Manufacturing method of Fumantianxia gourd bottle jun porcelain artware

A production method and gourd bottle technology, which is applied in the fields of decorative art, clay products, special decorative structures, etc., can solve the problems of low treasure rate and easy cracking, and achieve the effect of high yield, uniform glaze color distribution, and beautiful handicrafts

Inactive Publication Date: 2018-09-28
禹州市晋家钧窑有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A large number of gourd vases are fired, and the shape of the utensils also changes. The key to gourd vase Jun porcelain is the enamel. The color change of the enamel after glaze firing determines the value of Jun porcelain. Very easy to crack, resulting in low treasure rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of Fumantianxia gourd bottle jun porcelain artware

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Such as figure 1 Shown, a kind of making method of Fumantianxia gourd vase Jun porcelain handicraft, comprises the following steps:

[0022] Step 1. Select pottery clay; the pottery clay includes the following components: 50 parts of kaolin, 5 parts of alkaline earth, 3 parts of quartz stone, 8 parts of sandstone, 8 parts of lead powder, 8 parts of mullite, and 1 part of iron ore;

[0023] Step 2, practice mud; first coarsely crush the clay into sand or powder, then grind it, add water and mix it into a mud ball;

[0024] Step 3, drawing the billet; drawing the mud ball into a green body, the green body is gourd-shaped;

[0025] Step 4, mold making; carve the models of the dragon head, small ring, lion head and big ring respectively, and make plaster molds for the carved models;

[0026] Step 5, grouting molding; the pottery clay in step 1 is first roughly crushed into sand or powder, and then ground to a fineness of 230 mesh, mixed with water and ball milled to make ...

Embodiment 2

[0033] A method for making Fumantianxia gourd vase Jun porcelain handicraft, comprising the following steps:

[0034] Step 1. Select pottery clay; the pottery clay includes the following components: 65 parts of kaolin, 10 parts of alkaline earth, 5 parts of quartz stone, 12 parts of sandstone, 10 parts of lead powder, 10 parts of mullite, and 2 parts of iron ore;

[0035] Step 2, practice mud; first coarsely crush the clay into sand or powder, then grind it, add water and mix it into a mud ball;

[0036] Step 3, drawing the billet; drawing the mud ball into a green body, the green body is gourd-shaped;

[0037] Step 4, mold making; carve the models of the dragon head, small ring, lion head and big ring respectively, and make plaster molds for the carved models;

[0038] Step 5, grouting molding; the pottery clay in step 1 is first roughly crushed into sand or powder, and then ground to a fineness of 250 mesh, mixed with water and ball milled to make a slurry; then the slurry ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of Fumantianxia gourd bottle jun porcelain artware. The manufacturing method comprises the following steps: 1, selecting argil; 2, pugging; 3, jiggering:jiggering a mud pie, wherein the green body is gourd-shaped; 4, manufacturing a mold: engraving a dragon head, a small ring, a lion head and a big ring model separately and manufacturing gypsum moldscorrespondingly by using the engraved models; 5, molding by slip casting; 6, drying: drying the repaired green body at normal temperature, wherein the water content of the dried green body is less than 3 percent; 7, biscuiting; 8, glazing; and 9, firing. The blank glaze bonding performance is high, the finished product rate of the jun porcelain is high, and the creative and artistic effects of the works can be embodied.

Description

technical field [0001] The invention relates to the field of Jun porcelain crafts, in particular to a method for making a Fumantianxia gourd vase Jun porcelain handicraft. Background technique [0002] Jun Porcelain is known as the first of my country's "Five Famous Porcelains". It is a specialty of Yuzhou City, Henan Province. , out of the kiln and other unique features, which cannot be achieved and compared with other ceramic handicrafts. Since the Tang Dynasty, the bottle shaped like a gourd has been loved by the people because of its homonym "Fulu", and has become a traditional shape. The name "Daji bottle" means good luck. A large number of gourd vases are fired, and the shape of the utensils also changes. The key to gourd vase Jun porcelain is the enamel. The color change of the enamel after glaze firing determines the value of Jun porcelain. It is very easy to crack, resulting in a low treasure rate. Contents of the invention [0003] In view of this, the present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/28C03C8/00C04B41/86B44C5/00
CPCB44C5/00C03C8/00C04B33/13C04B33/28C04B41/009C04B41/5022C04B41/86C04B2235/3272C04B2235/3418C04B2235/3463C04B2235/40
Inventor 晋晓瞳晋文龙
Owner 禹州市晋家钧窑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap