A flash welding method for hrb600 high-strength hot-rolled steel bar

A welding method and steel bar technology, applied in welding equipment, resistance welding equipment, metal processing equipment, etc., can solve the problems of long welding process, high alloy addition, low strength level, etc., and achieve high strength, high toughness and reliability of welded joints. Safety, saving welding time, and strong applicability

Active Publication Date: 2022-02-18
INST OF RES OF IRON & STEEL JIANGSU PROVINCE +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flash welding process matching the high-strength and high-carbon equivalent steel bar HRB600 has not been reported yet.
Patent CN106112241B discloses a flash welding method for high-corrosion-resistant and high-strength steel bars. This method is only suitable for high-alloy corrosion-resistant steel bars. The alloy addition is high but the strength level is low. Preheating before welding is slow and temperature requirements are low, and After welding, tempering is required to eliminate abnormal structures, and the overall welding process takes a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A flash welding method for hrb600 high-strength hot-rolled steel bar
  • A flash welding method for hrb600 high-strength hot-rolled steel bar
  • A flash welding method for hrb600 high-strength hot-rolled steel bar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Flash butt welding of ∮20mm specification HRB600 steel bar:

[0034] The main components of the HRB600 steel bar are C 0.25, Si 0.62, Mn 1.55, V 0.15, Ceq=0.52.

[0035] (1) Pretreatment before welding: Grinding the end face of the steel bar to be welded to remove rust and scale to ensure its smoothness;

[0036] (2) Clamping of steel bars to be welded: Clamp the two ends of the steel bars to be welded in the electrode chuck and pass through the induction coil to ensure that the transverse ribs of the steel bars to be welded are penetrated and the longitudinal ribs are relatively parallel. Upsetting length 25mm.

[0037] (3) Flash welding process setting: induction heating temperature 980°C, induction heating time 15s, flash heat 75kJ, flash distance 16mm, flash speed 1.5mm / s, upsetting air pressure 0.75MPa, upsetting time ≤ 1s, pressure maintenance time 15s.

[0038] (4) Turn on the power and start the program, and the steel bars to be welded are subjected to induct...

Embodiment 2

[0044] Flash butt welding of ∮28mm HRB600 steel bars:

[0045] The main components of the HRB600 steel bar are C 0.27, Si 0.71, Mn 1.35, V 0.18, Ceq=0.53.

[0046] (1) Pre-welding pretreatment: grinding the end face of the steel bar to be welded to remove rust and oxide skin to ensure its smoothness and smoothness;

[0047] (2) Clamping of the steel bars to be welded: Clamp the two ends of the steel bars to be welded in the electrode chuck and pass through the induction coil to ensure that the transverse ribs of the steel bars to be welded pass through and the longitudinal ribs are relatively parallel. Upset forging length 40mm.

[0048] (3) Flash welding process settings: induction heating temperature 1040℃, induction heating time 22s, flash heat 120kJ, flash distance 30mm, flash speed 0.2mm / s, upsetting pressure 1.25MPa, upsetting time ≤1.5s, pressure maintained Time 30s.

[0049] (4) Turn on the power supply and start the program, and the steel bars to be welded undergo ...

Embodiment 3

[0055] Flash butt welding of ∮12mm HRB600 steel bars:

[0056] The main components of the HRB600 steel bar are C 0.24, Si 0.57, Mn 1.40, V 0.14, and Ceq=0.50.

[0057] (1) Pre-welding pretreatment: grinding the end face of the steel bar to be welded to remove rust and oxide skin to ensure its smoothness and smoothness;

[0058] (2) Clamping of the steel bar to be welded: Clamp the two ends of the steel bar to be welded in the electrode chuck and pass through the induction coil to ensure that the transverse ribs of the steel bar to be welded pass through and the longitudinal ribs are relatively parallel. Upset forging length 15mm.

[0059] (3) Flash welding process settings: induction heating temperature 920℃, induction heating time 6s, flash heat 40kJ, flash distance 8mm, flash speed 2.0mm / s, upsetting pressure 0.35MPa, upsetting time ≤ 0.5s, pressure maintained Time 5s.

[0060] (4) Turn on the power supply and start the program, and the steel bars to be welded undergo the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flash welding method of HRB600 high-strength hot-rolled steel bar, which comprises the following steps: (1) pretreatment of the welding end face of the steel bar to be welded; (2) clamping and fixing the steel bar to be welded and adjusting the welding gap distance and upsetting length; 3) Set the flash welding process parameters that match the specifications of the steel bars to be welded; (4) Start the welding machine, and the steel bars to be welded are sequentially subjected to welding zone induction heating, flash discharge, pressure upsetting, and pressure maintenance to complete the welding; (5) ) air-cooled to room temperature after welding. The invention can realize flash welding of high-carbon equivalent HRB600 high-strength hot-rolled steel bars, and the welding joint is acicular ferrite + polygonal ferrite + pearlite with good strength and toughness, meeting the fast, simple and reliable welding requirements of the construction industry.

Description

technical field [0001] The invention belongs to the field of welding technology, and in particular relates to a flash welding method for HRB600 high-strength hot-rolled steel bars. Background technique [0002] The rapid development of China's economic construction in recent years has made the construction industry put forward higher requirements for hot-rolled steel bars. Using higher-strength HRB600 high-strength steel bars to replace HRB400 steel bars as building steel bars can save steel usage and reduce structural weight, improve building safety, save energy, reduce emissions, and be environmentally friendly. At present, the carbon equivalent Ceq of HRB600 high-strength steel bars is estimated to be ≥0.50, which belongs to the difficult-to-weld steel bar; at the same time, due to the good strength and plasticity of the base metal, the welded joint needs higher strength and toughness. For this kind of high-strength and difficult-to-weld steel bars, the construction site...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K11/04B23K11/16B23K11/34B23K11/36
CPCB23K11/04B23K11/34B23K11/36B23K11/16
Inventor 杨晓伟陈焕德周云张宇
Owner INST OF RES OF IRON & STEEL JIANGSU PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap