A production technology for a high energy gem biology wave health care yarn
A production process and bio-wave technology, applied in the field of yarn production, can solve problems such as damage to guide holes and knitting needles, easy breakage of yarn stretching, and abnormal horizontal stripes on the cloth surface, so as to enhance vitality and health, and relieve pain , the effect of balancing the potential of the human body
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
Specific Example 1
[0022] A production process of high-energy gem biowave health-care yarn includes the following steps:
[0023] Step 1. Use zirconium oxychloride powder to dissolve in water to form a zirconium oxychloride aqueous solution, and add an appropriate interface agent to protect and reduce the zirconia and avoid secondary agglomeration in the subsequent process; the interface agent is: polyvinylpyrrolidone ( PVP), whose chemical formula is (C6H9NO)n;
[0024] Step 2. The obtained powder is blended with PET through a twin-screw. In twin-screw blending production, the reaction temperature is 270°C and is carried out under vacuum. 2 O and HCl are pumped out to make the reaction proceed as follows:
[0025] ZrOCl 2 ·8H 2 O→Zr(OH) 4 +2HCl+5H 2 O;
[0026] The above method can be made into extremely fine zirconia blended in PET masterbatch, drawn into PET plastic yarn by drawing equipment.
Example Embodiment
Specific Example 2
[0027] A production process of high-energy gem biowave health-care yarn includes the following steps:
[0028] Step 1. Use zirconium oxychloride powder to dissolve in water to form a zirconium oxychloride aqueous solution, and add an appropriate interface agent to protect and reduce the zirconia and avoid secondary agglomeration in the subsequent process; the interface agent is: dodecyl Sodium sulfate (SDS), its chemical formula is C12H25SO4Na;
[0029] Step 2. The obtained powder is blended with PET through a twin-screw. In the twin-screw blending production, the reaction temperature is 290℃, and it is carried out under vacuum. 2 O and HCl are pumped out to make the reaction proceed as follows:
[0030] ZrOCl 2 ·8H 2 O→Zr(OH) 4 +2HCl+5H 2 O;
[0031] The above method can be made into extremely fine zirconia blended in PET masterbatch, drawn into PET plastic yarn by drawing equipment.
Example Embodiment
Specific Example 3
[0032] A production process of high-energy gem biowave health-care yarn includes the following steps:
[0033] Step 1. Use zirconium oxychloride powder to dissolve in water to form a zirconium oxychloride aqueous solution, and add an appropriate interface agent to protect and reduce the zirconia and avoid secondary agglomeration in the subsequent process; the interface agent is dodecylbenzene Sodium sulfonate (SDBS), its chemical formula is C18H29NaO3S;
[0034] Step 2. The obtained powder is blended with PET through a twin-screw. In the twin-screw blending production, the reaction temperature is 280℃, and it is carried out under vacuum. 2 O and HCl are pumped out to make the reaction proceed as follows:
[0035] ZrOCl 2 ·8H 2 O→Zr(OH) 4 +2HCl+5H 2 O;
[0036] The above method can be made into extremely fine zirconia blended in PET masterbatch, drawn into PET plastic yarn by drawing equipment.
[0037] In the present invention, plastic pellets with zirconium element...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap