A preparation device and method for polyimide thick film or polyimide ultra-thick film

A polyimide thick film and polyimide technology, which is applied in the coating and other directions, can solve the problems of difficult volatilization of polyamic acid solvent, and achieve the effects of improving the volatilization condition, realizing recovery and recycling, and having a simple structure.

Active Publication Date: 2021-03-02
GUANGXI NORMAL UNIV +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation device of polyimide thick film or polyimide ultra-thick film of the present invention solves the problem of premature hardening of the transition state surface of polyamic acid in the heat treatment furnace in the prior art, which makes the solvent in polyamic acid difficult to volatilize Problem, polyimide thick film or polyimide ultra-thick film with a thickness greater than 50 μm can be prepared, and the structure is simple and easy to operate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation device and method for polyimide thick film or polyimide ultra-thick film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] like figure 1 As shown, a preparation device for a polyimide thick film or a polyimide ultra-thick film of the present embodiment includes a housing 1, and the inside of the housing 1 is provided with a metal plate 2 parallel to the bottom surface of the housing 1. The metal plate 2 divides the interior of the housing 1 into two mutually independent heating chambers 3 and a cooling chamber 4 located on the upper part of the heating chamber 3, the top of the heating chamber 3 is provided with a heating pipe 5 parallel to the metal plate 2, The two sides of the cooling chamber 4 are respectively provided with an air inlet 6 and an air outlet 7, and the outer side of the housing 1 is provided with a blower 8, and the blower 8 communicates with the cooling chamber 4 through the air inlet 6. A thermocouple 9 is arranged in the middle of the metal plate 2 .

[0048] The preparation device of polyimide thick film or polyimide ultra-thick film of this embodiment, when polyamic...

Embodiment 2

[0060] The device for preparing a polyimide thick film or polyimide ultra-thick film in this embodiment is the same as that in Embodiment 1. Wherein, the material of the metal plate 2 is copper plate.

[0061] A condensation recovery device 10 is also provided outside the housing 1 , and the condensation recovery device 10 communicates with the cooling chamber 4 through the air outlet 7 .

[0062] The method for preparing a polyimide thick film or a polyimide ultra-thick film using the above-mentioned polyimide thick film or polyimide thick film preparation device of this embodiment includes the following steps:

[0063] Step 1: Under the protection of nitrogen atmosphere, add 20.00g of 3,4'-diaminodiphenyl ether into 330g of N,N-dimethylacetamide solution, stir at room temperature to dissolve, then slowly add 29.39g in several times

[0064] 3,3',4,4'-biphenyltetracarboxylic dianhydride was stirred for 6 hours after the addition to obtain a viscous polyamic acid solution (so...

Embodiment 3

[0071] The device for preparing a polyimide thick film or polyimide ultra-thick film in this embodiment is the same as that in Embodiment 1. Wherein, the material of the metal plate 2 is aluminum plate.

[0072] A condensation recovery device 10 is also provided outside the housing 1 , and the condensation recovery device 10 communicates with the cooling chamber 4 through the air outlet 7 .

[0073] The method for preparing a polyimide thick film or a polyimide ultra-thick film using the above-mentioned polyimide thick film or polyimide thick film preparation device of this embodiment includes the following steps:

[0074] Step 1: Under the protection of nitrogen atmosphere, add 13.00 g of p-phenylenediamine and 8.03 g of 4,4'-diaminodiphenyl ether into 390 g of N,N-dimethylformamide solution, stir at room temperature to dissolve, and slowly Add 47.60 g of 3,3',4,4'-biphenyltetracarboxylic dianhydride several times, and stir for 6 hours after the addition to obtain a viscous ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation device and method for polyimide thick film or polyimide ultra-thick film, belonging to the technical field of polyimide film. The preparation device includes a shell, and a metal plate parallel to the bottom surface of the shell is arranged inside the shell, and the metal plate divides the inside of the shell into two independent heating chambers and a cooling chamber located on the upper part of the heating chamber. The top of the heating chamber is provided with a heating pipe parallel to the metal plate, the two sides of the cooling chamber are respectively provided with an air inlet and an air outlet, and the outer side of the housing is provided with a blower, and the blower passes through the air inlet It communicates with the cooling cavity, and a thermocouple is arranged in the middle of the metal plate. The invention also discloses a method for preparing polyimide thick film or polyimide ultra-thick film by using the above preparation device. The invention can prepare a polyimide thick film or a polyimide ultra-thick film with a thickness greater than 50 μm, and has simple structure and easy operation.

Description

technical field [0001] The invention relates to a preparation device and method for polyimide thick film or polyimide ultra-thick film, belonging to the technical field of polyimide film. Background technique [0002] Polyimide has excellent high temperature resistance, low temperature resistance, good mechanical properties and chemical stability, and small thermal expansion coefficient. It is the polymer material with the best insulation performance in the world. Polyimide membrane materials are widely used in various high-tech fields such as electronics and aviation. [0003] According to the thickness, polyimide film can be classified into ultra-thin film (d≤8μm), conventional thin film (8μm<d≤50μm), thick film (50μm<d≤125μm) and ultra-thick film (d>125μm). The preparation process of polyimide thick film and ultra-thick film is complicated, so the price is much higher than that of polyimide conventional film. [0004] At present, the preparation method of polyi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C41/24C08G73/10C08J5/18
CPCB29C41/24C08G73/10C08J5/18
Inventor 黄思玉黄孙息
Owner GUANGXI NORMAL UNIV