Novel aqueous damping coating material for automotive interiors, preparation method and equipment thereof

A technology for damping coatings and automotive interiors, applied in the field of damping coatings, can solve the problems of easy cracking, easy to produce blisters, poor impact resistance, etc., and achieve the effect of solving bubbling, increasing strength, and filling gaps

Inactive Publication Date: 2020-04-03
清远明宇材料科技有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, although the existing water-based damping coating has strong adhesion, its impact resistance is poor, and bubbles are easily generated inside during the coating process, so that there are a large number of gaps inside the coated coating, which is easily broken when impacted. cracked problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel aqueous damping coating material for automotive interiors, preparation method and equipment thereof
  • Novel aqueous damping coating material for automotive interiors, preparation method and equipment thereof
  • Novel aqueous damping coating material for automotive interiors, preparation method and equipment thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033]The novel water-based damping coating for automotive interior provided in this embodiment is made of the following components by weight: 10-20 parts of graphene slurry, 1-3 parts of defoamer, and 0.5-1.5 parts of thickener , 50-60 parts of modified glass powder, 3-5 parts of curing agent, 30-40 parts of environmentally friendly flame retardant, 60-80 parts of filler and 2-6 parts of film-forming aid.

[0034] Specifically, in this embodiment, it is made of the following components by weight: 10 parts of graphene slurry, 1 part of defoamer, 0.5 parts of thickener, 50 parts of modified glass powder, 3 parts of curing agent, environmental protection 30 parts of flame retardant, 60 parts of filler and 2 parts of film-forming aid.

[0035] Wherein, the defoamer is one or a combination of emulsified silicone oil and high-carbon alcohol fatty acid ester compound, and the thickener is homopolymer or copolymer emulsion of acrylic acid and methacrylic acid One or more combination...

Embodiment 2

[0042] The novel water-based damping paint, preparation method and equipment provided by the present embodiment are basically the same as in Example 1, except that:

[0043] The novel water-based damping coating for automotive interior provided in this embodiment is made of the following components by weight: 15 parts of graphene slurry, 2 parts of defoamer, 1 part of thickener, 55 parts of modified glass powder 4 parts, 4 parts of curing agent, 35 parts of environmentally friendly flame retardant, 70 parts of filler and 4 parts of film-forming aid.

[0044] The preparation method of the aforementioned novel water-based damping paint for interior decoration of automobiles specifically comprises the following steps:

[0045] S1. Preparation of raw materials: Weigh the raw materials in appropriate proportions with measuring tools in advance, and store them separately for later use. Add 55 parts of modified glass powder and 35 parts of environmentally friendly flame retardants to...

Embodiment 3

[0049] The novel water-based damping paint, preparation method and equipment provided by the present embodiment are basically the same as those in Examples 1 and 2, except that:

[0050] The novel water-based damping paint for interior decoration of a kind of automobile provided by the present embodiment is made of the following components by weight: 20 parts of graphene slurry, 3 parts of defoamer, 1.5 parts of thickener, 60 parts of modified glass powder 5 parts, 5 parts of curing agent, 40 parts of environmentally friendly flame retardant, 80 parts of filler and 6 parts of film-forming aid.

[0051] The preparation method of the aforementioned novel water-based damping paint for interior decoration of automobiles specifically comprises the following steps:

[0052] S1. Preparation of raw materials: Weigh the appropriate proportion of raw materials with measuring tools in advance, and store them separately for later use. Add 60 parts of modified glass powder and 40 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel aqueous damping coating material for automotive interiors, a preparation method and equipment thereof, wherein the novel aqueous damping coating material is prepared from the following components in parts by weight: 10-20 parts of a graphene slurry, 1-3 parts of a defoaming agent, 0.5-1.5 parts of a thickening agent, 50-60 parts of modified glass powder, 3-5 parts of a curing agent, 30-40 parts of an environment-friendly flame retardant, 60-80 parts of a filler and 2-6 parts of a film forming aid. According to the invention, by improving the matching of the components, the preparation method and the equipment of the material, the problems of low comprehensive performance, complex preparation process, many devices and high comprehensive manufacturing cost ofthe material are solved, the comprehensive performance of the material is improved, the preparation process is simplified, the number of the equipment is reduced, and the comprehensive manufacturing cost is reduced; after the graphene and the modified glass powder in the material are mixed, a stable damping structure is formed in the coating; and the bubbles generated in the mixing process of thegraphene and the modified glass powder are removed through the defoaming agent, so that the damping layer is mixed tightly, the gaps are filled, the strength of the damping layer is improved, the preparation process is simplified, and the number of equipment is reduced.

Description

technical field [0001] The invention relates to the technical field of damping coatings, in particular to a novel water-based damping coating for automotive interior decoration, a preparation method and equipment. Background technique [0002] The damping coating is prepared by adding a proper amount of fillers and auxiliary materials to a polymer resin. It is a special coating that can be coated on the surface of various metal plate structures. It has vibration reduction, heat insulation and certain sealing properties. It can be widely used. It is used for the vibration reduction of aircraft, ships, vehicles and various machinery. Since the coating can be directly sprayed on the surface of the structure, the construction is convenient, especially for the surface with complex structure such as ships and aircraft, etc., it shows its superiority. Damping coating Generally, it is directly applied on the surface of the metal plate, and it can also be used in conjunction with epo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/61C09D7/63C09D7/65C09D7/43C09D7/44C09D5/18B01F3/20B01F3/22B01F7/24B01F23/70B01F23/80
CPCC09D1/00C09D7/61C09D7/63C09D7/65C09D7/43C09D7/44C09D5/18B01F23/71B01F23/808B01F27/92
Inventor 汤海宇潘国维李桂琴杨涛郭逍遥罗晖刘志郑勇俊
Owner 清远明宇材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap