Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Paint with jade luster and preparation method thereof

A gloss and paint technology, applied in the field of building decoration, can solve the problems of high process requirements, high energy consumption and high cost, and achieve the effects of good flexibility, low cost and good scratch resistance.

Inactive Publication Date: 2018-07-20
NANJING YIHE CULTURE CREATIVE CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are few researches on jade paint, and most of them are based on crushed jade as raw material. The cost is high, and because jade needs to be calcined and melted, it consumes a lot of energy and has relatively high process requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of jade luster paint is formed by combining the following substances according to mass components:

[0029] 37 parts of polymethyl methacrylate; 10 parts of polyisooctyl methacrylate; 9 parts of titanium dioxide; 7 parts of resin; 4 parts of film former; 7 parts of thickener; 2 parts of wetting agent; pigment components: 35 parts; the color of the pigment is azure and beige pigment; the pigment contains at least 20 parts of water-based pigment; 15 parts of oil pigment. Sky blue is fat-soluble, beige is water-soluble.

[0030] The resin is a water-soluble resin.

[0031] The thickener is white soft waxy polyamide wax.

[0032] The film forming agent is 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate.

[0033] The wetting agent is polyoxyethylene fatty alcohol ether.

[0034] A kind of jade luster paint preparation method is:

[0035] Step 1: Mix and stir polymethyl methacrylate, titanium dioxide, film forming agent, thickener, and wetting agent

[0036] Step...

Embodiment 2

[0039] A kind of jade luster paint is formed by combining the following substances according to mass components:

[0040] 35 parts of polymethyl methacrylate; 5 parts of polyisooctyl methacrylate; 6 parts of titanium dioxide; 4 parts of resin; 2 parts of film forming agent; 5 parts of thickener; 1 part of wetting agent; pigment components: 30 parts; the color of the pigment is azure and beige pigment; the pigment contains at least 20 parts of water-based pigment; 10 parts of oil pigment. Sky blue is fat-soluble, beige is water-soluble.

[0041] The resin is a water-soluble resin.

[0042] The thickener is white soft waxy polyamide wax.

[0043] The film forming agent is 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate.

[0044] The wetting agent is polyoxyethylene fatty alcohol ether.

[0045] A kind of jade luster paint preparation method is:

[0046] Step 1: Mix and stir polymethyl methacrylate, 8 parts of titanium dioxide, film forming agent, thickener, and wetting ag...

Embodiment 3

[0050] A kind of jade luster paint is formed by combining the following substances according to mass components:

[0051] 40 parts of polymethyl methacrylate; 15 parts of polyisooctyl methacrylate; 12 parts of titanium dioxide; 10 parts of resin; 6 parts of film-forming agent; 10 parts of thickener; 3 parts of wetting agent; pigment components: 40 parts; the color of the pigment is azure and beige pigment; the pigment contains at least 20 parts of water-based pigment; 20 parts of oil pigment; azure is fat-soluble, and beige is water-soluble.

[0052] The resin is a water-soluble resin.

[0053] The thickener is white soft waxy polyamide wax.

[0054] The film forming agent is 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate.

[0055] The wetting agent is polyoxyethylene fatty alcohol ether.

[0056] A kind of jade luster paint preparation method is:

[0057] Step 1: Mix and stir polymethyl methacrylate, 8 parts of titanium dioxide, film forming agent, thickener, and wetting...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a paint with jade luster and a preparation method thereof. The paint is composed of, by mass, 35-40 parts of polymethyl methacrylate, 5-15 parts of isooctyl polymethacrylate, 6-12 parts of titanium dioxide, 4-10 parts of resin, 2-6 parts of a film-forming agent, 5-10 parts of a thickener, 1-3 parts of a wetting agent and 30-40 parts of a pigment component, wherein the pigment component is composed of azure and yellow pigments and at least comprises 20-30 parts of an aqueous pigment and 10-20 parts of an oil pigment. The various components of the paint provided by the invention produce good synergistic effect; in particular, the paint with jade gloss is prepared by blending fat-soluble and water-soluble pigments; and the prepared paint has the characteristics of low cost, a stable color, long-lasting gloss, high hardness, good flexibility, good scratch resistance and good miscibility, is non-toxic and environmentally-friendly, and accords with the concept of healthy living.

Description

technical field [0001] The invention proposes a paint used in the field of building decoration, in particular a method for preparing a jade luster paint. Background technique [0002] Jade, delicate in texture, diverse in color, crystal clear and full of beauty, is a kind of decoration and artwork that people love. However, jade resources are scarce and expensive, so it is difficult to use them in paints and as decorations. CN201210531761.0 invention proposes a preparation method of negative ion jade paint. After firing, powdering and sieving of jade materials, the paint material is prepared, and negative ion jade paint is prepared. The paint material of the present invention uses chlorosulfonated polyethylene as a film-forming material, jade powder as a body material, and tourmaline powder is added to the paint material. The lacquer has the sensory effect of jade, and has a smooth surface, is not easy to accumulate dirt, and can generate negative ions. It is suitable fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/12C09D133/10C09D7/61C09D7/63C09D7/65
CPCC09D133/12C08L2205/02C08L2205/035C08L33/10C08L101/00C08L77/00C08L71/02C08K13/02C08K2003/2241C08K5/103
Inventor 王军红
Owner NANJING YIHE CULTURE CREATIVE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com