A kind of water-repellent agent for high light-transmitting glass and preparation method thereof

A technology of light-transmitting glass and hydrophobic agent, applied in the direction of coating, can solve the problems of harsh use conditions, weak resistance to sand and dust erosion, limited application scope, etc., and achieve the effects of environmental protection, good catalytic effect, and broad market prospects.

Active Publication Date: 2021-11-23
湖北隆胜四海新材料有限公司
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are glass hydrophobic agents for daily car maintenance on the market, but they are generally short-acting hydrophobic agents with weak sand and dust resistance, and the glass surface needs to be cleaned to achieve a good hydrophobic effect. The use conditions are relatively harsh. limited range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-repellent agent for high light-transmitting glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of water-repellent agent for high light-transmitting glass, each substance and content in the raw material are as shown in Table 1, and the unit of each substance content is g;

[0027] Dimethylcyclosiloxane is octamethylcyclotetrasiloxane;

[0028] Phenyl-containing siloxanes include octaphenylcyclotetrasiloxane, tetramethyltetraphenylcyclotetrasiloxane, short-chain dimethyldiphenylsiloxane, short-chain methylphenylsiloxane, The weight ratio is 1:2:1:3;

[0029] The silane coupling agent is N-β-(aminoethyl)-γ-aminopropylmethyltrimethoxysilane;

[0030] Basic catalyst tetramethylammonium hydroxide;

[0031] Non-ionic surfactants include nonylphenol polyoxyethylene ether, fatty alcohol polyoxyethylene ether, isomeric tridecyl alcohol polyoxyethylene ether, and the weight ratio is 2:1:3;

[0032] The solvent is ethanol.

[0033] A preparation method of a high-transparency glass hydrophobic agent based on the above-mentioned material components, comprising the f...

Embodiment 2

[0035] A kind of water-repellent agent for high light-transmitting glass, each substance and content in the raw material are as shown in Table 1, and the unit of each substance content is g;

[0036] Dimethylcyclosiloxane is dimethylcyclosiloxane;

[0037] The phenyl-containing siloxane is octaphenylcyclotetrasiloxane;

[0038] The silane coupling agent is N-β-(aminoethyl)-γ-aminopropylmethyl trimethoxysilane;

[0039] The basic catalyst is tetramethylammonium hydroxide;

[0040] The nonionic surfactant is isomeric tridecyl alcohol polyoxyethylene ether;

[0041] The solvent is acetone.

[0042] A preparation method of a high-transparency glass hydrophobic agent based on the above-mentioned material components, comprising the following steps: S1, weighing dimethylcyclosiloxane, phenyl-containing siloxane and silane coupling agent in proportion, mixing and stirring Homogeneous, heated to 90°C to get the hot material; S2, under the condition of 125-130°C, continuously add th...

Embodiment 3

[0044] A kind of water-repellent agent for high light-transmitting glass, each substance and content in the raw material are as shown in Table 1, and the unit of each substance content is g;

[0045] Dimethylcyclosiloxane includes octamethylcyclotetrasiloxane and dimethylcyclosiloxane in a weight ratio of 1:1;

[0046] Phenyl-containing siloxanes include octaphenylcyclotetrasiloxane, tetramethyltetraphenylcyclotetrasiloxane, short-chain dimethyldiphenylsiloxane, short-chain methylphenylsiloxane , the weight ratio is 3:3:1:1;

[0047] The silane coupling agent is N-β-(aminoethyl)-γ-aminopropylmethyltrimethoxysilane;

[0048] The basic catalyst is tetramethylammonium hydroxide;

[0049] Non-ionic surfactants include nonylphenol polyoxyethylene ether, fatty alcohol polyoxyethylene ether, isomeric tridecyl alcohol polyoxyethylene ether, and the weight ratio is 1:1:1;

[0050] The solvents are methanol, ethanol, and isopropanol, and the weight ratio is 1:1:1.

[0051] A prepara...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of glass surface hydrophobic treatment, and in particular relates to a highly transparent glass hydrophobic agent and a preparation method thereof. A water-repellent agent for high light-transmitting glass, prepared from the following raw materials in parts by weight: 100 parts of dimethylcyclosiloxane, 20-50 parts of phenylsiloxane, 5-10 parts of silane coupling agent 0.1-1 part of basic catalyst, 5-100 parts of non-ionic surfactant, 10-90 parts of solvent, can form a layer of transparent hydrophobic film on the glass surface, water droplets form water droplets on the glass surface, and the contact angle is as high as 110°, which greatly speeds up the falling speed of water droplets, and can realize automatic rolling without leaving traces, thus solving the problem of unclear vision.

Description

technical field [0001] The invention belongs to the technical field of glass surface hydrophobic treatment, and in particular relates to a highly transparent glass hydrophobic agent and a preparation method thereof. Background technique [0002] The surface of ordinary glass is a hydrophilic surface. When water droplets spread on the glass, the light transmission of the glass will deteriorate. The blurring of car windshields, side windshields, and front and rear view mirrors is an important cause of traffic accidents. In the case of rain or high humidity, attached droplets will form on the surface of the car glass and affect the line of sight. [0003] There are glass hydrophobic agents for daily car maintenance on the market, but they are generally short-acting hydrophobic agents with weak sand and dust resistance, and the glass surface needs to be cleaned to achieve a good hydrophobic effect. The use conditions are relatively harsh. The scope is limited. Contents of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/28C03C17/30
CPCC03C17/006C03C17/28C03C17/30C03C2217/29C03C2217/40C03C2217/70C03C2218/11
Inventor 王薛成耿学辉杨帆杨开柱
Owner 湖北隆胜四海新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com