Preparation method of ceramic brick with three-dimensional texture

A three-dimensional texture and ceramic tile technology, which is applied in the field of ceramic tiles and architectural ceramic tiles, can solve the problems of inability to form natural stone line textures and unnatural decorative effects, and achieve various effects, clear line textures, and simple preparation processes.

Inactive Publication Date: 2020-03-27
FOSHAN OCEANO CERAMICS
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the ceramic tile products formed by this process only form a group of decorative effects by particles, and cannot form the line texture of natural stone, and the decorative effect is unnatural

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing ceramic tiles with a three-dimensional texture, comprising the following process steps:

[0021] 1) Prepare the transparent material into transparent granules with a particle size of 1 mm, and mix it evenly with the ultra-white material. The transparent granules account for 20% by weight of the mixture to obtain a mixture, which is then distributed on the bottom of the core of the press to form a thickness The mixture layer is 3mm, and then covered with ordinary ceramic bricks until the core of the press is filled to form a base material layer with a thickness of 10mm;

[0022] 2) Adopt the anti-beating cloth pressing molding process, and turn it over by the turning machine to obtain the green body with the mixture on the top and the ordinary ceramic brick on the bottom;

[0023] 3) After the green body is thrown to a depth of 0.1 mm, it is then dried by microwave or on the reverse side of the kiln, inkjet printed, applied with transparent glaze, ...

Embodiment 2

[0025] A method for preparing ceramic tiles with a three-dimensional texture, comprising the following process steps:

[0026] 1) Prepare the transparent material into transparent granules with a particle size of 3 mm, and mix them evenly with the ultra-white material. The transparent granules account for 15% by weight of the mixture to obtain a mixture, which is then distributed on the bottom of the core of the press to form a thickness The mixture layer is 5mm, and then covered with ordinary ceramic bricks until the core of the press is filled to form a base material layer with a thickness of 8mm;

[0027] 2) Adopt the anti-beating cloth pressing molding process, and turn it over by the turning machine to obtain the green body with the mixture on the top and the ordinary ceramic brick on the bottom;

[0028] 3) The green body is fired at a high temperature in a kiln after microwave drying or kiln reverse drying, inkjet printing, and transparent glaze application to obtain th...

Embodiment 3

[0030] A method for preparing ceramic tiles with a three-dimensional texture, comprising the following process steps:

[0031] 1) Prepare the transparent material into transparent granules with a particle size of 2mm, and mix it evenly with the ultra-white material. The transparent granules account for 18% by weight of the mixture to obtain a mixture, which is then distributed on the bottom of the core of the press to form a thickness The mixture layer is 4mm, and then covered with ordinary ceramic bricks until the core of the press is filled to form a base material layer with a thickness of 9mm;

[0032] 2) Adopt the anti-beating cloth pressing molding process, and turn it over by the turning machine to obtain the green body with the mixture on the top and the ordinary ceramic brick on the bottom;

[0033] 3) The green body is fired at a high temperature in a kiln after microwave drying or kiln reverse drying, inkjet printing, and transparent glaze application to obtain the t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a ceramic brick with three-dimensional texture. The preparation method comprises the following process steps that 1), transparent granular material andsuper-white material are uniformly mixed and then are arranged on the bottom of a press mold core to form a mixed material layer, and common ceramic brick material is used for covering until the pressmold core is full with the common ceramic brick material to form a base material layer; 2), an inverse cloth pressing and forming process is adopted to obtain a green body with the mixed material onthe upper part and the common ceramic brick material in the lower part; and 3), the green body is subjected to throwing, drying, ink-jet printing and transparent glaze coating and then is put into a kiln for high-temperature firing so as to obtain a finished product. According to the preparation method, after the subsequent high-temperature firing is performed, the ink-jet printing pattern forms adifferent color showing effect on the transparent granular material and the super-white material area, so that the pattern effect of the brick surface of the ceramic tile is varied, the line textureis clear, and the feeling of natural marble standing is highlighted. The preparation process is simple, the surface of the green body can be directly inkjet printed without coating over glaze, so thatthe printing pattern is natural and free of deviation in the color showing of the super-white material layer, and large-scale industrial production is facilitated.

Description

technical field [0001] The invention relates to the field of architectural ceramic bricks, in particular to a ceramic brick with three-dimensional texture. Background technique [0002] In recent years, due to the rapid popularization of inkjet printing technology, glazed tiles have gradually replaced polished tiles and occupied the mainstream of the market due to their rich patterns and colors and delicate textures. Bricks, sunken glazes, candy glazes, etc., these products are all to better achieve the differentiated effect of glazed tiles, so as to better adapt to the market. Some ceramic manufacturers achieve the three-dimensional effect on the surface of ceramic tiles by adopting some specific techniques, making the ceramic tiles look more like natural marble. , but due to the diffusion of the penetration aid, the resolution of the pattern will be reduced, affecting the decorative effect of the ceramic tiles, and some ceramic tiles with concave-convex textures on the su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B28B3/02B28B11/04B28B11/00B28B11/24
CPCB28B3/02B28B11/001B28B11/044B28B11/241B28B11/243
Inventor 柯善军蒙臻明王妹妹
Owner FOSHAN OCEANO CERAMICS