An environment-friendly metallic texture permeable pavement material

A metal texture, permeable pavement technology, applied in roads, roads, fibrous fillers, etc., can solve the problems of poor freeze-thaw cycle and noise reduction performance of concrete pavement, poor resistance to water damage of asphalt, and large gaps between particles. Good freeze-thaw cycle performance, bright and diverse colors, and low dosage

Active Publication Date: 2022-03-15
HENAN XIAN NEW BUILDING MATERIALS +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Permeable concrete pavement has the disadvantages of concrete pavement: poor bending resistance and easy cracking
However, because permeable pavement materials generally use single-graded or intermittently graded aggregates, the gaps between particles are large, and the pavement peels off after cracking.
In addition, concrete pavements perform poorly in terms of freeze-thaw cycles and noise reduction
Permeable asphalt pavement has high requirements for road materials, and the asphalt itself has poor resistance to water damage, and it is easy to cause spalling under the action of water
In addition, the concrete pavement is generally off-white, the asphalt pavement is generally black, and the colored pavement on the market is generally dyed in the later stage, which is easy to fade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An environment-friendly metallic texture permeable pavement material
  • An environment-friendly metallic texture permeable pavement material
  • An environment-friendly metallic texture permeable pavement material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of nano-SiO 2 The preparation method of film-coated flaky aluminum pigments comprises the following steps: ①Add 2.7g of pretreated aluminum powder and 67.5mL of absolute ethanol into a 250 mL four-neck flask, and then heat up to 50°C; Add liquid A and liquid B dropwise into the pressure dropping funnel at the same time. After the dropwise addition, raise the temperature to 80°C, react for 3 hours, and then filter and dry to obtain nano-SiO 2 Film-coated flaky aluminum pigments; solution A is 40.5 mL of TEOS ethanol solution (6g of TEOS), solution B is a mixed solution of 40.5 mL of ethanol, ammonia water and water (4.9 mL of ammonia water diluted with absolute ethanol and 10.8 mL of water ), the dropping speed of liquid A and liquid B is 1 drop / second.

Embodiment 2

[0027] A kind of nano-SiO 2 The preparation method of film-coated flaky aluminum pigments comprises the following steps: ①Add 2.7g of pretreated aluminum powder and 67.5mL of absolute ethanol into a 250 mL four-necked flask, and then heat up to 45°C; Add liquid A and liquid B dropwise into the pressure dropping funnel at the same time. After the dropwise addition, raise the temperature to 80°C, react for 4 hours, and then filter and dry to obtain nano-SiO 2 Film-coated flake-shaped aluminum pigment; liquid A is 40.5 mL of TEOS ethanol solution (7g of TEOS), and liquid B is a mixed solution of 40.5 mL of ethanol, ammonia water and water (4.9 mL of ammonia water diluted with absolute ethanol and 10.8 mL of water ), the dropping speed of liquid A and liquid B is 1 drop / second.

Embodiment 3

[0029] A kind of nano-SiO 2 The preparation method of film-coated flaky aluminum pigments comprises the following steps: ①Add 2.7g of pretreated aluminum powder and 67.5mL of absolute ethanol into a 250 mL four-neck flask, and then heat up to 55°C; Add liquid A and liquid B dropwise into the pressure dropping funnel at the same time. After the dropwise addition, raise the temperature to 80°C, react for 3 hours, and then filter and dry to obtain nano-SiO 2 Film-coated flaky aluminum pigments; solution A is 40.5 mL of TEOS ethanol solution (6.5 g of TEOS), solution B is a mixed solution of 40.5 mL of ethanol, ammonia and water (4.9 mL of ammonia diluted with absolute ethanol and 10.8 mL of water), the dropping speeds of liquid A and liquid B are both 1 drop / second.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention provides an environment-friendly metal texture permeable pavement material, which uses a high molecular polymer as a cementing material to improve the bending resistance and hydraulic resistance of the pavement, and has good freeze-thaw cycle performance; the high molecular polymer is mostly colorless , can better highlight the original color of gravel, and use the color of natural gravel as the decorative color, which is also convenient for coloring; changing ordinary pigments to silica-coated metallic pigments, the colors are bright and diverse and have a metallic texture, stable performance, and are not easy to paint. Discoloration, easy to disperse in the cement, less dosage, good effect; the construction process of the present invention is simple, the construction period is short, and the general construction can be opened for traffic within 24 hours; the continuous porosity is large, the noise reduction ability is strong, the material is environmentally friendly, and no secondary pollution is caused. Secondary pollution, easy to repair.

Description

technical field [0001] The invention belongs to the technical field of road construction, and in particular relates to an environment-friendly metallic texture permeable pavement material. Background technique [0002] With the development of society, the scale of cities is getting bigger and bigger, and the performance limitations of impervious pavements are becoming more and more obvious. On the one hand, when it rains, we can only rely on the municipal drainage pipe network to drain the water. When the precipitation is large, the drainage load will be increased, which will aggravate urban waterlogging. On the other hand, it blocks the natural ground evaporation circulation system, which is one of the main reasons for the urban heat island effect. In addition, impermeable pavement has many disadvantages such as increased urban noise and traffic hazards caused by stagnant water. In response to the above problems, permeable pavement materials came into being, and with the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/16C04B20/12C04B20/10C04B38/00E01C7/30E01C7/08C09C1/62C09C3/06C04B111/40C04B111/82
CPCC04B26/16C04B38/0041C04B20/1066C04B20/12E01C7/30E01C7/085C09C1/62C09C3/066C04B2201/50C04B2111/82C04B2111/40C04B2111/00284C04B22/04C04B14/02C04B38/0038C04B20/1059
Inventor 司政凯苏向东张梦闫丽伟曹林方江慧时广贺
Owner HENAN XIAN NEW BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products