Fluorine-containing paint and preparation method thereof, and fluorine release film based on coating by fluorine-containing paint

A technology of fluorine-containing coatings and basic coatings, applied in the direction of fireproof coatings, epoxy resin coatings, chemical instruments and methods, etc., can solve the problem of affecting the normal use of the release film, generation of debris and burrs, and poor die-cutting effect of the release film. Good and other problems, to achieve the effect of mild conditions, stable release force and easy realization

Inactive Publication Date: 2018-07-20
KUNSHAN QIAO WEI NEW MATERIAL
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese Invention Patent Publication CN 104057669A (publication date: 2014.9.24) discloses a production process of a fluorine release film. The release film prepared by this process has stable release force and good aging resistance, and is very suitable for use in All silicone protective tapes can be used in high temperature and high humidity environment to obtain good isolation effect, but the die-cutting effect of the release film is not good, resulting in debris and burrs, which affects the release film to a certain extent. Normal use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorine-containing paint and preparation method thereof, and fluorine release film based on coating by fluorine-containing paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of fluorine-containing paint, comprising the steps of:

[0027] S1, weigh 13g of fluorine-containing epoxy resin, 30g of base paint, 35g of n-heptane, 3.5g of ethylene-acrylic acid copolymer, 17.5g of ethylene glycol amine, and 1g of pH regulator;

[0028] S2, take the basic paint in S1, mix n-heptane and ethylene-acrylic acid copolymer, stir, disperse evenly, and heat the system temperature to 40-50°C;

[0029] S3, add fluorine-containing epoxy resin, ethylene glycol amine and pH regulator to the reaction system of S2 in sequence, adjust the temperature of the system to 40-50° C., and react at constant temperature for 5 hours.

Embodiment 2

[0031] A preparation method of fluorine-containing paint, comprising the steps of:

[0032] S1, weigh 15g of fluorine-containing epoxy resin, 45g of base paint, 15g of n-heptane, 5g of ethylene-acrylic acid copolymer, 18g of ethylene glycol amine, and 2g of pH regulator;

[0033] S2, take the basic paint in S1, mix n-heptane and ethylene-acrylic acid copolymer, stir, disperse evenly, and heat the system temperature to 40-50°C;

[0034] S3, add fluorine-containing epoxy resin, ethylene glycol amine and pH regulator to the reaction system of S2 in sequence, adjust the temperature of the system to 40-50° C., and react at constant temperature for 5.5 hours.

Embodiment 3

[0036] A preparation method of fluorine-containing paint, comprising the steps of:

[0037] S1, weigh 5g of fluorine-containing epoxy resin, 45g of base paint, 28g of n-heptane, 2g of ethylene-acrylic acid copolymer, 18g of ethylene glycol amine, and 2g of pH regulator;

[0038] S2, take the basic paint in S1, mix n-heptane and ethylene-acrylic acid copolymer, stir, disperse evenly, and heat the system temperature to 40-50°C;

[0039] S3, adding fluorine-containing epoxy resin, ethylene glycol amine and pH regulator to the reaction system of S2 in sequence, adjusting the temperature of the system to 40-50° C., and reacting at a constant temperature for 6 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fluorine-containing paint and a preparation method thereof, and a fluorine release film based on coating by the fluorine-containing paint. The fluorine-containing paint usesa basic paint as a main body, and then fluorine-containing epoxy resin and diethanol amine are added; a reaction is carried out under the conditions of a pH value of 8 to 9 and a temperature of 40 to50 DEG C for 5 to 6 h so as to obtain the fluorine-containing paint; and reaction process is simple, reaction conditions are mild, and the reaction can be easily implemented. The fluorine release filmuses the fluorine-containing paint as a release layer; an adhesive layer, a first middle layer and a second middle layer are arranged between a base layer and the release layer; and the outer side ofthe base layer is provided with a thermal insulation layer. Through interaction among the above six structures, the fluorine release film has stable release force and resistance to high temperature and ageing, and does not produce chips and burrs during die cutting.

Description

technical field [0001] The invention relates to the technical field of thin films, in particular to a fluorine-containing coating, a preparation method thereof and a fluorine release film coated based on the fluorine-containing coating. Background technique [0002] The release film refers to a film with a separable surface. The release film is not sticky or slightly sticky after being in contact with a specific material under limited conditions. [0003] Release film, also known as peeling film, isolation film, separation film, barrier film, release film, film, plastic film, hole masking film, silicone oil film, silicone oil paper, anti-adhesive film, slip film, Tianna paper, release film Paper. Usually, in order to increase the release force of the plastic film, the plastic film will be treated with plasma, or coated with fluorine, or coated with a silicon release agent on the surface of the film material, so that it can be used for various organic pressure-sensitive adhe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/20C09D163/00C09D123/08C09D7/63B32B27/36B32B27/08B32B27/28B32B7/12B32B9/04
CPCC09D5/20B32B7/12B32B9/045B32B27/08B32B27/281B32B27/36B32B27/365B32B2255/00B32B2255/26B32B2307/304B32B2307/306B32B2307/552C08L2201/08C09D5/18C09D163/00C08L23/0869
Inventor 杨龙庚
Owner KUNSHAN QIAO WEI NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com