Low-gloss soft-touch modified thermoplastic resin and preparation method thereof

A thermoplastic resin, low-gloss technology, applied in the field of low-gloss and soft-touch modified thermoplastic resin and its preparation, can solve the problems of complex processing technology, low surface gloss, performance loss, etc., and achieve simple production process, low gloss, low gloss effect

Inactive Publication Date: 2020-04-28
SHANDONG DAWN POLYMER CO LTD
View PDF16 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adding mica and carbon fiber to improve the performance loss caused by a large number of elastomers is not only costly but also complex in processing technology. The specific color of carbon fiber limits its use in areas with color requirements
[0007] In summary, there is currently a lack of a new material with low cost, high performance, beautiful appearance, low surface gloss, soft touch and simple preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-gloss soft-touch modified thermoplastic resin and preparation method thereof
  • Low-gloss soft-touch modified thermoplastic resin and preparation method thereof
  • Low-gloss soft-touch modified thermoplastic resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] 50KG of polypropylene (brand 548RQ, melt index 28), 20KG of elastomer masterbatch (EPDM rubber, polypropylene elastomer masterbatch, hardness of Shore A 65), 5KG of nylon 6, 22KG of talcum powder (brand HYT-04C, 3000 mesh) and 0.1KG antioxidant 1010, 0.1KG antioxidant 168, 0.4KG lubricant, 0.6KG flow modifier, 0.8KG coupling agent, mixed at high speed and put into twin-screw extrusion Melting process in the machine, the set temperature of the twin-screw extruder is 190-230°C, the speed of the main machine is 400r / min, the speed of the pelletizer is 600r / min, and the product pellets with low gloss and soft touch are obtained by traction cooling and pelletizing.

Embodiment 2

[0053] 56KG of polypropylene (grade 548RQ, melt index 28), 20KG of elastomer masterbatch (EPDM rubber, polypropylene elastomer masterbatch, hardness of Shore A 65), 2KG of nylon 6 and 0.1KG of antioxidant 1010, 0.1KG antioxidant 168, 0.4KG lubricant, 0.6KG flow modifier, 0.8KG coupling agent, after high-speed mixing evenly, put into the twin-screw extruder for melting treatment, and the set temperature of the twin-screw extruder is 190-230°C, the speed of the main engine is 400r / min, the speed of the pelletizer is 600r / min, 22KG talc powder (brand name is HYT-04C, 3000 mesh) is added into the melt from the side feeding weight loss scale, and it is cooled and cut by traction. The product particles with low gloss and soft touch are obtained.

Embodiment 3

[0055] 53KG polypropylene (grade 548RQ, melt index 28), 5KG PA6 (grade PA6 28200, viscosity 2.7), 20KG elastomer masterbatch (EPDM rubber, polypropylene elastomer masterbatch, hardness is Shore A 65), 22KG talc powder (brand is CP250, 3000 mesh), and 0.1KG antioxidant 1010, 0.1KG antioxidant 168, 0.4KG lubricant, 0.6KG flow modifier, 0.8KG coupling agent, high-speed mixing After uniformity, put it into a twin-screw extruder for melting treatment. The temperature of the twin-screw extruder is set at 190-230°C, and the speed of the main machine is 400r / min. After being pulled, cooled and pelletized, the product pellets with low gloss and soft touch are obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
elastic modulusaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to low-gloss soft-touch modified thermoplastic resin and a preparation method thereof, and belongs to the technical field of modified plastics and composite materials, the low-gloss soft-touch modified thermoplastic resin comprises the following substances by weight: 40-80 parts of thermoplastic resin; 10-40 parts of elastomer master batch; 0-20 parts of nylon; 0-30 parts ofinorganic mineral powder; 0-6 parts of a compatilizer; 0-2 parts of a coupling agent; 0.01-2 parts of an antioxidant; 0-2 parts of a colorant; 0.5-2 parts of a flow modifier; 0.2-1 part of lubricant.The modified thermoplastic resin prepared by the method is relatively low in cost; smooth and attractive appearance, the product has low glossiness and high performance, soft touch can be improved, the preparation method is simple, operation is completed in one step, the product can be widely applied to the fields of automobile industry, daily home furnishing, electrical equipment, construction and building materials, safety labor protection and the like, meanwhile, the production process is simple, original production equipment is used, and additional investment for purchasing equipment is not needed; the raw material cost is low and the product added value is high. Therefore, the device can be widely used and popularized.

Description

technical field [0001] The invention belongs to the technical field of modified plastics and composite materials, in particular to a modified thermoplastic resin with low gloss and soft touch and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, people pay more and more attention to the quality of life. Taking automotive instrumentation materials as an example, it is not only required to have beautiful textures, suitable colors, meet safe physical performance indicators, but also need to present comfortable visual and good tactile effects. [0003] JP510177 discloses a reinforced polypropylene composition, the components include 5-90% by weight of soft polypropylene material, 5-60% by weight of mineral or glass fiber and processing aids, etc., with good scratch resistance Sex and soft touch. In the above reports, in order to improve the fluidity of the material, a certain amount of peroxide needs to be added; in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/16C08L77/02C08L51/06C08K13/02C08K3/34C08K13/04C08K7/08
CPCC08L23/12C08L2205/03C08L2205/035C08K2201/005C08L23/16C08L77/02C08K13/02C08K3/34C08K13/04C08K7/08C08L51/06
Inventor 徐雪梅王红高健王少君
Owner SHANDONG DAWN POLYMER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap