Self-cleaning glass water repellent agent

A hydrophobic agent and self-cleaning technology, which is applied in the direction of coating, etc., can solve the problems of poor light transmission, car windshield, side windshield, front and rear view mirrors, etc. The effect of hydrophobicity and weather resistance

Active Publication Date: 2019-05-21
湖北隆胜四海新材料有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The surface of ordinary glass is a hydrophilic surface. When water droplets spread on the glass, the light transmission of the glass will deteriorate. The blurring of car windshields, side windshields, and front and rear view mirrors is an important cause of traffic accidents.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-cleaning glass water repellent agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A self-cleaning glass hydrophobic agent, including A component and B component;

[0026] Each substance and content in each raw material in component A are as shown in Table 1, and the unit of each component content is g;

[0027] Dimethylcyclosiloxane is octamethylcyclotetrasiloxane;

[0028] Phenyl-containing siloxanes include octaphenylcyclotetrasiloxane, tetramethyltetraphenylcyclotetrasiloxane, short-chain dimethyldiphenylsiloxane, short-chain methylphenylsiloxane, The weight ratio is 1:2:1:3;

[0029] The silane coupling agent is N-β-(aminoethyl)-γ-aminopropylmethyltrimethoxysilane;

[0030] Basic catalyst tetramethylammonium hydroxide;

[0031] Surfactants include nonylphenol polyoxyethylene ether, fatty alcohol polyoxyethylene ether, isomeric tridecyl alcohol polyoxyethylene ether, and the weight ratio is 2:1:3;

[0032] The solvent is ethanol;

[0033] The nanoparticles are nano silicon dioxide;

[0034] The substances and contents of each raw material in...

Embodiment 2

[0037] A self-cleaning glass hydrophobic agent, including A component and B component;

[0038] Each substance and content in each raw material in component A are as shown in Table 1, and the unit of each component content is g;

[0039] Dimethylcyclosiloxane includes octamethylcyclotetrasiloxane and dimethylcyclosiloxane in a weight ratio of 1:1;

[0040] Phenyl-containing siloxanes include octaphenylcyclotetrasiloxane, tetramethyltetraphenylcyclotetrasiloxane, short-chain dimethyldiphenylsiloxane, short-chain methylphenylsiloxane, The weight ratio is 2:3:1:1;

[0041] The silane coupling agent is N-β-(aminoethyl)-γ-aminopropylmethyltrimethoxysilane;

[0042] Basic catalyst tetramethylammonium hydroxide;

[0043] Surfactant is nonylphenol polyoxyethylene ether;

[0044] The solvent is methanol, ethanol, isopropanol, the weight ratio is 1:1:1;

[0045] The nanoparticles are nano zinc oxide;

[0046] Each material and content in each raw material in B component are as sho...

Embodiment 3

[0049] A self-cleaning glass hydrophobic agent, including A component and B component;

[0050] Each substance and content in each raw material in component A are as shown in Table 1, and the unit of each component content is g;

[0051] Dimethylcyclosiloxane includes octamethylcyclotetrasiloxane and dimethylcyclosiloxane in a weight ratio of 1:4;

[0052] Phenyl-containing siloxanes include octaphenylcyclotetrasiloxane, tetramethyltetraphenylcyclotetrasiloxane, short-chain dimethyldiphenylsiloxane, short-chain methylphenylsiloxane, The weight ratio is 4:4:1:1;

[0053] The silane coupling agent is N-β-(aminoethyl)-γ-aminopropylmethyltrimethoxysilane;

[0054] Basic catalyst tetramethylammonium hydroxide;

[0055] Surfactants include nonylphenol polyoxyethylene ether, fatty alcohol polyoxyethylene ether, isomeric tridecyl alcohol polyoxyethylene ether, and the weight ratio is 1:1:1;

[0056] Solvents include acetonitrile and acetone in a weight ratio of 1:1;

[0057] The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
refractive indexaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of surface treatment of glass and particularly relates to a self-cleaning glass water repellent agent. The self-cleaning glass water repellent agent comprises a component A and a component B, wherein the component A is prepared from the following raw materials in parts by weight: 100 parts of dimethylcyclosiloxane, 20-50 parts of phenyl siloxane, 5-10 parts of a silane coupling agent, 0.1-10 parts of a basic catalyst, 5-40 parts of a surfactant and 10-90 parts of a solvent; the component B is prepared from the following raw materials in parts by weight: 80 parts of organic fluorine, 4-15 parts of a silane coupling agent, 10-30 parts of dimethylcyclosiloxane, 10-20 parts of phenyl siloxane, 0.1-10 parts of a basic catalyst, 5-40 parts of a surfactant, 10-90 parts of a solvent and 1-20 parts of nano-titanium oxide. After the water repellent agent is used on glass of an automobile, water drops can form water beads on the surface of the glass, the contact angle of each of the water beads can be as high as 125 degrees, and the water beads can automatically fall off without leaving a trace, so that the problem of unclear sight is solved.

Description

technical field [0001] The invention belongs to the technical field of glass surface treatment, in particular to a self-cleaning glass hydrophobic agent. Background technique [0002] The surface of ordinary glass is a hydrophilic surface. When water droplets spread on the glass, the light transmission of the glass will deteriorate. The blurring of car windshields, side windshields, and front and rear view mirrors is an important cause of traffic accidents. In the case of rain or high humidity, attached droplets will form on the surface of the car glass and affect the line of sight. Contents of the invention [0003] In order to solve the above problems, the present invention provides a self-cleaning glass hydrophobic agent, water droplets can form water droplets on the glass surface, and its contact angle can be as high as 125°, which can automatically roll off without leaving traces, thereby solving the problem of unclear vision question. [0004] The present invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/08C09D7/61
Inventor 耿学辉杨伟田坤杨帆杨开柱
Owner 湖北隆胜四海新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap