A method for producing glass fiber by using spodumene slag as flux clarifying agent
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A glass fiber and spodumene technology, applied in glass manufacturing equipment, manufacturing tools, etc., can solve the problems of glass fiber deliquescent agglomeration, high cost, and high production difficulty
Active Publication Date: 2021-05-18
NEIJIANG HUAYUAN ELECTRONICS MATERIALS
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In view of the above-mentioned prior art, the technical problem to be solved in the present invention is to provide a method for producing glass fibers using spodumene slag as a flux clarifying agent, so as to solve the problems of deliquescent agglomeration, high cost and high cost of glass fibers in the process of making. Technical problems with high production difficulty
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] Weigh the raw materials with the total weight of the raw materials as 100kg, the required amount of each raw material is: kaolin: 12kg, of which: SiO 2 ≥45%, Al 2 o 3 ≥33%, Fe 2 o 3 ≤0.9%, H 2 O≤1%; pyrophyllite: 31kg, of which: SiO 2 ≥72%, Al 2 o 3 ≥16.5%, Fe 2 o 3 ≤0.50%, H 2 O≤1%; quicklime: 17kg, of which: CaO≥88%, Fe 2 o 3 ≤0.30%, MgO≤3%, H 2 O≤1%; Dolomite: 6kg, of which CaO≥30%, Fe 2 o 3 ≤0.12%, MgO≤19.5%, H 2 O≤1%; colemanite: 6kg, of which CaO≥28%, Fe 2 o 3 ≤0.10%, SiO 2 ≤6.5%, B 2 o 3 ≥40%, H 2 O≤1%; leucoporite: 25kg, of which SiO 2 ≥82%, Al 2 o 3 ≥11%, Fe 2 o 3 ≤0.50%, H 2 O≤1%; Fluorite: 2kg, of which: CaF 2 ≥90%, H 2 O≤1%; industrial spodumene slag 1kg, of which SiO 2 ≥55%, Al 2 o 3 ≥21%, Fe2 o 3 ≤0.9%, SO 3 ≥5.5,H 2 O≤1%; the above percentages are mass percentages.
[0033] Before weighing, the composition content of CaO in quicklime should be detected every day, and the lime ratio should be adjusted according to the con...
Embodiment 2
[0042] Weigh the raw materials with the total weight of the raw materials as 100kg, the required amount of each raw material is: kaolin: 10kg, of which: SiO 2 ≥45%, Al 2 o 3 ≥33%, Fe 2 o 3 ≤0.9%, H 2 O≤1%; pyrophyllite: 37kg, of which: SiO 2 ≥72%, Al 2 o 3 ≥16.5%, Fe 2 o 3 ≤0.50%, H 2 O≤1%; quicklime: 20kg, of which: CaO≥88%, Fe 2 o 3 ≤0.30%, MgO≤3%, H 2 O≤1%; Dolomite: 5kg, of which CaO≥30%, Fe 2 o 3 ≤0.12%, MgO≤19.5%, H 2 O≤1%; colemanite: 7kg, of which CaO≥28%, Fe 2 o 3 ≤0.10%, SiO 2 ≤6.5%, B 2 o 3 ≥40%, H 2 O≤1%; leucoporite: 15kg, of which SiO 2 ≥82%, Al 2 o 3 ≥11%, Fe 2 o 3 ≤0.50%, H 2 O≤1%; Fluorite: 3kg, of which: CaF 2 ≥90%, H 2 O≤1%; industrial spodumene slag 3kg, of which SiO 2 ≥55%, Al 2 o 3 ≥21%, Fe 2 o 3 ≤0.9%, SO 3 ≥5.5,H 2 O≤1%; the above percentages are mass percentages.
[0043] Before weighing, the composition content of CaO in quicklime should be detected every day, and the lime ratio should be adjusted according to the c...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a method for producing glass fiber by using spodumene slag as a fluxing and clarifying agent, which comprises the steps of weighing, batching, melting, passing through, wire drawing, drying and the like; the components are weighed according to the following parts by weight: Kaolin: 100-120, pyrophyllite: 150-410, quicklime: 150-200, dolomite: 50-70, colemanite: 50-70, leucolite: 130-310, fluorite: 20-30, lithium 10-30 parts of pyroxene slag, the sum of parts by weight of each component is 1000. The present invention uses spodumene slag as a melting flux clarifying agent, which can prevent deliquescent agglomeration of the prepared glass fiber, and the spodumene slag can reduce the refractoriness of kaolin, and does not need to keep the melting temperature stable, thus reducing industrial production. difficulty. Adopting the method provided by the invention to produce glass fiber not only reduces the cost, but also reduces the environmental pollution caused by slag, and has good economic and social benefits.
Description
technical field [0001] The invention belongs to the technical field of glass fiber manufacture, and in particular relates to a method for producing glass fiber by using spodumene slag as a melting flux clarifying agent. Background technique [0002] Glass fiber is an inorganic non-metallic material with excellent performance, which has the advantages of good insulation, strong heat resistance, good corrosion resistance and high mechanical strength. The glass fiber is usually used as reinforcing material, electrical insulation and heat insulation materials in composite materials, and it is widely used in various fields of national economy. [0003] At present, my country's glass fiber industry mainly adopts the pool kiln wire drawing production process. When glass fiber is produced by this process, the main raw material for fluxing and clarifying agent is Glauber's salt. When Glauber's salt is used as a fluxing and clarifying agent, because of its raw material characteristic...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).