Method for producing lead sulfate with electrochemical activity from waste lead-acid batteries

A lead-acid battery and lead sulfate technology, applied in the direction of lead sulfate, etc., can solve problems such as sales difficulties, low prices, and output reduction, and achieve the effects of reducing production costs, simple process, and reducing pollution risks

Active Publication Date: 2017-05-10
SOUTHEAST UNIV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although ammonium sulfate can be used as fertilizer, the price is very low an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing lead sulfate with electrochemical activity from waste lead-acid batteries
  • Method for producing lead sulfate with electrochemical activity from waste lead-acid batteries
  • Method for producing lead sulfate with electrochemical activity from waste lead-acid batteries

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Step (1): Gently disassemble the lead-acid battery to obtain the positive electrode sheet and the negative electrode sheet, and then separate the lead alloy grid and the electrode powder to obtain the positive electrode grid alloy, the negative electrode grid alloy, the positive electrode powder and the negative electrode powder. The content of lead sulfate in positive electrode powder and negative electrode powder was analyzed respectively.

[0053] Step (2): Put the obtained positive electrode powder (or negative electrode powder) into a stirred reactor, and then press the PbSO 4 Add sufficient amount of ammonium carbonate solution and stir to make it react. The reaction temperature is between room temperature and 50°C, and the reaction time is between 0.5 and 3 hours. Filter or centrifuge the solid (for positive electrode powder, the solid is PbO 2 and PbCO 3 The mixture of the negative electrode powder is Pb and PbCO 3 mixture) and solution (ammonium sulfate sol...

Embodiment 2

[0060] Step (1): Gently disassemble the lead-acid battery to obtain the positive electrode sheet and the negative electrode sheet, and then separate the lead alloy grid and the electrode powder to obtain the positive electrode grid alloy, the negative electrode grid alloy, the positive electrode powder and the negative electrode powder. The content of lead sulfate in positive electrode powder and negative electrode powder was analyzed respectively.

[0061] Step (2): Put the obtained positive electrode powder (or negative electrode powder) into a stirred reactor, and then press the PbSO 4 Add sufficient amount of ammonium carbonate solution and stir to make it react. The reaction temperature is between room temperature and 50°C, and the reaction time is between 0.5 and 3 hours. Filter or centrifuge the solid (for positive electrode powder, the solid is PbO 2 and PbCO 3 The mixture of the negative electrode powder is Pb and PbCO 3 mixture) and solution (ammonium sulfate sol...

Embodiment 3

[0068] Step (1): Gently disassemble the lead-acid battery to obtain the positive electrode sheet and the negative electrode sheet, and then separate the lead alloy grid and the electrode powder to obtain the positive electrode grid alloy, the negative electrode grid alloy, the positive electrode powder and the negative electrode powder. The content of lead sulfate in positive electrode powder and negative electrode powder was analyzed respectively.

[0069] Step (2): Put the obtained positive electrode powder (or negative electrode powder) into a stirred reactor, and then press the PbSO 4 Add sufficient amount of ammonium carbonate solution and stir to make it react. The reaction temperature is between room temperature and 50°C, and the reaction time is between 0.5 and 3 hours. Filter or centrifuge the solid (for positive electrode powder, the solid is PbO 2 and PbCO 3 The mixture of the negative electrode powder is Pb and PbCO 3 mixture) and solution (ammonium sulfate sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for producing lead sulfate with electrochemical activity from waste lead-acid batteries, belonging to the field of waste lead-acid battery recycling chemical techniques. By optimizing the waste lead-acid battery recycling process, the ammonium carbonate is used as a desulfurizer of lead sulfate, and a series of reactions are carried out to convert the lead sulfate which loses the electrochemical activity in the waste lead-acid batteries into lead sulfate with electrochemical activity; and the ammonium sulfate, ammonium acetate, ammonium sulfate solution and the like obtained by reaction can be used as reaction raw materials for the subsequent batches. The process is simple and easy to implement and forms a closed circulation; the method does not generate low-value byproducts, conforms to the clean production requirements, greatly reduces the pollution risk, lowers the production cost, and provides a new feasible scheme for recycling and sustainable production of waste lead-acid batteries.

Description

technical field [0001] The invention belongs to the field of recycling chemical technology of waste lead-acid batteries, and in particular relates to a method for producing electrochemically active lead sulfate by using waste lead-acid batteries. Background technique [0002] Lead sulfate is the electrode active material of lead-acid batteries. When a lead-acid battery is discharged, lead sulfate is formed on both electrodes. Studies have proved that chemically synthesized lead sulfate can be used as the positive active material of lead-acid batteries (Ke Zhang, Wei Liu, Beibei Ma, Mohammed Adnan Mezaal, Guanghua Li, Rui Zhang and Lixu Lei, "Leadsulfate used as the positive active material of lead acid batteries”, Journal of Solid State Electrochemistry, 20, 2267-2273 (2016)), and can also be used as its negative active material (YiLiu, Pengran Gao, Xianfu Bu, GuizhiKuang, Wei Liu, Lixu Lei, “Nanocrosses of leadsulphate as the negative active material of lead acid batterie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G21/20
CPCC01G21/20
Inventor 雷立旭周言庆邰建马蓓蓓刘巍
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap