High-rigidity PE (Polyethylene) alloy

A high-hardness, alloy technology, applied in the field of polymer materials, can solve the problems of low insulation of high-density polyethylene and high price of high-density polyethylene, and achieve improved compatibility, improved abrasion resistance, and improved surface hardness. Effect

Inactive Publication Date: 2018-05-04
虞海盈
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in some special fields, PE is required to have high hardness, good friction resistance and antibacterial properties, and PE alone cannot meet these requirements
[0003] In order to increase the scope of use of polyethylene and increase the hardness of polyethylene, the hardness of high-density polyethylene can basically meet the current requirements for polyethylene hardness by using high-density polyethylene, but the price of high-density polyethylene is relatively high, and then Increase the production cost of products made of high-density polyethylene, on the other hand, the insulation of high-density polyethylene is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-rigidity PE (Polyethylene) alloy
  • High-rigidity PE (Polyethylene) alloy
  • High-rigidity PE (Polyethylene) alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Weigh 50 parts of PE, 10 parts of PMMA, 0.2 part of PE-g-MAH, 0.05 part of Irganox1010, 0.05 part of Irganox168 and 0.1 part of ethylene bisstearamide.

[0024] The weighed above-mentioned materials were stirred by a high-speed mixer for 10 minutes to form a mixed material.

[0025] The mixed material is put into the hopper of the twin-screw extruder, melted and reacted, then extruded and granulated.

[0026] Among them, the temperature of the high-speed mixer is 70° C., and the rotation speed is 120 r / min. The twin-screw extruder consists of six zones, in which the temperature and screw speed of each zone are: the temperature of the first zone is 150°C, the temperature of the second zone is 170°C, the temperature of the third zone is 170°C, the temperature of the fourth zone is 170°C, and the temperature of the fifth zone is 170°C. The temperature is 170°C, the temperature in the sixth zone is 170°C, the head temperature is 170°C; the screw speed is 180r / min.

Embodiment 2

[0028] Weigh 70 parts of PE, 30 parts of PMMA, 0.6 part of PE-g-MAH, 0.25 part of Irganox1010, 0.25 part of Irganox168 and 0.3 part of simethicone.

[0029] The weighed above-mentioned materials were stirred by a high-speed mixer for 12 minutes to form a mixed material.

[0030] The mixed material is put into the hopper of the twin-screw extruder, melted and reacted, then extruded and granulated.

[0031] Among them, the temperature of the high-speed mixer is 120° C., and the rotation speed is 240 r / min. The twin-screw extruder consists of six zones, of which the temperature and screw speed of each zone are: the temperature of the first zone is 180°C, the temperature of the second zone is 200°C, the temperature of the third zone is 200°C, the temperature of the fourth zone is 200°C, and the temperature of the fifth zone is 200°C. The temperature is 200°C, the temperature in the sixth zone is 200°C, the head temperature is 200°C; the screw speed is 240r / min.

Embodiment 3

[0033] Weigh 60 parts of PE, 20 parts of PMMA, 0.4 part of PE-g-MAH, 0.15 part of Irganox1010, 0.15 part of Irganox168 and 0.2 part of simethicone.

[0034] The weighed above-mentioned materials were stirred by a high-speed mixer for 11 minutes to form a mixed material.

[0035] The mixed material is put into the hopper of the twin-screw extruder, melted and reacted, then extruded and granulated.

[0036] Wherein the temperature of the high-speed mixer is 95° C., and the rotation speed is 180 r / min. The twin-screw extruder consists of six zones, in which the temperature and screw speed of each zone are: the temperature of the first zone is 165°C, the temperature of the second zone is 185°C, the temperature of the third zone is 185°C, the temperature of the fourth zone is 185°C, and the temperature of the fifth zone is 185°C. The temperature is 185°C, the temperature in the sixth zone is 185°C, the head temperature is 185°C; the screw speed is 210r / min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
crystallinityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-rigidity PE (Polyethylene) alloy. The high-rigidity PE alloy is prepared from the following components in parts by weight: 50 to 70 parts of PE, 10 to 30 parts of PMMA(Polymethyl Methacrylate), 0.2 to 0.6 part of a compatilizer, 0.1 to 0.5 part of an antioxidant and 0.1 to 0.3 part of a lubricant. According to the high-rigidity PE alloy, the high-surface-rigidity material is added with the polymethyl methacrylate and the disadvantage that the surface rigidity of a polyethylene material is low can be improved, so that the effect of improving abrasion resistanceis realized.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, in particular to a high-hardness PE alloy. Background technique [0002] Polyethylene (PE) is an important thermoplastic polymer with good dimensional stability, good insulation, water and oil resistance, and is widely used in household appliances, mechanical parts, office supplies and communication equipment and other fields. However, in some special fields, PE is required to have high hardness, good friction resistance and antibacterial properties, and PE alone cannot meet these requirements. [0003] In order to increase the scope of use of polyethylene and increase the hardness of polyethylene, the hardness of high-density polyethylene can basically meet the current requirements for polyethylene hardness by using high-density polyethylene, but the price of high-density polyethylene is relatively high, and then The production cost of products made of high-density polyethylene is inc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L33/12C08L51/06C08K5/134C08K5/526
CPCC08L23/06C08L2205/03C08L2205/08C08L33/12C08L51/06C08K5/1345C08K5/526
Inventor 虞海盈
Owner 虞海盈
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com