Water-based Anti-corrosion coating composition

A technology of composition and water-based coatings, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of increasing the complexity and duration of the formation process of corrosion-resistant coatings

Active Publication Date: 2018-11-23
SOLVAY SA
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] Indeed, multi-step coating increases the complexity and duration of the corrosion resistant coating formation process on such large parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based Anti-corrosion coating composition
  • Water-based Anti-corrosion coating composition
  • Water-based Anti-corrosion coating composition

Examples

Experimental program
Comparison scheme
Effect test

example 3

[0118] Use water (17.25 parts by weight), defoamer 035 (0.2 parts by weight), dispersant 151 (0.51 parts by weight), and A mixture of PE F87 surfactant (2.03 parts by weight) and AMP 95 neutralizer (0.51 parts by weight) was used as the liquid base. Will 10M0 (20.05 parts by weight), K-white 450H (5.07 parts by weight) and 130M (1.52 parts by weight) is dispersed therein and then supplemented with 52.76 parts by weight of P580 Latex.

[0119] Viscosity was adjusted by adding rheology modifier Rheolate 255 (0.1 parts by weight).

[0120] The PVC of this formulation is 30% vol, with a density of 1.39 g / l and a solids content of 60% wt.

[0121] The viscosity of this formulation was 3000 cP, its pH was 6.89, and its CCT was found to exceed 500 μm.

[0122] This example shows that a copolymer (VDC) latex which is very stable to dehydrochlorination and thus contains free chlorine in an amount less than 1000 ppm and which does not crystallize under coalescence / heating c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
coating thicknessaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention pertains to an aqueous coating composition comprising: an aqueous latex of a copolymer consisting essentially of recurring units derived (i) from vinylidene chloride (VDC), (ii) from vinyl chloride (VC), (iii) from one or more than one alkyl (meth)acrylate having from 1 to 12 carbon atoms in the alkyl group [monomer (MA)] and (iv) from one or more than one aliphatic alpha-beta unsaturated carboxylic acids [monomer (AA)], the proportion of recurring units derived from monomer (AA) being of at least 1.0 wt %, with respect to the total weight of the copolymer [copolymer (A)], wherein: (A) the said copolymer (A) is stable against dehydrochlorination, in a manner such that the total chloride content of the solid residue of the aqueous latex, after thermal treatment at about 120 DEG C for 2 hours, is of less than 1000 ppm, with respect to the total weight of the copolymer (A); (B) the said copolymer (A) does not to undergo any significant crystallization upon heating, in a manner such that the ratio of (j) its crystallinity index (CI) after a thermal treatment involving heating at 60 DEG C for 48 hours to (jj) its crystallinity index before such thermal treatment (Clafter thermal treatment / CI before thermal treatment) is less than 1.15; and at least one anti-corrosion pigment comprising an aluminium salt of a (poly)phosphoric acid modified with an alkaline earth metal oxide [pigment (P)]; at least one non-ionic surfactant [surfactant (NS)]; and at least one inorganic filler [filler (I)] different from pigment (P), in an amount such that the overall pigment volume concentration (PVC), comprehensive of pigment (P) and filler (I), is comprised from 20 to 40 % vol., when determined with respect to the dried coating composition.

Description

[0001] Cross References to Related Applications [0002] This application claims priority from European Application No. 16305299.6 filed on March 18, 2016, the entire content of which is hereby incorporated by reference for all purposes. technical field [0003] The present invention relates to aqueous coating compositions and methods for forming protective coatings on substrates, especially metal-containing substrates. More specifically, the present invention relates to coating compositions, methods, and coating systems involving aqueous coating compositions that can be applied at high coating thicknesses as a direct-to-metal coat, providing excellent finishing and corrosion protection. Background technique [0004] Aqueous or water-based coating compositions for protective coatings of substrates, such as preventing corrosion or rusting of ferrous metals, are well known. [0005] Particularly advantageous are compositions that do not require any "baking" periods at temper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/08C08K3/32C09D5/08
CPCC09D5/084C08K2003/327C09D127/08C08K3/32C08K5/32C09D7/61C09D7/70C09D7/45
Inventor 潘延中A.查普托特Y.范德维肯
Owner SOLVAY SA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com