Alkali-resistant glass formulation

A formula and glass technology, applied in the food field, can solve the problems of poor alkali resistance and many bubbles of glass, and achieve the effect of good resistance to alkaline environment.

Inactive Publication Date: 2018-04-17
徐州桐圣建材有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glass is a common material in life, and is often made into various utensils and the like, but it is often seen in life that glass has poor alkali resistance and contains many bubbles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] An alkali-resistant glass formula, the raw materials in the formula are composed by weight percentage: quartz sand 60%, rutile 2%, feldspar 4%, potassium nitrate 2%, borax 2%, soda ash 10%, clarifier 6% , 10% zircon sand, the alkali resistance of alkali-resistant glass is poor at this time.

Embodiment 2

[0009] An alkali-resistant glass formula, the raw materials in the formula are composed by weight percentage: quartz sand 70%, rutile 6%, feldspar 4%, potassium nitrate 8%, borax 6%, soda ash 18%, clarifier 7%, Zircon sand is 16%, and the cost of alkali-resistant glass is too high at this time.

Embodiment 3

[0011] An alkali-resistant glass formula, the raw materials in the formula are composed by weight percentage: quartz sand 65%, rutile 4%, feldspar 9%, potassium nitrate 5%, borax 4%, soda ash 14%, clarifier 7%, Zircon sand 13%, at this time, alkali-resistant glass has good performance against alkaline environment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is an alkali-resistant glass formula. The raw materials in the formula are composed of 60-70% of quartz sand, 2-6% of rutile, 4-14% of feldspar, 2-8% of potassium nitrate, and 2% of borax according to the weight percentage. -6%, soda ash 10-18%, clarifying agent 6-8%, zircon sand 10-16%, the alkali-resistant glass of the present invention has good performance against alkaline environment.

Description

technical field [0001] The invention relates to an alkali-resistant glass formulation, which belongs to the field of food. Background technique [0002] Glass is a common material in life, and is often made into various utensils and the like. However, glass is often seen in life with poor alkali resistance and contains many bubbles. SUMMARY OF THE INVENTION [0003] In view of the above-mentioned problems in the prior art, the present invention provides an alkali-resistant glass formulation, and the alkali-resistant glass has good performance against alkaline environments. [0004] In order to achieve the above purpose, the present invention is achieved through the following technical solutions: a kind of alkali-resistant glass, the raw materials in the formula are respectively composed by weight percentage: 60-70% of quartz sand, 2-6% of rutile, 4-14% of feldspar, Potassium nitrate 2-8%, borax 2-6%, soda ash 10-18%, clarifier 6-8%, zircon sand 10-16%. [0005] Beneficia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C4/20C03C3/093
CPCC03C4/20C03C3/093
Inventor 彭松
Owner 徐州桐圣建材有限公司