid the expansion of accidents, it has the functions of smoke resistance, fire prevention and dust prevention. Therefore, the plugging material is widely used in vertical and horizontal wire and cable penetration holes in power plants, industrial and mining enterprises, high-rise buildings, shipbuilding power, post and telecommunications, substations, metallurgy and other system engineering. [0003] However, the current fireproof mud has poor service life and poor environmental protection during use. It has insufficient fire resistance, smoke blocking, oil resistance, water resistance, and corrosi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L65/00C08L63/00C08L91/06C08K13/02C08K3/34C08K3/36C08K3/22C08K5/11C08K3/32C08K5/053
CPCC08L65/00C08K2003/2224C08K2003/2227C08K2003/322C08K2201/014C08L2201/02C08L2201/04C08L2201/08C08L2205/035C08L63/00C08L91/06C08K13/02C08K3/34C08K3/346C08K3/36C08K3/22C08K5/11C08K3/32C08K5/053
Inventor 殷世尧
Owner HEFEI ANLI ELECTRIC POWER ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap