Production process of forged coal carburant

The invention relates to a production process and a technology for a recarburizer, which is applied in the field of the production process of the forged coal carburizer, and can solve the problems of increasing the production cost of forging coal, mixing impurities, and prolonging the production process flow of the forging coal, so as to reduce breakage and improve the structural strength. , the effect of improving the purity

Active Publication Date: 2020-03-27
山西晋武能源有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing carburizers are often mixed with impurities during production, and new impurities are introduced in the production process of forged coal. Additional

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A production process of a forging coal carburizer, comprising the following processing steps:

[0026] Step S110, mixing raw materials, taking 300 mesh powdered petroleum coke and carbonaceous materials and mixing, mixing the mixed powder with asphalt to obtain mixed raw materials; in the step S110, the carbonaceous materials micro-purified graphite and free carbon The mixture has a mixing ratio of 3:2, and the mass fractions of each raw material are 20 parts of petroleum coke, 78 parts of carbonaceous materials, and 2 parts of pitch;

[0027] Step S120, raw material pretreatment, adding water to the mixed raw material in step S110 and performing rotary granulation;

[0028] Step S130, surface treatment, the pellets in step S120 are rotated in the drum until the surface is smooth without protrusions; the rotation time of the pellets in the drum is 5h, and this process is used to prevent the surface of the pellets from protruding, so that the surface of the pellets can b...

Embodiment 2

[0035] A production process of a forging coal carburizer, comprising the following processing steps:

[0036] Step S110, mixing raw materials, taking 300 mesh powdered petroleum coke and carbonaceous materials and mixing, mixing the mixed powder with asphalt to obtain mixed raw materials; in the step S110, the carbonaceous materials micro-purified graphite and free carbon The mixture has a mixing ratio of 3:2, and the mass fractions of each raw material are 20 parts of petroleum coke, 78 parts of carbonaceous materials, and 2 parts of pitch;

[0037] Step S120, raw material pretreatment, adding water to the mixed raw material in step S110 and performing rotary granulation;

[0038] Step S130, surface treatment, the pellets in step S120 are rotated in the drum until the surface is smooth without protrusions; the rotation time of the pellets in the drum is 5h, and this process is used to prevent the surface of the pellets from protruding, so that the surface of the pellets can b...

Embodiment 3

[0045] A production process of a forging coal carburizer, comprising the following processing steps:

[0046] Step S110, mixing raw materials, taking 300 mesh powdered petroleum coke and carbonaceous materials and mixing, mixing the mixed powder with asphalt to obtain mixed raw materials; in the step S110, the carbonaceous materials micro-purified graphite and free carbon The mixture has a mixing ratio of 3:2, and the mass fractions of each raw material are 25 parts of petroleum coke, 74 parts of carbonaceous materials, and 1 part of pitch;

[0047] Step S120, raw material pretreatment, adding water to the mixed raw material in step S110 and performing rotary granulation;

[0048] Step S130, surface treatment, the pellets in step S120 are rotated in the drum until the surface is smooth without protrusions; the rotation time of the pellets in the drum is 8h, and this process is used to prevent the surface of the pellets from protruding, so that the surface of the pellets can be...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production process of a forged coal carburant, wherein the process comprises the following processing steps: step S110, mixing of raw materials: mixing 300-mesh powdered petroleum coke and a carbon-containing material, and uniformly mixing the mixed powder with asphalt to obtain a mixed raw material; step S120, pretreatment of the raw materials: adding water into the mixed raw materials in the step S110, and performing rotary disc granulation; step S130, surface treatment: placing the granules in the step S120 in a roller, rotating till the surfaces of the granules are smooth and free of protrusions; step S140, screening; step S150, drying; step S160, graphitization treatment; and S170, packaging. The production process has the beneficial effects that a carburantis subjected to graphitization treatment, so that the structural strength of the carburant can be improved, the breakage of the carburant in the transportation process is reduced, and the carburant has a better particle shape; the purity of the carburant produced by the process is improved, and the thermal and electrical conductivity of the forged coal can be improved after the forged coal is modified.

Description

technical field [0001] The invention relates to the technical field of calcined coal processing, in particular to a production process of a forged coal carburizer. Background technique [0002] Calcined coal is processed by electric furnace or calciner at high temperature. It is an electrode material with low ash, low sulfur, low phosphorus, high calorific value and high compressive strength. In the process of forging coal processing, it is necessary to add a certain amount of carburant to anthracite to change the physical and chemical properties of forging coal, so that it has better structural strength and reduces its specific resistance value. Existing carburizers are often mixed with impurities during production, and new impurities are introduced in the production process of forged coal. Additional processing steps are required to remove impurities, which prolongs the process flow of forged coal production and increases the production cost of forged coal. Contents of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B32/205
CPCC01B32/205Y02P10/20
Inventor 乔会武
Owner 山西晋武能源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap