A kind of manufacturing method of multi-layer color-splashing ceramics

A production method and multi-level technology, which is applied in the production of multi-level splash color ceramics and ceramic art works, can solve the problems of deviating from splash color art in pursuit of natural beauty and unnatural patterns, so as to increase expressiveness and improve texture clarity , to avoid peeling effect

Inactive Publication Date: 2020-09-29
史文清 +2
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, the texture formed by this method has the effect of post-modification, and the pattern is unnatural, which deviates from the art of splashing color and pursues the beauty of nature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 250g of cobalt blue material, 7.5g of sodium tripolyphosphate and 700g of water were quickly ball milled for 20 minutes, then 42.5g of carboxymethyl cellulose was added, and then ball milled for 10 minutes to obtain a blue water-based slurry. The viscosity of the slurry was 120mPa·s , Take 1000g of this aqueous slurry into container 1.

[0028] Mix 200g praseodymium yellow material, 7.5g WL21-17000, 80g isooctyl alcohol, 400g 20 # Engine oil, 312.5g kerosene, fast ball milling for 20 minutes to obtain a yellow oily slurry, the viscosity of the slurry is 98mPa·s, take 1000g of the slurry and put it into the container 2.

[0029] 250g zirconium iron red material, 10g WL21-17240, 100g ethanol, 350g diesel oil, 292.5g camphor oil, fast ball mill for 20min to obtain a red oily slurry, the viscosity of the slurry is 450mPa·s, take 1000g of the slurry into the container 3 in.

[0030] The slurry in the container 1-3 is bundled and poured onto the flat ceramic body at an angle of 30°...

Embodiment 2

[0032] 150g of cobalt blue material, 9g of ammonium polyacrylate and 761g of water were quickly ball milled for 20 minutes, then 80g of polyvinyl alcohol was added, and then ball milled for 10 minutes to obtain a blue water-based slurry. The viscosity of the slurry was 30mPa·s. Take 1000g of this material The slurry is put into container 1.

[0033] 300g of zirconium iron red material, 5g of fairy water and 675g of water were quickly ball milled for 20 minutes, then 20g of gelatin was added, and then ball milled for 10 minutes to obtain a red water-based slurry. The viscosity of the slurry was 180mPa·s. Take 1000g of the slurry and put it into container 2 in.

[0034] 300g of praseodymium yellow material, 15g of maleic acid-acrylic acid copolymer, 20g of pentanol, 400g of frankincense oil, 265g of turpentine, fast ball milling for 20 minutes to obtain a yellow oily slurry, the viscosity of the slurry is 150mPa·s, take 1000g of the slurry Into container 3.

[0035] 250g titanium whi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method for a multi-layered splash-color ceramic. The method is that one or more ceramic pigments are separately used to prepare a water-based slurry and an oily slurry, the water-based slurry is used as one or more bundles, the oily slurry is used as the other bundle or the other bundles, splashing is performed on a ceramic blank from different angles to makethe water-based slurry and the oily slurry form random mixing, the characteristic that the water-based slurry and the oily slurry are not dissolved with each other is utilized to improve definition ofa splash-color pattern, density difference of the water-based slurry and the oily slurry is utilized, separation of an upper layer and a lower layer is generated in the flowing process, so that the splash-color pattern has a multi-layered three-dimensional effect, and display of the pattern is increased. The surface of the fired splash-color ceramic product is smooth and bright, the decorative pattern has a unique style, a random and various type, smoothness, naturalness, and enriched texture and aura, the decorative effect is abundant, the meaning expression is accurate, and therefore the multi-layered splash-color ceramic has broad market prospects.

Description

Technical field [0001] The invention belongs to the field of ceramic decoration and production, and specifically relates to a method for producing multi-level splash-color ceramics, and is particularly suitable for producing porcelain vases, porcelain plates and other ceramic art works of various types. Background technique [0002] The so-called splash-color ceramic art is a means of using the texture changes produced by the flow of ceramic colored paint and oil, and decorating in the texture changes. As one of the ceramic decoration techniques, splashing color is based on the traditional Chinese painting art, and has been continuously developed through exploration, inheritance, reference and innovation, forming a rich set of modern ceramic painting art expression techniques. [0003] There are four methods of splash-color painting on ceramic decoration. One is the pastel splash-ink painting method. Pastel is a combination of raw materials and oil (camphor oil, turpentine oil, fra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/87C04B41/89
CPCC04B41/009C04B41/5048C04B41/52C04B41/87C04B41/89C04B35/00C04B41/5045C04B41/5042C04B41/4539C04B41/0072C04B41/5041C04B41/5022
Inventor 史文清杨庆云杨灏
Owner 史文清
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com