Method for making willow-leaf-shaped vase Jun porcelain artware

A production method and handicraft technology, applied in the production field of willow-leaf vase Jun porcelain handicrafts, can solve the problems of easy cracking of Jun porcelain, low yield rate, and difficulty in achieving artistic effects, and achieve high firing difficulty, high yield rate, and blank Good glaze binding performance

Inactive Publication Date: 2019-01-11
禹州市元丰钧陶瓷有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

like figure 1 As shown, the shape of the willow-leaf bottle is modeled after a lady wearing a cheongsam. The bamboo leaves on the bottle have the implication of green bamboo leaves, youth and elegance. The existing enamel formula is also difficult to achieve this artistic effect. When firing, Jun porcelain is very easy to crack after cooling out of the kiln, and the yield is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making willow-leaf-shaped vase Jun porcelain artware

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Such as figure 1 Shown, a kind of manufacture method of willow leaf vase Jun porcelain handicraft, comprises the following steps:

[0021] Step 1, select clay; said clay includes the following components: 50 parts of kaolin, 5 parts of alkaline earth, 3 parts of quartz stone, 8 parts of sandstone, 8 parts of lead powder, 10 parts of mullite, and 1 part of iron ore;

[0022] Step 2, practice mud; first coarsely crush the clay into sand or powder, then grind it, add water and mix it into a mud ball;

[0023] Step 3, drawing the blank; drawing the mud ball into a vase blank, the diameter of the lower part of the blank is smaller than the diameter of the upper part of the blank, and the transition from the lower part of the blank to the upper part is smooth;

[0024] Step 4. Carve out a V-shaped gap with a smooth transition at the bottle mouth of the green body; and stick arc-shaped willow branches and multiple willow leaves on the green body; figure 1 As shown, the radia...

Embodiment 2

[0031] Such as figure 1 Shown, a kind of manufacture method of willow leaf vase Jun porcelain handicraft, comprises the following steps:

[0032] Step 1. Select pottery clay; the pottery clay includes the following components: 65 parts of kaolin, 10 parts of alkaline earth, 5 parts of quartz stone, 10 parts of sandstone, 10 parts of lead powder, 10 parts of mullite, and 2 parts of iron ore;

[0033] Step 2, practice mud; first coarsely crush the clay into sand or powder, then grind it, add water and mix it into a mud ball;

[0034] Step 3, drawing the blank; drawing the mud ball into a vase blank, the diameter of the lower part of the blank is smaller than the diameter of the upper part of the blank, and the transition from the lower part of the blank to the upper part is smooth;

[0035] Step 4. Carve out a V-shaped gap with a smooth transition at the bottle mouth of the green body; and stick arc-shaped willow branches and multiple willow leaves on the green body;

[0036] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for making a willow-leaf-shaped vase Jun porcelain artware. The method comprises the following steps: 1, selection of pottery clay; 2, processing for making mud; 3, drawing for making a body; 4, engraving of the bottleneck of the body with a smoothly transitional V-shaped gap, and bonding of an arc-shaped willow branch and multiple willow leaves-the body; 5, drying; 6, biscuit firing; 7, glazing; and 8, sintering. The pottery clay comprises 50-65 parts of kaolin, 5-10 parts of alkaline earth, 3-5 parts of quartz stones, 8-12 parts of sandstones, 8-10 parts of lead powder, 8-10 parts of mullite and 1-2 parts of iron ores. The body and the glaze are well bonded, the Jun porcelain yield is high, and the shape and the color of the Jun porcelain artware can wellreflect the creative and artistic effects of the artware.

Description

technical field [0001] The invention relates to the field of Jun porcelain crafts, in particular to a method for making a willow-leaf vase Jun porcelain handicraft. Background technique [0002] Jun Porcelain is known as the first of my country's "Five Famous Porcelains". It is a specialty of Yuzhou City, Henan Province. , out of the kiln and other unique features, which cannot be achieved and compared with other ceramic handicrafts. Such as figure 1 As shown, the shape of the willow-leaf bottle is modeled after a lady wearing a cheongsam. The bamboo leaves on the bottle have the implication of green bamboo leaves, youth and elegance. The existing enamel formula is also difficult to achieve this artistic effect. When firing, Jun porcelain is very easy to crack after cooling out of the kiln, and the yield of finished products is low. Contents of the invention [0003] In view of this, the present invention provides a method for making willow-leaf vase Jun porcelain handic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B33/13C04B41/89
CPCC04B33/13C03C8/00C04B41/009C04B41/52C04B41/89C04B2235/3272C04B2235/3418C04B2235/3463C04B2235/40C04B41/504C04B41/5022
Inventor 于杰
Owner 禹州市元丰钧陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com