High-performance polyester resin powder coating and preparation method thereof

A polyester resin and powder coating technology, applied in powder coatings, polyester coatings, coatings, etc., can solve problems such as poor bending resistance, weak bonding force of substrates, and unsmooth appearance of coatings

Inactive Publication Date: 2018-04-06
GUILIN HEXIN WATERPROOF DECORATION MATERIAL
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the appearance of the existing powder coating coating is not smooth enough, the bonding force with the substrate is weak, and the bending resistance is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance polyester resin powder coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] First, weigh the following components by weight: 35 parts of polyester resin, 10 parts of triglycidyl isocyanurate, 20 parts of rutile titanium dioxide, 10 parts of barium sulfate, 15 parts of calcium carbonate, 5 parts of leveling agent Parts, 5 parts of 1.0% silane coupling agent.

[0015] Then, prepare the coating: weigh each component in proportion, place it in a mixer, crush and mix it for 5-8 minutes, and then place it in a twin-screw extruder with a feeding speed of 1000r / min and a main screw speed of 2500r / min Melt extrusion, while controlling the temperature of the first zone to 90°C and the temperature of the second zone to 100°C, the melted raw materials are placed in a cooling tablet press with a conveyor belt and a tablet press with a speed of 1000r / min, and finally placed in a main mill with a grinding speed of 5000r / min, auxiliary grinding speed 2600r / min grinding system, the grinding particle size of 33 ~ 37um polyester resin powder coating.

Embodiment 2

[0017] First, weigh the following components by weight: 37 parts of polyester resin, 12 parts of triglycidyl isocyanurate, 18 parts of rutile titanium dioxide, 13 parts of barium sulfate, 13 parts of calcium carbonate, and 4 parts of leveling agent Parts, 3 parts of 1.0% silane coupling agent.

[0018] Then, prepare the coating: weigh each component in proportion, place it in a mixer, crush and mix it for 5-8 minutes, and then place it in a twin-screw extruder with a feeding speed of 1000r / min and a main screw speed of 2500r / min Melt extrusion, while controlling the temperature of the first zone to 90°C and the temperature of the second zone to 100°C, the melted raw materials are placed in a cooling tablet press with a conveyor belt and a tablet press with a speed of 1000r / min, and finally placed in a main mill with a grinding speed of 5000r / min, auxiliary grinding speed 2600r / min grinding system, the grinding particle size of 33 ~ 37um polyester resin powder coating.

Embodiment 3

[0020] First, weigh the following components by weight: 40 parts of polyester resin, 15 parts of triglycidyl isocyanurate, 15 parts of rutile titanium dioxide, 15 parts of barium sulfate, 10 parts of calcium carbonate, and 3 parts of leveling agent Parts, 2 parts of 1.0% silane coupling agent.

[0021] Then, prepare the coating: weigh each component in proportion, place it in a mixer, crush and mix it for 5-8 minutes, and then place it in a twin-screw extruder with a feeding speed of 1000r / min and a main screw speed of 2500r / min Melt extrusion, while controlling the temperature of the first zone to 90°C and the temperature of the second zone to 100°C, the melted raw materials are placed in a cooling tablet press with a conveyor belt and a tablet press with a speed of 1000r / min, and finally placed in a main mill with a grinding speed of 5000r / min, auxiliary grinding speed 2600r / min grinding system, the grinding particle size of 33 ~ 37um polyester resin powder coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-performance polyester resin powder coating. The coating is prepared from, by weight, 35-45 parts of polyester resin, 10-20 parts of triglycidyl isocyanurate, 10-20 partsof rutile type titanium dioxide, 10-20 parts of barium sulfate, 5-15 parts of calcium carbonate, 1-5 parts of flow smoothing agent and 1-5 parts of 1.0% silane coupling agent. According to the high-performance polyester resin powder coating, the polyester resin is used as a raw material basis, auxiliary materials such as curing agent, pigments, padding and addition agent are added, the polyester resin powder coating is prepared through scientific and reasonable matching. The invention further provides a preparation method of the powder coating. The method is simple and easy to implement, the prepared powder coating is smooth and flat in appearance, high in binding force with basic materials, resistant to impact, resistant to scratch, good in anti-bending performance and excellent in weather resistance, and the high-performance powder coating meets multi-aspect requirements of the market.

Description

technical field [0001] The invention relates to a waterproof coating, in particular to a high-performance polyester resin powder coating and a preparation method thereof. Background technique [0002] Powder coatings are made of specific chemical substances, after specific preparation processes such as physical or mechanical treatment, made into uniformly fine particle powder, and coated in powder form. It is different from general solvent-based coatings and water-based coatings. It does not use solvent or water as the dispersion medium, but uses air as the dispersion medium. It is a new type of solvent-free 100% solid powder coating, which has the advantages of saving energy, resources and environment. The characteristics of small pollution impact, simple process, easy automatic coating, durable coating, recyclable powder, reduced labor intensity and high mechanical strength of the coating film are increasingly widely used in industrial production. [0003] At present, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D5/03C09D7/61C09D7/63
CPCC09D167/00C08K5/34924C08K2003/2241C08K2003/265C08K2003/3045C09D5/033
Inventor 黄志强
Owner GUILIN HEXIN WATERPROOF DECORATION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap