Hot-melt pressure-sensitive adhesive for manufacturing tire label coating and preparation method thereof

A hot-melt, pressure-sensitive adhesive technology, applied in the direction of pressure-sensitive films/sheets, adhesives, heat-activated films/sheets, etc., can solve the problem of not being able to stably achieve the quality of high-end tire label products

Inactive Publication Date: 2020-06-23
厦门鼎宏热熔胶有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a hot-melt pressure-sensitive adhesive for tire label coating and its preparation method, which solves the problem that many hot-melt adhesive manufacturers fail to stably achieve the quality of high-end tire label products. market demand issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The embodiment of the present invention provides. A hot-melt pressure-sensitive adhesive for coating tire labels. The components of the hot-melt pressure-sensitive adhesive in parts by mass include: 32 parts of organic polymer elastomer and 12 parts of viscosity regulator , 12 parts of tackifier, 0.6 parts of other additives.

[0026] The organic polymer elastomer is a mixture of two or four of hydrogenated styrene copolymer, hydrogenated styrene block copolymer, styrene copolymer, and styrene block copolymer.

[0027] The viscosity regulator is a mixture of one or more of polyisobutylene, polybutene, naphthenic oil, and low-viscosity petroleum resin.

[0028] The tackifier is a mixture of two or more of hydrogenated DPCP resin, hydrogenated low viscosity carbon five petroleum resin, hydrogenated carbon nine petroleum resin, hydrogenated terpene resin, and terpene resin.

[0029] Other additives are a mixture of antioxidants and ultraviolet absorbers.

[0030] A method for prep...

Embodiment 2

[0038] The embodiment of the present invention provides. A hot-melt pressure-sensitive adhesive for coating tire labels. The components of the hot-melt pressure-sensitive adhesive in parts by mass include: 36 parts of organic polymer elastomer and 18 parts of viscosity regulator , 22 parts of tackifier, 0.8 parts of other additives.

[0039] The organic polymer elastomer is a mixture of two or four of hydrogenated styrene copolymer, hydrogenated styrene block copolymer, styrene copolymer, and styrene block copolymer.

[0040] The viscosity regulator is a mixture of one or more of polyisobutylene, polybutene, naphthenic oil, and low-viscosity petroleum resin.

[0041] The tackifier is a mixture of two or more of hydrogenated DPCP resin, hydrogenated low-viscosity carbon five petroleum resin, hydrogenated carbon nine petroleum resin, hydrogenated or unhydrogenated terpene resin.

[0042] Other additives are a mixture of antioxidants and ultraviolet absorbers.

[0043] A method for prepa...

Embodiment 3

[0051] The embodiment of the present invention provides. A hot-melt pressure-sensitive adhesive used in the production of tire label coating. The components of the hot-melt pressure-sensitive adhesive in parts by mass include: 43 parts of organic polymer elastomer and 23.6 parts of viscosity regulator , 30 parts of tackifier, 1 part of other additives.

[0052] The organic polymer elastomer is a mixture of two or four of hydrogenated styrene copolymer, hydrogenated styrene block copolymer, styrene copolymer, and styrene block copolymer.

[0053] The viscosity regulator is a mixture of one or more of polyisobutylene, polybutene, naphthenic oil, and low-viscosity petroleum resin.

[0054] The tackifier is a mixture of two or more of hydrogenated DPCP resin, hydrogenated low viscosity carbon five petroleum resin, hydrogenated carbon nine petroleum resin, hydrogenated terpene resin, and terpene resin.

[0055] Other additives are a mixture of antioxidants and ultraviolet absorbers.

[005...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides a hot-melt pressure-sensitive adhesive for manufacturing tire label coating and a preparation method thereof, and relates to the field of hot-melt pressure-sensitive adhesives.The hot-melt pressure-sensitive adhesive for manufacturing the tire label coating is prepared from the following components in parts by mass: 32 to 45 parts of an organic polymer elastomer, 10 to 26 parts of a viscosity regulator, 10 to 30 parts of a tackifier and 0.3 to 1 part of other auxiliary agents, by selecting a plurality of high-quality organic polymer new materials which have specific functions and are produced abroad, the selection material and the proportion of the conventional hot-melt pressure-sensitive adhesive are broken through. The method is characterized in that a self-ownednew process and an equipment process parameter method are adopted. The four technical requirements that the product quality of numerous hot melt adhesive production enterprises cannot stably meet thehigh-end tire label due to high product quality requirement and high production difficulty of the hot melt pressure-sensitive adhesive for coating the high-end tire label are solved.

Description

Technical field [0001] The invention relates to the technical field of hot-melt pressure-sensitive adhesives, in particular to a hot-melt pressure-sensitive adhesive used for making tire label coating and a method for preparing the same. Background technique [0002] The hot-melt pressure-sensitive adhesive used for tire label coating is different from the hot-melt pressure-sensitive adhesive used for general label coating. The difference is that the main base material for making tires is non-polar rubber, and its labeling surface It also contains residues of dimethyl silicone oil and other pollutants. This is due to the release agent sprayed on the mold during the tire vulcanization process. Therefore, hot melt pressure sensitive adhesives are required: 1. It must have a strong initial Adhesive force and appropriate final adhesive strength; 2. It must have sufficient elastic modulus to adapt to high-speed slitting, printing, and die-cutting without overflowing glue, without stic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J153/02C09J7/35C09J7/38G09F3/02
CPCC08L2201/08C08L2205/025C08L2205/035C08L2207/04C09J153/02C09J153/025C09J2203/334C09J7/35C09J7/387G09F3/02C08L53/025C08L53/02
Inventor 丘鼎锡
Owner 厦门鼎宏热熔胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap