Halogen-free flame-retardant solid silicone rubber condensing pipe and preparation method thereof
A flame-retardant, solid silicon technology, which is applied in the field of halogen-free flame-retardant solid silicone rubber cold-shrink tube and its preparation, can solve the problem of low flame-retardant grade, and achieve the effect of high mechanical properties and high expansion ratio
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0039] The preparation method of the above-mentioned halogen-free flame-retardant solid silicone rubber cold shrinkable tube comprises the following steps:
[0040] Step 1: Preparation of compound rubber: add methyl vinyl silicone rubber, phenyl vinyl silicone rubber, vinyl silicone oil, fumed silica, and internal mold release agent to the internal mixer and mix evenly, heat up to 160ºC and vacuumize Stir for 4 hours. After cooling, add flame retardant and mix evenly. After standing at room temperature for 24 hours, add vulcanizing agent to the mixed rubber on the open mill with cooling water, and mix evenly.
[0041] Step 2: Rubber vulcanization: The rubber obtained in step 1 is vulcanized into a tube blank by extrusion molding, wherein the temperature of the vertical vulcanization tank is 530-600°C, the temperature of the horizontal vulcanization tank is 230-300°C, and the vulcanization speed is 1.5-3.0m / min.
[0042] Step 3: pipe expansion: the vulcanized pipe obtained in ...
preparation Embodiment 1
[0044] In parts by weight, take 90 parts of methyl vinyl silicone rubber, 15 parts of phenyl vinyl silicone rubber, 2 parts of vinyl silicone oil, 40 parts of fumed white carbon black, and 1 part of internal release agent zinc stearate and add it to the banburying Mix evenly with a machine, heat up to 160ºC and stir for 4 hours under vacuum. After cooling, add 60 parts of flame retardant (composed of 30 parts of aluminum hydroxide, 10 parts of molybdenum trioxide, and 20 parts of expandable graphite) and mix evenly. After 24 hours at room temperature, Add 1 part of vulcanizing agent (composed of 0.5 part of platinum complex catalyst and 0.5 part of hydrogen-containing silicone oil) to the mixed rubber material on the open mill with cooling water, and mix evenly.
[0045] The obtained rubber material was vulcanized into a tube blank by extrusion molding, the temperature of the vertical vulcanization tank was 550°C, the temperature of the horizontal vulcanization tank was 250°C, ...
preparation Embodiment 2
[0049] In parts by weight, take 95 parts of methyl vinyl silicone rubber, 5 parts of phenyl vinyl silicone rubber, 4 parts of vinyl silicone oil, 50 parts of fumed white carbon black, and 2 parts of internal release agent zinc stearate and add them to the banburying Mix evenly with a machine, heat up to 160ºC and stir in vacuum for 4 hours. After cooling, add 40 parts of flame retardant (composed of 20 parts of aluminum hydroxide, 10 parts of antimony trioxide, and 10 parts of expandable graphite) and mix evenly. After 24 hours at room temperature, , Add 2 parts of vulcanizing agent (composed of 1 part of platinum complex catalyst and 1 part of hydrogen-containing silicone oil) to the mixed rubber material on the open mill with cooling water, and mix evenly.
[0050] The obtained rubber material was vulcanized into a tube blank by extrusion molding, the temperature of the vertical vulcanization tank was 580°C, the temperature of the horizontal vulcanization tank was 270°C, and ...
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
particle size (mesh) | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap