Calcium-carbonate-containing high-performance composite calcium-sulfonate-based lubricating grease and preparation method thereof
A technology for compound calcium sulfonate and synthesis of calcium sulfonate, which is applied in lubricating compositions, petroleum industry, etc., can solve the problem that compound calcium sulfonate-based grease cannot have anti-aging hardening and high temperature resistance at the same time, and achieve formula components Less, improve high temperature performance, good extreme pressure effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0042] Example 1:
[0043] A preparation method of calcium carbonate-containing high-performance calcium sulfonate-based grease includes the following steps:
[0044] S1: At room temperature, weigh 350mgKOH / g of high-alkaline calcium sulfonate 1000g and 150BS base oil 1300g into the reactor and stir and mix, continue to stir and heat to 95°C to obtain mixture A;
[0045] S2: Add 10g of dodecyl hydroxystearic acid, 12g of dodecylbenzene sulfonic acid, and 100g of water to the mixture A to mix, and then quickly add 20g of acetic acid after the mixture is evenly mixed. Keep the system at 95°C and continue to stir for 1.5 hours to obtain a viscosity Mixture B;
[0046] S3: Add 150g of modified nano-calcium carbonate to viscous mixture B, keep at 95°C and keep stirring for 15min, then increase the temperature to 180°C and keep stirring for 20min to carry out the dehydration reaction. After dehydration, add 150g of 150BS base oil to cool down to 100°C. After grinding and homogenizing, the ...
Example Embodiment
[0059] Example 2:
[0060] A preparation method of calcium carbonate-containing high-performance calcium sulfonate-based grease includes the following steps:
[0061] S1: At room temperature, weigh 350mgKOH / g of high alkali value calcium sulfonate 1000g and 150BS base oil 1400g into the reactor and stir and mix, continue to stir and heat to 95°C to obtain mixture A;
[0062] S2: Add 15g of dodecyl hydroxystearic acid, 15g of dodecylbenzene sulfonic acid, and 120g of water to the mixture A and mix, and then quickly add 28g of acetic acid after the mixture is evenly mixed. Keep the system at 95°C and continue stirring for 1.5 hours to obtain a viscous Mixture B;
[0063] S3: Add 200g of modified nano-calcium carbonate to viscous mixture B, keep at 95°C and keep stirring for 15min, then increase the temperature to 180°C and keep stirring for 20min to carry out the dehydration reaction. After dehydration, add 220g of 150BS base oil to cool to 100°C. After grinding and homogenizing, the c...
Example Embodiment
[0076] Example 3:
[0077] A preparation method of calcium carbonate-containing high-performance calcium sulfonate-based grease includes the following steps:
[0078] S1: At room temperature, weigh 450mgKOH / g of 1000g of high alkali value calcium sulfonate and 1100g of 150BS base oil into the reactor and stir and mix, continue to stir and heat to 95°C to obtain mixture A;
[0079] S2: Add 10g of dodecyl hydroxystearic acid, 11g of dodecylbenzene sulfonic acid, and 100g of water to the mixture A and mix, and then quickly add 26g of acetic acid after the mixture is evenly mixed. Keep the system at 95°C and continue to stir for 1.5 hours to obtain a viscosity Mixture B;
[0080] S3: Add 180g of modified nano-calcium carbonate to viscous mixture B, keep at 95°C and keep stirring for 15min, then increase the temperature to 180°C and keep stirring for 20min to carry out the dehydration reaction. After dehydration, add 180g of 150BS base oil to cool to 100°C. After grinding and homogenizing...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap