Preparation method for anti-wrinkling textile fabric

A textile fabric, anti-wrinkle technology, applied in textiles and papermaking, improved handle fiber, biochemical fiber treatment, etc., can solve problems such as poor effect, and achieve the effect of improved elasticity, good anti-wrinkle performance, and soft hand feeling

Inactive Publication Date: 2018-11-16
FOSHAN YIXIANG DISI CLOTHING DESIGN CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to prevent the fabric from deforming and wrinkling during use, the fabric is generally subjected to further post-treatment, and the treated fabric tends to deform and wrinkle with the increase in the number of washings during use, and the effect is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The present embodiment provides a kind of preparation method of anti-wrinkle type textile fabric, comprises the following steps:

[0021] Step 1, take 5 parts of epichlorohydrin, 8 parts of fatty alcohol polyoxyethylene ether, 1 part of amino silicone oil, 7 parts of water-soluble polyurethane resin, 10 parts of ammoniated epoxy resin, 10 parts of lactic acid, 30 parts of ethanol according to parts by weight , 18 parts of polyacrylate and 50 parts of water, and mix the above raw materials evenly to obtain a treatment liquid.

[0022] Step 2, immersing the pre-prepared textile fabric substrate in the above-mentioned treatment liquid, controlling the bath ratio to 1:4, to obtain the treated textile fabric.

[0023] After the above-mentioned treated textile fabric is taken out from the treatment liquid, it is spin-dried until the liquid content of the textile fabric is 50%.

[0024] In step 3, the textile fabric in step 2 is subjected to pressing treatment at 150° C., and...

Embodiment 2

[0028] The present embodiment provides a kind of preparation method of anti-wrinkle type textile fabric, comprises the following steps:

[0029] Step 1, take 7 parts of epichlorohydrin, 12 parts of fatty alcohol polyoxyethylene ether, 3 parts of amino silicone oil, 13 parts of water-soluble polyurethane resin, 18 parts of ammoniated epoxy resin, 13 parts of lactic acid, 20 parts of ethanol according to parts by weight , 29 parts of polyacrylate and 600 parts of water, and mix the above raw materials evenly to obtain a treatment liquid.

[0030] Step 2, immersing the pre-prepared textile fabric matrix in the above-mentioned treatment liquid, controlling the bath ratio to 1:6, to obtain the treated textile fabric.

[0031] After the above-mentioned treated textile fabric is taken out from the treatment liquid, it is spin-dried until the liquid content of the textile fabric is 50%.

[0032] In step 3, the textile fabric in step 2 is subjected to pressing treatment at 160° C., an...

Embodiment 3

[0036] The present embodiment provides a kind of preparation method of anti-wrinkle type textile fabric, comprises the following steps:

[0037] Step 1, take 10 parts of epichlorohydrin, 15 parts of fatty alcohol polyoxyethylene ether, 5 parts of amino silicone oil, 15 parts of water-soluble polyurethane resin, 25 parts of ammoniated epoxy resin, 15 parts of lactic acid, 50 parts of ethanol according to parts by weight , 35 parts of polyacrylate and 800 parts of water, and mix the above raw materials evenly to obtain a treatment liquid.

[0038] Step 2, immersing the pre-prepared textile fabric matrix in the above-mentioned treatment liquid, controlling the liquor ratio to 1:10, to obtain the treated textile fabric.

[0039] After the above-mentioned treated textile fabric is taken out from the treatment liquid, it is spin-dried until the liquid content of the textile fabric is 50%.

[0040] In step 3, the textile fabric in step 2 is subjected to pressing treatment at 180° C....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method for anti-wrinkling textile fabric. The method comprises the following steps: according to the parts by weight, taking 5-10 parts of epoxy chloropropane, 8-15 parts of fatty alcohol-polyoxyethylene ether, 1-5 parts of amino silicon oil, 7-15 parts of a water-soluble polyurethane resin, 10-25 parts of an ammoniated epoxy resin, 10-15 parts of lactic acid, 30-50 parts of ethyl alcohol, 18-35 parts of polyacrylate and 500-800 parts of water, uniformly mixing the raw materials, to obtain treating fluid, and dipping a textile fabric matrix in the treating fluid, performing pressing treatment and oxygen bleaching treatment on the textile fabric, washing and drying the textile fabric after the oxygen bleaching treatment, to obtain the anti-wrinkling textile fabric. The preparation method is simple in operation, and the obtained textile fabric has the good anti-wrinkling effect.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a preparation method of an anti-wrinkle textile fabric. Background technique [0002] With the improvement of people's quality of life, the requirements for daily necessities are getting higher and higher, and the softer the cotton fabrics, the better. After washing, they are as soft and gorgeous as new ones. At this time, softeners are applied. After washing with washing powder, softener is added during rinsing. The smoothing and softening effect of the softener is mainly due to the fact that the softener is adsorbed on the surface of the fiber, preventing direct contact between the fiber and the fiber, and reducing the coefficient of dynamic and static friction between the fiber and the fiber. ,Reduce the resistance between the fabric components and the resistance between the fabric and the human body, so as to achieve the effect of soft, smooth and comfortable wearing. Espec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/53D06M15/643D06M15/564D06M15/55D06M15/285D06M13/11D06M13/207D06M13/144D06M10/00D06L4/13
CPCD06M15/53D06L4/13D06M10/00D06M13/11D06M13/144D06M13/207D06M15/285D06M15/55D06M15/564D06M15/6436D06M16/00D06M2200/20D06M2200/25D06M2200/50
Inventor 刘广飞
Owner FOSHAN YIXIANG DISI CLOTHING DESIGN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap