Quick coating removing method of coating thermal forming steel
A technology for thermoforming steel and coating, which is applied in the directions of cleaning methods, cleaning methods and utensils using liquids, chemical instruments and methods, etc., which can solve the problems of insufficient processing stability, high laser cost, low production efficiency, etc. The effect of low input cost, low process cost and high work efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0031] Example 1: Removal of the alloy layer of the plating layer of the 22MnB5 plating hot-formed steel, with a removal depth of 28 μm. The water flow pressure is 380Mpa, the traveling speed is 8m / min, the gun head is 5mm away from the workpiece, and the gun head is tilted 15°. See you on the removed metallographic photos Figure 5 , The removal effect is good.
Example Embodiment
[0032] Example 2: Removal of the alloy layer and transition layer of the 22MnB5 coating hot-formed steel, with a removal depth of 42 μm. The water flow pressure is 420Mpa, the traveling speed is 6m / min, the gun head is 4mm away from the workpiece, and the gun head is inclined 15°. See you on the removed metallographic photos Image 6 , The removal effect is good.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap