A high-performance carboxylated styrene-butadiene emulsion for artificial turf

A carboxylated styrene-butadiene emulsion, artificial turf technology, applied in the direction of adhesive types, hydrocarbon copolymer adhesives, etc., can solve the limitation of industrial application, no bonding strength and water resistance are improved to satisfactory results, Improve the limited and other problems to achieve excellent bond strength and water resistance, improve bond strength and water resistance, and improve the effect of stress defects

Active Publication Date: 2020-11-24
COCREATION GRASS CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the emulsion is applied to the artificial turf adhesive, the precipitation of the emulsifier will cause a weak boundary layer to form between the adhesive film and the grass silk, thus affecting the adhesion and water resistance of the adhesive layer
In response to this problem, the Chinese patent with the publication number CN103374090A once disclosed a method for preparing carboxylated styrene-butadiene emulsion for artificial turf back coating by soap-free emulsion polymerization. This method improves the adhesive force of the glue layer to a certain extent, but the improvement is limited. At the same time, the emulsion prepared by soap-free emulsion polymerization has poor stability and low solid content, which greatly limits its industrial application
[0005] In the prior art, carboxylated styrene-butadiene emulsion has a certain bonding strength, but the water resistance is generally poor; the improvement of the bonding strength and water resistance starts with a single performance, and has a certain effect, but when it is applied to mechanical These improved emulsions are still far from satisfactory results in improving the bonding strength and water resistance for sports artificial turf with higher performance requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-performance carboxylated styrene-butadiene emulsion for artificial turf
  • A high-performance carboxylated styrene-butadiene emulsion for artificial turf
  • A high-performance carboxylated styrene-butadiene emulsion for artificial turf

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Formula: 55 parts of main monomer styrene, 45 parts of main monomer butadiene, 1 part of carboxylic acid monomer acrylic acid, 1 part of modified monomer vinyltrimethoxysilane, modified monomer triethylene glycol diacrylic acid 4 parts of ester, 0.8 part of anionic emulsifier sodium dodecylbenzenesulfonate, 3.2 parts of reactive emulsifier sodium acrylamide stearate, 0.4 part of molecular weight regulator dodecyl mercaptan, 0.6 part of initiator potassium persulfate , 0.3 parts of chelating agent ethylenediamine tetraacetic acid, 0.5 parts of pH regulator sodium hydroxide, and 107 parts of deionized water.

[0041] Process: 55 parts of styrene, 1 part of acrylic acid, 1 part of vinyltrimethoxysilane, 4 parts of triethylene glycol diacrylate, 0.8 parts of sodium dodecylbenzenesulfonate, 3.2 parts of Sodium acrylamide stearate, 0.4 parts of dodecyl mercaptan, 0.3 parts of ethylenediamine tetraacetic acid, 80 parts of deionized water are put into the reactor, the stirring ...

Embodiment 2

[0043] Formula: 55 parts of main monomer styrene, 45 parts of main monomer butadiene, 1 part of carboxylic acid monomer acrylic acid, 1 part of modified monomer vinyltrimethoxysilane, modified monomer triethylene glycol diacrylic acid 4 parts of ester, 1.2 parts of anionic emulsifier sodium dodecylbenzenesulfonate, 2.8 parts of reactive emulsifier sodium acrylamide stearate, 0.4 part of molecular weight regulator dodecyl mercaptan, 0.6 part of initiator potassium persulfate , 0.3 parts of chelating agent ethylenediamine tetraacetic acid, 0.5 parts of pH regulator sodium hydroxide, and 107 parts of deionized water.

[0044] The polymerization process was unchanged, and it was the same as in Example 1 to prepare a carboxylated styrene-butadiene emulsion.

[0045] Table 2 Emulsion application performance testing results

[0046]

[0047] From Table 2, it can be seen that comparative examples 8, 9, and 10 use silane-type modified monomers and reactive emulsifiers, silane-type ...

Embodiment 3

[0049] Formula: 55 parts of main monomer styrene, 45 parts of main monomer butadiene, 1 part of carboxylic acid monomer methacrylic acid, 1.5 parts of modified monomer vinyltriisopropoxysilane, modified monomer tripropylene glycol 3.5 parts of diacrylate, 2.2 parts of anionic emulsifier sodium dodecylbenzenesulfonate, 1.8 parts of reactive emulsifier 2-acrylamide-2,2-dimethylethanesulfonate, molecular weight regulator dodecyl 0.4 part of mercaptan, 0.6 part of initiator potassium persulfate, 0.3 part of chelating agent ethylenediaminetetraacetic acid, 0.5 part of pH regulator sodium hydroxide, and 107 parts of deionized water.

[0050] Process: 55 parts of styrene, 1 part of methacrylic acid, 1.5 parts of vinyl triisopropoxysilane, 3.5 parts of tripropylene glycol diacrylate, 2.2 parts of sodium dodecylbenzenesulfonate, 1.8 Parts of 2-acrylamide-2,2-dimethylethanesulfonate sodium, 0.4 parts of dodecyl mercaptan, 0.3 parts of ethylenediaminetetraacetic acid, 80 parts of deioniz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-performance carboxylic styrene-butadiene emulsion for artificial turf, and the bottom back of the artificial turf with the high-performance carboxylic styrene-butadieneemulsion for the artificial turf has excellent bonding strength and water resistance. The high-performance carboxylic styrene-butadiene emulsion for artificial turf is prepared from monomers, an emulsifier, other auxiliary agents and water, wherein the monomers used in the preparation consist of a main monomer, an unsaturated carboxylic acid monomer and a modified monomer, the modified monomer isa mixed modified monomer containing an unsaturated silane-type monomer and a multi-double bond type monomer, and the mixed modified monomer content is 0.2-10 wt% of the total monomer content. According to the high-performance carboxylic styrene-butadiene emulsion for artificial turf, groups which can be cross-linked in a curing stage can be introduced through the modified monomer, so that the compactness of an adhesive film is increased, the stress defect of an adhesive layer is reduced, and then the mechanical properties and water resistance of the adhesive layer can be improved; and a uniquesilicone structure can be introduced into the polymer through the unsaturated silane-type monomer, thereby providing more hydrophobic characteristics to the adhesive layer, and further improving thewater resistance.

Description

technical field [0001] The invention relates to a styrene-butadiene emulsion, in particular to a high-performance carboxylated styrene-butadiene emulsion for artificial turf. Background technique [0002] Artificial turf was born in the United States in the 1960s. After half a century of development, it has been more and more accepted by people. In the process of artificial turf production, it is necessary to paint a layer of adhesive on the back of the grass to fix the grass. At present, the commonly used adhesive is an environmentally friendly water-based adhesive. Partial composition. The emulsion can be pure acrylic emulsion, styrene-acrylic emulsion, styrene-butadiene emulsion, carboxylated styrene-butadiene emulsion, polyvinyl acetate emulsion, etc., and carboxylated styrene-butadiene emulsion is favored for its high bonding strength and good stability. However, when the carboxylated styrene-butadiene emulsion commonly used by artificial turf manufacturers is applied...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F236/10C08F220/06C08F230/08C08F222/20C08F2/24C08F2/26C09J125/10
CPCC08F2/24C08F2/26C08F212/08C08F236/10C09J125/10C08F220/06C08F230/08C08F222/102
Inventor 汪青李翠赵春贵
Owner COCREATION GRASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap