Epoxy-cured 70:30 polyester resin with excellent leveling property and solvent resistance and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A polyester resin and solvent-resistant technology, applied in epoxy resin coatings, polyester coatings, powder coatings, etc. Problems such as leveling on the surface of the film, to achieve the effect of high cross-linking density, excellent leveling, and prolonging the gelation time
Active Publication Date: 2021-06-04
安徽永利新材料科技有限公司
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] In view of the high activity of the carboxyl group in the 70:30 hybrid powder coating polyester in the prior art, the gelation time is short, the softening point of the polyester resin and the high-temperature melt viscosity are relatively large, resulting in insufficient leveling of the final coating film surface and The defect that the conventional coating film that forms is poor in solvent resistance, in order to improve the leveling and solvent resistance of 70:30 mixed type powder coating, the object of the present invention is to provide a kind of epoxy curing 70 with excellent leveling property and solvent resistance : 30 polyester resin and preparation method, this method uses tetradecanedioic acid, the use of 1,9-nonanediol long-chain flexible raw material can effectively reduce the melt viscosity of polyester, increase the leveling property of film surface, use Polyethylene glycol trimethoxysilyl propyl ether, glyceryl monocaprate and other components with low surface tension and viscosity are used as raw materials, which have excellent self-lubricating properties and can improve the compatibility of various materials in powder coatings during curing. , at the same time, it has the ability to migrate to the coating surface, and has the function of helping leveling and improving the fineness of the coating film surface
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] An epoxy-cured 70:30 polyester resin with excellent leveling properties and solvent resistance, its raw material composition and molar ratio are:
[0033]
[0034]
[0035] A method for preparing the excellent epoxy curing 70:30 polyester resin of above-mentioned leveling property and solvent resistance, comprising the following steps:
[0036] A. Add the formulated amount of 1,9-nonanediol, neopentyl glycol and 1,2,6-hexanetriol into the reaction kettle, heat and melt below 125°C, stir and mix evenly;
[0037]B. Add the formulated amount of terephthalic acid and catalyst to the above mixture, slowly raise the temperature to 170°C at a heating rate of 5°C / h and keep it warm for 2 hours. When the esterification water is not obvious, start the vacuum and keep the vacuum degree at React for 2 hours under the condition of 70mmHg, then remove the vacuum, add the formulated amount of tetradecanedioic acid, polyethylene glycol trimethoxysilyl propyl ether and glyceryl mo...
Embodiment 2
[0042] An epoxy-cured 70:30 polyester resin with excellent leveling properties and solvent resistance and a preparation method thereof, the raw material composition and molar ratio are:
[0043]
[0044] Its preparation method etc. are the same as embodiment 1.
[0045] The acid value of the prepared polyester resin is: 31 mgKOH / g, and the melt viscosity (200° C.): 4075 mPa·s.
Embodiment 3
[0047] An epoxy-cured 70:30 polyester resin with excellent leveling properties and solvent resistance and a preparation method thereof, the raw material composition and molar ratio are:
[0048]
[0049]
[0050] Its preparation method etc. are the same as embodiment 1.
[0051] The acid value of the prepared polyester resin is: 38 mgKOH / g, and the melt viscosity (200° C.): 3820 mPa·s.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
acid value
aaaaa
aaaaa
acid value
aaaaa
aaaaa
acid value
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to an epoxy-cured 70:30 polyester resin with excellent leveling property and solvent resistance and a preparation method thereof, belonging to the technical field of powder coating chemical industry. The use of long-chain flexible raw materials such as tetradecanedioic acid effectively reduces the melt viscosity of polyester and increases the leveling of the coating film surface. Use the high-functionality fluorine-containing end-capping agent tetrakis (3,4,5,6-tetrafluorophthalate) pentaerythritol ester to end-cap the polyester, reduce the activity of the carboxyl group of the polyester resin, and E-12 epoxy resin The curing speed is delayed, the gelation time is prolonged, and sufficient leveling time is ensured, and the coating film leveling property is excellent after curing. The end-capping agent has very high functionality, the cured coating film has a high cross-linking density, and the end-capping agent itself has a high fluorine content, so that the final cured coating film has excellent resistance to conventional organic solvents. It is finally used in powder coatings to obtain coatings with excellent leveling and solvent resistance. The raw materials used are easy to obtain, the preparation process is easy to operate, suitable for large-scale production, and conducive to improving the popularization and application of powder coatings.
Description
technical field [0001] The invention relates to a polyester resin for powder coatings and a preparation method thereof, in particular to an epoxy-cured 70:30 polyester resin with excellent leveling properties and solvent resistance and a preparation method thereof, belonging to the technical field of powder coating chemical industry. Background technique [0002] Powder coating has the characteristics of economy, environmental protection and excellent performance, and has attracted more and more attention from people. Among them, hybrid powder coatings account for more than 80% of the total powder coatings. Considering energy saving and consumption reduction and coating substrate factors, hybrid powder coatings have become a new development direction of the powder coating industry and are widely used in household appliances, hardware Components, metal furniture and other fields. [0003] Hybrid powder coatings are also called polyester-epoxy hybrid powder coatings, which ca...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more