High-temperature-resistant silicone rubber material, and preparation method thereof

A high-temperature-resistant silicone rubber and rubber technology, which is applied in the field of high-temperature-resistant silicone rubber materials and its preparation, can solve the problems of high toxicity of benzotriazole, poor mechanical properties, and many inorganic raw materials, and achieve good anti-aging performance in hot air, Good compatibility, the effect of reducing agglomeration

Inactive Publication Date: 2019-06-14
国网河南省电力公司新野县供电公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cost of platinum complexes in the above patents is high, the toxicity of benzotriazole is high, and there are many inorganic raw materials, resulting in poor compatibility between raw materials and poor mechanical properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant silicone rubber material, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A high temperature resistant silicone rubber material, made of the following raw materials in parts by weight: 100 parts of methyl vinyl silicone rubber, 30 parts of fumed silica, 3 parts of polyimide, 0.5 parts of modified aluminum nitride nanoparticles 0.5 parts of zinc stearate, 2 parts of hexamethyldisilazane, 0.5 parts of methyl hydrogen silicone oil and 1 part of vulcanizing agent.

[0027] The molecular weight of the methyl vinyl silicone rubber is 450000-650000, and the vinyl content is 0.13-0.22%.

[0028] The vulcanizing agent is bis-penta vulcanizing agent.

[0029] The preparation method of the modified aluminum nitride nanoparticles comprises the following steps:

[0030] (1) Mix aluminum nitride nanoparticles, KH570 and absolute ethanol, stir for 5 hours, then add styrene and dibenzoyl peroxide, and react in a water bath at 80°C for 10 hours to obtain a mixed solution;

[0031] The weight ratio of the aluminum nitride nanoparticles, KH570, styrene, and d...

Embodiment 2

[0040] A high temperature resistant silicone rubber material, made of the following raw materials in parts by weight: 100 parts of methyl vinyl silicone rubber, 35 parts of fumed silica, 4 parts of polyimide, 0.6 parts of modified aluminum nitride nanoparticles 0.6 parts of zinc stearate, 2.5 parts of hexamethyldisilazane, 0.8 parts of methyl hydrogen silicone oil and 1.5 parts of vulcanizing agent.

[0041] The molecular weight of the methyl vinyl silicone rubber is 450000-650000, and the vinyl content is 0.13-0.22%.

[0042] The vulcanizing agent is bis-penta vulcanizing agent.

[0043] The preparation method of the modified aluminum nitride nanoparticles comprises the following steps:

[0044] (1) Mix aluminum nitride nanoparticles, KH570 and absolute ethanol, stir for 6 hours, then add styrene and dibenzoyl peroxide, and react in a water bath at 65°C for 12 hours to obtain a mixed solution;

[0045] The weight ratio of the aluminum nitride nanoparticles, KH570, styrene, ...

Embodiment 3

[0054] A high temperature resistant silicone rubber material, made of the following raw materials in parts by weight: 100 parts of methyl vinyl silicone rubber, 40 parts of fumed silica, 5 parts of polyimide, 0.8 parts of modified aluminum nitride nanoparticles 0.7 parts of zinc stearate, 3 parts of hexamethyldisilazane, 1.0 parts of methyl hydrogen silicone oil and 2 parts of vulcanizing agent.

[0055] The molecular weight of the methyl vinyl silicone rubber is 450000-650000, and the vinyl content is 0.13-0.22%.

[0056] The vulcanizing agent is bis-penta vulcanizing agent.

[0057] The preparation method of the modified aluminum nitride nanoparticles comprises the following steps:

[0058] (1) Mix aluminum nitride nanoparticles, KH570 and absolute ethanol, stir for 6 hours, then add styrene and dibenzoyl peroxide, and react in a water bath at 70°C for 10 hours to obtain a mixed solution;

[0059] The weight ratio of the aluminum nitride nanoparticles, KH570, styrene, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-temperature-resistant silicone rubber material. The high-temperature-resistant silicone rubber material is prepared from, by weight, 100 parts of methyl vinyl silicone rubber, 30 to 50 parts of fumed silica, 3 to 7 parts of polyimide, 0.5 to 1.5 parts of modified aluminum nitride nanoparticle, 0. 5 to 1.0 part of zinc stearate, 2 to 5 parts of hexamethyldisilazane, 0.5 to 1.5 parts of methyl hydrogen silicone oil, and 1to 3 parts of a vulcanizing agent. The high-temperature-resistant silicone rubber material possesses good raw material mutual compatibility, highhardness, high mechanical strength, good performance after aging by hot air, and is suitable for long time working under high temperature conditions.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a high-temperature-resistant silicone rubber material and a preparation method thereof. Background technique [0002] Silicone rubber is a special rubber with Si-O-Si as the main chain, which has excellent high and low temperature resistance, oil resistance, chemical resistance, weather resistance and electrical insulation properties. However, in a high temperature or combustion environment, the side methyl group in the silicone rubber is prone to oxidative degradation when heated to generate free radicals to trigger the degradation of the silicone rubber, resulting in poor high temperature resistance of the silicone rubber. With the wide application of silicone rubber in silicone rubber insulators in recent years, it is of great significance to improve the high temperature resistance of silicone rubber materials. [0003] The Chinese patent with the notifi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L79/08C08L83/05C08K13/06C08K9/06C08K3/28C08K3/36C08K5/098C08K5/544B29C35/02
Inventor 李小松翟建军王真张爱梅赵颖博黄涛陈静方勇黄成鑫
Owner 国网河南省电力公司新野县供电公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap