High-strength anticorrosive artificial artistic stone plate and production method thereof

A stone slab and high-strength technology, which is applied in the field of artificial art stone slab and its preparation, can solve the problems affecting the use effect and life, and the artificial stone slab is easy to be corroded, so as to achieve low production cost, easy control of production process conditions, and bending resistance. good folding performance

Active Publication Date: 2019-08-16
深圳市绿志新型建材研究院有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a corrosion-resistant high-strength artificial art stone plate and its preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength anticorrosive artificial artistic stone plate and production method thereof
  • High-strength anticorrosive artificial artistic stone plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] The present invention also provides the preparation method of the above-mentioned artificial art stone plate, comprising the following steps:

[0031] A. Regenerate coarse aggregate 42-55 parts, regenerated fine aggregate 18-30 parts, quick-hardening cement 18-25 parts, basalt fiber 0.2-0.6 parts, and water reducing agent 0.5-0.7 parts of the aforementioned mass parts ratio , 1-2 parts of water-based epoxy resin, 2-4 parts of curing agent and 3.5-4.5 parts of water are mixed evenly for use;

[0032] B. Lay a release film on the bottom of the forming mold frame; the release film is a silicone film with a predetermined engraving;

[0033] C. Evenly distribute the evenly mixed raw materials on the release film in the forming mold frame; because a high-elasticity silicone film with a predetermined engraving (texture) is used as the base film during forming, the forming and demoulding are easy, and the forming pattern Abundant, diverse and accessible;

[0034] When using b...

Example Embodiment

[0038] Example 1

[0039] Prepare artificial art stone plate raw materials (×5kg) according to the following proportions by weight:

[0040] Recycled coarse aggregate: 42

[0041] Recycled fine aggregate: 18

[0042] Fast hardening cement: 18

[0043] Basalt fiber: 0.2

[0044] Water reducing agent: 0.5

[0045] Waterborne epoxy resin: 1

[0046] Hardener: 2

[0047] Water: 3.5

[0048] The recycled coarse aggregate is 5-31.5mm steel-mixed construction waste recycled material, the recycled fine aggregate is 0-5.0mm steel-mixed construction waste recycled material, and the fast-hardening cement is 42.5 low alkalinity sulphoaluminate Cement (Henan Dengdian Group Cement Co., Ltd.), basalt fiber is 3-5mm long chopped basalt fiber, water reducing agent is polycarboxylate superplasticizer (WS-PC type of Shenzhen Wushan New Building Materials Co., Ltd.), water-based epoxy resin The resin is modified low molecular weight bisphenol A epoxy resin BH-644 (Dongguan Heima Chemical ...

Example Embodiment

[0050] Example 2

[0051] Prepare artificial art stone plate raw materials (×5kg) according to the following proportions by weight:

[0052] Recycled coarse aggregate: 49

[0053] Recycled fines: 24

[0054] Fast hardening cement: 22

[0055] Basalt fiber: 0.4

[0056]Water reducing agent: 0.6

[0057] Waterborne epoxy resin: 1.5

[0058] Hardener: 3

[0059] Water: 4.0

[0060] The recycled coarse aggregate is 5-25mm plain mixed construction waste recycled material, the recycled fine aggregate is 0-5.0mm plain mixed construction waste recycled material, and the fast-hardening cement is 52.5 fast-hardening sulfoaluminate cement ( Yicheng Anda Special Cement Co., Ltd.), the basalt fiber is basalt mesh cloth with a pore diameter of 4mm, the water reducing agent is a polycarboxylate superplasticizer (WS-PC type of Shenzhen Wushan New Building Materials Co., Ltd.), and the water-based epoxy resin is BH-653 (Dongguan Heima Chemical Co., Ltd.), the curing agent is water-base...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-strength anticorrosive artificial artistic stone plate and a production method thereof. The artificial artistic stone plate comprises, by mass, 42-55 parts of recycledcoarse aggregates, 18-30 parts of recycled fine aggregates, 18-25 parts of fast-hardening cement, 0.2-0.6 part of basalt fibers, 0.5-0.7 part of a water reducing agent, 1-2 parts of water-based epoxyresin and 2-4 parts of a curing agent. The high-strength anticorrosive artificial artistic stone plate has the advantages of good compression resistance, good impact resistance, good bending resistance, good pollution resistance, good corrosion resistance and environmental protection, and the production method has the advantages of simplicity, easiness in control of the production process conditions, and low production cost due to the main material being recycled building wastes.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a corrosion-resistant and high-strength artificial art stone plate and a preparation method thereof. Background technique [0002] Artificial art stone slabs are mainly used for sidewalks in municipal engineering, pedestrian street pavement, overpasses, and outside hanging decorations on expressways. At present, most of the artificial stone slabs used in municipal engineering use cement as the binder and inorganic marble, quartz stone and other scraps as aggregates. Since the binder is inorganic cement, the high alkalinity produced after cement hydration The environmental matrix is ​​easily corroded after long-term rain or exposure to acidic environment outdoors, which will affect the appearance, service life and service life. Contents of the invention [0003] The object of the present invention is to provide a corrosion-resistant and high-strength artificial art s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/06B28B1/087B28B1/52B28B1/30
CPCB28B1/0873B28B1/30B28B1/52C04B28/06C04B2111/2023C04B2111/23C04B2111/28C04B2111/54C04B2201/50C04B18/167C04B14/46C04B2103/302C04B24/281C04B2103/0068
Inventor 杨根宏朱学文李正茂孙国彬
Owner 深圳市绿志新型建材研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap