Hollow capsule enteric coated sealing ring composition and preparation method and application thereof
A technology of hollow capsules and compositions, which is applied in the fields of capsule delivery, non-active ingredients of polymer compounds, pharmaceutical formulations, etc., to achieve the effects of mechanical properties, anti-collision, firm adhesion, and good effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0041] The empty capsules in the embodiment are gelatin enteric-coated empty capsules, and the model is 0#. The content is standard myrtle oil, and the filling volume is 400mg.
[0042] The components of the ring-sealing composition are as follows: 23wt% gelatin, 15wt% methacrylic acid copolymer, 1wt% glycerin, and 61% water.
[0043]Weigh 23 parts by mass of gelatin, 44 parts by mass of water, and 1 part by mass of glycerin in proportion, put them into the cooking liquid tank, turn on the heating to 65°C, stir at a speed of 60r / min for 40min, and record it as liquid A. Take 17 parts by mass of water and 15 parts by mass of methacrylic resin at room temperature, stir at a speed of 40 r / min for 20 min, and record it as liquid B. Mix the AB and AB solutions that have been stirred enough, and use an emulsifier to stir at a speed of 600 r / min for 15 minutes at 50°C. Let the emulsified liquid stand still to obtain the enteric-coated ring-sealing solution, which is stored at a con...
Embodiment 2
[0048] In the embodiment, the hollow capsule is selected from hydroxypropyl methylcellulose enteric-coated hollow capsule, and the model is 1#. The content is fish oil, and the loading capacity is 300mg.
[0049] The components of the ring sealing composition are as follows: 14wt% of hydroxypropyl methylcellulose, 11.5wt% of hydroxypropylmethylcellulose phthalate, 2wt% of propylene glycol, 65wt% of water, 7wt% of ethanol, soybean lecithin 0.5wt%,.
[0050] Weigh 14 parts by mass of hydroxypropyl methylcellulose, 62 parts by mass of water, 0.5 parts by mass of soybean lecithin, and 2 parts by mass of propylene glycol in proportion, put them into the boiling liquid tank, turn on the heating to 65°C, / min speed stirring for 40min, recorded as A solution. Take 7 parts by mass of ethanol, 3 parts by mass of water, and 11.5 parts by mass of hydroxypropylmethylcellulose phthalate at room temperature, stir at a speed of 40 r / min for 20 minutes, and record it as liquid B. Mix the tw...
Embodiment 3
[0055] The hollow capsules in the embodiment are pullulan enteric-coated hollow capsules, the type of which is 2#. The content is garlic essential oil, with a loading capacity of 200mg.
[0056] The components of the ring sealing composition are as follows: gelatin 13wt%, methacrylic acid copolymer 8wt%, pectin 2wt%, sorbitol 1.5wt%, water 64.5wt%, ethanol 5.5wt%, 5wt% Tween 80, 0.5wt% % Simethicone.
[0057] Weigh 13 parts by mass of gelatin, 52.5 parts by mass of water, 1.5 parts by mass of sorbitol, 5 parts by mass of Tween 80, and simethicone oil of 0.5 parts by mass, put them into the boiling liquid tank, turn on and heat until Stir at 60°C for 40min at a speed of 60r / min, and record it as liquid A. Take 12 parts by mass of water, 5.5 parts by mass of ethanol, 8 parts by mass of methacrylic acid copolymer, and 2 parts by mass of pectin at 70°C, stir at a speed of 40 r / min for 20 minutes, and record it as liquid B. Mix the AB and AB solutions that have been stirred enou...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com