PEEK (polyether-ether-ketone) surface modification method

A surface modification, polyether ether ketone technology, applied in the direction of coating, etc., can solve the problems of not being able to induce bone-like hydroxyapatite well, limiting the application range of implant materials, and not easy to bond bone tissue. Achieve the effect of improving biological performance, improving biocompatibility, and excellent comprehensive performance

Active Publication Date: 2018-09-07
SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the biological activity of PEEK is poor, and the implant cannot induce the formation of bone-like hydroxyapatite well, and it is not easy to bond with bone tissue, which limits its application range as an implant materi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PEEK (polyether-ether-ketone) surface modification method
  • PEEK (polyether-ether-ketone) surface modification method
  • PEEK (polyether-ether-ketone) surface modification method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The medical PEEK material is polished and washed with ethanol, acetone, and deionized water three times in sequence; b) Put the magneton in concentrated sulfuric acid, stir in a magnetic stirrer at 300r / min, and put PEEK in it to react 5min, put the sulfonated PEEK in deionized water, soak for 5min, take it out and let it dry naturally; c) Put the sulfonated PEEK in deionized water in a hydrothermal kettle at 120℃ for 4h and take it out Rinse the sample and dry it naturally; d) Put the hydrothermally treated sulfonated PEEK in 12g / L sodium borohydride dimethyl sulfoxide at 120°C in a hydrothermal kettle for 0.5h-48h and then take out the sample Rinse and dry naturally.

[0044] figure 1 It is the scanning electron micrograph of the surface of the reduced PEEK treated with different hydrothermal time in the first implementation example. (a) PEEK; (b) PEEK hydrothermal reduction treatment for 0.5 hours; (c) PEEK hydrothermal reduction treatment for 2 hours; (d) PEEK hydroth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a PEEK (polyether-ether-ketone) surface modification method. The method comprises steps as follows: PEEK is sulfonated with concentrated sulfuric acid, and sulfonated PEEK is obtained; sulfonated PEEK is subjected to reduction treatment with sodium borohydride at the temperature of 80-160 DEG C for 0.5 h or longer.

Description

Technical field [0001] The invention relates to a method for modifying the surface of PEEK. Specifically, it relates to a PEEK surface modification layer with different structures with hydroxyl functional groups obtained after reduction treatment with sodium borohydride, belonging to biological The technical field of surface modification of medical polymer materials. Background technique [0002] Polyetheretherketone (PEEK) is a semi-crystalline polymer with a crystallinity of 30-35% and a glass transition temperature of 143°C. As a new type of organic polymer compound, PEEK has the advantages of radiation semi-transmission and elastic modulus between bone cancellous and bone compact. It has a wide range of applications in the fields of injury, spine, joints and plastic surgery (Biomaterials28 (2007) 4845–4869). However, the biological activity of polyether ether ketone is poor, the implant can not well induce the formation of bone-like hydroxyapatite, and it is difficult to bo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J7/12C08J7/14C08J7/04C08G8/28C08L61/16
CPCC08G8/28C08J7/04C08J7/12C08J7/14C08J2361/16
Inventor 刘宣勇孙振杰欧阳丽萍马小涵
Owner SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap